RESUMO
A new homochiral BINAPDA-Zr-MOF was prepared by a new chiral organic linker of (R)-4,4'-(6,6'-dichloro-2,2'-diethoxyl-[1,1'-binaphthalene]-4,4'-diyl)dibenzoic acid (R-L) and ZrCl4 under solvothermal conditions. Its structure was determined by Pawley refinement on the basis of the measured PXRD pattern determined for BINAPDA-Zr-MOF, and it showed that the obtained chiral MOF crystallized in the F23 space group with the same topological structure as that of UiO-66. The obtained BINAPDA-Zr-MOF can be a very active catalyst to catalyze aldehyde cyanosilylation. In addition, the chiral BINAPDA-Zr-MOF was a typical solid catalyst, which was proved by a hot leaching test; moreover, it could be reused at least five times without loss of its catalytic activity and enantioselectivity.
RESUMO
A new Mn(II) metal-organic framework (MOF) 1 was synthesized by the combination of 4,4,4-trifluoro-1-(4-(pyridin-4-yl)phenyl)butane-1,3-dione (L) and Mn(OAc)2 in solution. 1 features a threefold-interpenetrating NbO net containing honeycomb-like channels, in which the opposite Mn(II)···Mn(II) distance is 23.5075(10) Å. Furthermore, 1 can be an ideal platform to support Pd-Au bimetallic alloy nanoparticles to generate a composite catalytic system of Pd-Au@Mn(II)-MOF (2). 2 can be a highly active bifunctional heterogeneous catalyst for the one-pot tandem synthesis of imines from benzyl alcohols and anilines and from benzyl alcohols and benzylamines.
RESUMO
A new composite Au@Cu(II)-MOF catalyst has been synthesized via solution impregnation and full characterized by HRTEM, SEM-EDS, XRD, gas adsorption-desorption, XPS, and ICP analysis. It has been shown here that the Cu(II)-framework can be a useful platform to stabilize and support gold nanoparticles (Au NPs). The obtained Au@Cu(II)-MOF exhibits a bifunctional catalytic behavior and is able to promote selective aerobic benzyl alcohol oxidation-Knoevenagel condensation in a stepwise way.
RESUMO
A new 3D porous Cu(II)-MOF (1) was synthesized based on a ditopic pyridyl substituted diketonate ligand and Cu(OAc)2 in solution, and it features a 3D NbO motif which is determined by the X-ray crystallography. Furthermore, the Pd NPs-loaded hybrid material Pd@Cu(II)-MOF (2) was prepared based on 1 via solution impregnation, and its structure was confirmed by HRTEM, SEM, XRPD, gas adsorption-desorption, and ICP measurement. 2 exhibits excellent catalytic activity (conversion, 93% to >99%) and selectivity (>99% to benzaldehydes) for various benzyl alcohol substrates (benzyl alcohol and its derivatives with electron-withdrawing and electron-donating groups) oxidation reactions in air. In addition, 2 is a typical heterogeneous catalyst, which was confirmed by hot solution leaching experiment, and it can be recycled at least six times without significant loss of its catalytic activity and selectivity.