RESUMO
STATEMENT OF PROBLEM: The mechanical properties of 3 dimensionally (3D) printed zirconia have been reported to be comparable with those of milled zirconia, except for the flexural strength. However, most previous studies tested 3 mol% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP), making it necessary to study 3D printed zirconia with 4 mol% yttria content (4Y-TZP). PURPOSE: The purpose of this in vitro study was to compare the flexural strength of 3D printed 4Y-TZP with 3Y-TZP materials and milled 4Y-TZP. MATERIAL AND METHODS: A total of 80 disk specimens (Ø15×1.5 mm) were fabricated and divided into 4 groups (n=20) using the fabrication method and yttria content: milled 3Y-TZP (Katana HT; Kuraray Noritake), 3D printed 3Y-TZP (TZ-3Y-E; Tosoh), milled 4Y-TZP (Katana STML; Kuraray Noritake), and 3D printed 4Y-TZP (3DMAT; Genoss). The biaxial flexural strength was determined with a piston-on-3-ball test (n=15). The flexural strength of each specimen was measured, and the Weibull modulus (m) and characteristic strength (σ0) were estimated from the fracture load distribution. Two intact and fractured specimens were examined with scanning electron microscopy (SEM). The crystalline phase of the specimens in each group was identified through X-ray diffraction (XRD) analysis (n=5). A 1-way ANOVA was used to compare the flexural strength among different groups. Subsequently, pairwise comparisons were conducted with the Tukey post hoc method (α=.05). RESULTS: The flexural strength of 3D printed 4Y-TZP was significantly higher than that of milled 4Y-TZP (P<.001). In contrast, the flexural strength of 3D printed 3Y-TZP was significantly lower than that of milled 3Y-TZP (P<.001). X-ray diffraction (XRD) analysis revealed that the tetragonal phase was the dominant phase in all groups, with the identification of some cubic phase peaks. CONCLUSIONS: Three dimensionally printed 4Y-TZP showed significantly higher flexural strength than milled 4Y-TZP and exhibited a clinically acceptable flexural strength exceeding 800 MPa.
Assuntos
Resistência à Flexão , Impressão Tridimensional , Ítrio , Zircônio , Microscopia Eletrônica de VarreduraRESUMO
BACKGROUND: The study on oral health-related quality of life (OHRQoL) of disabled patients is rare but critical for welfare of patients. The aim of this study was to examine the effect of fixed implants in edentulous areas on OHRQoL in Korean disabled patients. METHODS: The OHRQoL of 63 disabled individuals was evaluated using the Oral Health Impact Profile (OHIP)-14 questionnaires and studied by potential affecting variables such as age, sex, disability severity, and time of disability acquisition. Wilcoxon-signed rank tests were used to examine the OHIP-14 scores for those who had pre/post-fixed implants. Multiple linear regression analysis was used to examine the relationships between factors and OHIP-14 scores before and after implants. A partial correlation analysis was also performed to determine which variables influenced OHIP-14 scores before and after treatment. The Mann-Whitney test was employed for sex and time of disability acquisition analysis (α = 0.05). RESULTS: Significant improvement was found in OHIP-14 post-implant treatment scores (P < .001). After implant treatment, the severity of disability produced significantly different results (P = .009). Pearson's correlation coefficient between severity of disability and pre/post-implant OHIP-14 scores was 0.265 (P = .030). After controlling for severity of disability, the results showed older patients had lower OHIP-14 scores (P = .032). No differences were found for sex or time of disability acquisition (congenital vs. acquired). CONCLUSIONS: Fixed implant treatment improved OHRQoL for disabled patients, and the severity of disability was positively correlated with improvement of OHRQoL. For patients with a similar level of disability, the OHRQoL decreased with age.