RESUMO
Calcium phosphate is known as a major component of biological hard tissues. This study aimed to produce calcium phosphate by recycling kneaded surplus gypsum. ß-dihydrate gypsum was derived from commercial dental ß-hemihydrate gypsum, which was mechanically powdered and mixed with the liquid component of a commercial zinc phosphate cement. This mixture was fired at 1,200°C and evaluated by XRD analysis, thermal analysis and scanning electron microscopy (SEM). An acceptable ratio of mixing was 4 g of ß-dihydrate gypsum powder to 1.5 mL of phosphoric acid liquid. XRD peaks were monotonic below 800°C, but new ß-TCP was formed by firing at 900°C or more, although TG-DTA analysis of synthetic ß-TCP suggested that some residual dihydrate gypsum remained in the sample. SEM images indicated a fused-block bone-like structure covered with phosphorus and calcium. These results suggest that production of synthetic ß-TCP is possible through ecological techniques using recycled materials.
Assuntos
Substitutos Ósseos/química , Fosfatos de Cálcio/síntese química , Sulfato de Cálcio/química , Dureza , Temperatura Alta , Microscopia Eletrônica de Varredura , Ácidos Fosfóricos , Pós , Difração de Raios X , Cimento de Fosfato de Zinco/químicaRESUMO
This study aimed to develop a dental investment for titanium casting. ZrO(2) and Al(2)O(3) were selected as refractory materials to prepare three investments (Codes: A-C) according to the quantity of Zr. Al(2)O(3) cement was used as a binder at a ratio of 15%, they were mixed with special mixing liquid. B1 was used as a control mixed with water. Fundamental examinations were statistically evaluated. A casting test was performed with investment B. Fluidities, setting times, and green strengths showed no remarkable differences; however, they were significantly different from those of B1. Expansion values for A, B, C, and B1 at 850°C were 1.03%±0.08%, 1.96%±0.17%, 4.35%±0.23%, and 1.50%±0.28%, respectively. Castings were covered by only small amounts of mold materials. The hardness test showed no significant differences between castings from B and the ones from commercial investments. The experimental special mixing liquid effectively reduced the water/powder ratio and improved the strength and thermal expansion.