RESUMO
Due to the biodegradable and biocompatible nature of chitin and chitosan, they are extensively used in the synthesis of hydrogels for various applications. In this work, deacetylation of chitin is carried out with alkaline poly(dimethyldiallylammonium-hydroxide) that gave a higher amount of water-soluble chitin (with 84 % of the degree of deacetylation = chitosan0.84) compared to deacetylation using NaOH. The water-soluble chitosan0.84 is used as intercalating chains for the preparation of acrylic acid and vinylimidazole-based hydrogels. The quaternization of imidazole groups is done with 1,ω-dibromoalkanes, which sets off the crosslinking in the above polymer network. A set of three chitosan0.84 intercalated hydrogels, namely Cs-C4-hydrogel, Cs-C5-hydrogel, and Cs-C10-hydrogel are prepared bearing butyl, pentyl, and decyl chains as respective crosslinkers. The swell ratios of these intercalated hydrogels are compared with those of non-intercalated hydrogels (C4-hydrogel, C5-hydrogel, and C10-hydrogel). Chitosan0.84 intercalated Cs-C10-hydrogel has excellent swelling properties (2330 % swelling ratio) among six synthesized hydrogels. SEM analysis reveals that decyl crosslinker-bearing hydrogels are highly porous. The multi-functionality of Cs-C10-hydrogel and C10-hydrogel is explored towards -the controlled release of paracetamol/urea, and methyleneblue dye absorption. These studies disclose that chitosan0.84 intercalated hydrogels are showing superior-swelling behavior, high paracetamol/urea loading capacities and better dye entrapment than their non-intercalated counterparts.