Multiple free-radical-trapping and hydrogen-bonding-enhanced polyurethane foams with long-lasting flame retardancy, aging resistance, and toughness.

Flexible polyurethane foam (FPUF) is a ubiquitous material utilized in furniture cushions, mattresses, and various technical applications. Despite the widespread use, FPUF faces challenges in maintaining long-lasting flame retardancy and aging resistance, particularly in harsh environments, while retaining mechanical robustness. Here, we present a novel approach to address these issues by enhancing FPUF through multiple free-radical-trapping and hydrogen-bonding mechanisms. A hindered amine phosphorus-containing polyol (DTAP) was designed and chemically introduced into FPUF. The distinctive synergy between hindered amine and phosphorus-containing structures enables the formation of multiple hydrogen bonds with urethane, while also effectively capturing free radicals across a broad temperature spectrum. As a result, incorporating only 5.1 wt% of DTAP led to the material successfully passing vertical burning tests and witnessing notable enhancements in tensile strength, elongation at break, and tear strength. Even after enduring accelerated thermal aging for 168 hours, the foam maintained exceptional flame retardancy and mechanical properties. This study offers novel insights into material enhancement, simultaneously achieving outstanding long-lasting flame retardancy, toughness, and anti-aging performance.

Self-evolutionary recycling of flame-retardant polyurethane foam enabled by controllable catalytic cleavage.

Polyurethane (PU) foams, pivotal in modern life, face challenges suh as fire hazards and environmental waste burdens. The current reliance of PU on potentially ecotoxic halogen-/phosphorus-based flame retardants impedes large-scale material recycling. Here, our demonstrated controllable catalytic cracking strategy, using cesium salts, enables self-evolving recycling of flame-retardant PU. The incorporation of cesium citrates facilitates efficient urethane bond cleavage at low temperatures (160 °C), promoting effective recycling, while encouraging pyrolytic rearrangement of isocyanates into char at high temperatures (300 °C) for enhanced PU fire safety. Even in the absence of halogen/phosphorus components, this foam exhibits a substantial increase in ignition time (+258.8%) and a significant reduction in total smoke release (-79%). This flame-retardant foam can be easily recycled into high-quality polyol under mild conditions, 60 °C lower than that for the pure foam. Notably, the trace amounts of cesium gathered in recycled polyols stimulate the regenerated PU to undergo self-evolution, improving both flame-retardancy and mechanical properties. Our controllable catalytic cracking strategy paves the way for the self-evolutionary recycling of high-performance firefighting materials.