Macroporous photocrosslinked elastomer scaffolds containing microposity: preparation and in vitro degradation properties.

The engineering of soft tissue would benefit from the development of effective biodegradable scaffolds capable of dynamic, elastic loading. For this purpose, highly porous, elastomeric scaffolds containing microporous struts were prepared using a dual porogen approach and a photocrosslinkable elastomer. The combination of paraffin microbeads distributed through a water-in-[star-poly(lactide-co-epsilon-caprolactone) triacrylate dissolved in ethyl acetate] emulsion followed by photocrosslinking generated a macroporous foam scaffold of average porosities between 90% to 93%, with an average pore diameter of 104 +/- 31 microm with struts containing micropores of 3.1 +/- 2 microm average diameter. The mechanical properties of the scaffolds were readily manipulatable by altering the molecular weight of the star-poly(lactide-co-epsilon-caprolactone) triacrylate prepolymer used. The elastomer scaffolds degraded at the same rate as nonporous polymer samples of the same molecular weight, and exhibited similar changes in mass loss, mechanical properties, and sol fraction during in vitro degradation as found with the nonporous scaffolds. The modulus and stress at break of the scaffolds decreased continuously during degradation while the strain at break remained constant. These scaffolds show potential for use in the engineering of soft tissues.

Surface modifications of photocrosslinked biodegradable elastomers and their influence on smooth muscle cell adhesion and proliferation.

Photocrosslinked, biodegradable elastomers based on aliphatic polyesters have many desirable features as scaffolds for smooth muscle tissue engineering. However, they lack cell adhesion motifs. To address this shortcoming, two different modification procedures were studied utilizing a high and a low crosslink density elastomer: base etching and the incorporation of acryloyl-poly(ethylene glycol) (PEG)-Gly-Arg-Gly-Asp-Ser (GRGDS) into the elastomer network during photocrosslinking. Base etching improved surface hydrophilicity without altering surface topography, but did not improve bovine aortic smooth muscle cell adhesion. Incorporation of PEG-GRGDS into the elastomer network significantly improved cell adhesion for both high and low crosslink density elastomers, with a greater effect with the higher crosslink density elastomer. Incorporation of GRGDS into the high crosslink density elastomer also enhanced smooth muscle cell proliferation, while proliferation on the low crosslink density unmodified, base etched, and PEG-GRGDS incorporated elastomers was significantly greater than on the high crosslink density unmodified and base etched elastomer.