RESUMO
The thermochemical energy-storage material couple CuSO4/[Cu(NH3)4]SO4 combines full reversibility, application in a medium temperature interval (<350 °C), and fast liberation of stored heat. During reaction with ammonia, a large change in the sulfate solid-state structure occurs, resulting in a 2.6-fold expansion of the bulk material due to NH3 uptake. In order to limit this volume work, as well as enhance the thermal conductivity of the solid material, several composites of anhydrous CuSO4 with inorganic inert support materials were prepared and characterized with regard to their energy storage density, reversibility of the storage reaction, thermal conductivity, and particle morphology. The best thermochemical energy storage properties were obtained for a 10:1 CuSO4-sepiolite composite, combining an attractive energy storage density with slightly improved thermal conductivity and decreased bulk volume work compared to the pure salt.
RESUMO
Thermochemical energy storage is considered as an auspicious method for the recycling of medium-temperature waste heat. The reaction couple Mg(OH)2â»MgO is intensely investigated for this purpose, suffering so far from limited cycle stability. To overcome this issue, Mg(OH)2, MgCO3, and MgC2O4·2H2O were compared as precursor materials for MgO production. Depending on the precursor, the particle morphology of the resulting MgO changes, resulting in different hydration behavior and cycle stability. Agglomeration of the material during cyclization was identified as main reason for the decreased reactivity. Immersion of the spent material in liquid H2O decomposes the agglomerates restoring the initial reactivity of the material, thus serving as a regeneration step.