Ferromagnetic Fluctuations in the Heavily Overdoped Regime of Single-Layer High-Tc Cuprate Superconductors.

To investigate proposed ferromagnetic fluctuations in the so-called single-layer Bi-2201 and La-214 high-Tc cuprates, we performed magnetization and electrical resistivity measurements using single-layer Tl-2201 cuprates Tl2Ba2CuO6+δ and La-214 La2-xSrxCuO4 in the heavily overdoped regime. Magnetization of Tl2Ba2CuO6+δ and La2-xSrxCuO4 exhibited the tendency to be saturated in high magnetic fields at low temperatures, suggesting the precursor behavior toward the formation of a ferromagnetic order. It was found that the power of temperature n obtained from the temperature dependence of the electrical resistivity is ~4/3 and ~5/3 for Bi-2201 and La2-xSrxCuO4, respectively, and is ~4/3 at high temperatures and ~5/3 at low temperatures in Tl2Ba2CuO6+δ. These results suggest that two- and three-dimensional ferromagnetic fluctuations exist in Bi-2201 and La2-xSrxCuO4, respectively. In Tl2Ba2CuO6+δ, it is suggested that the dimension of ferromagnetic fluctuations is two at high temperatures and three at low temperatures, respectively. The dimensionality of ferromagnetic fluctuations is understood in terms of the dimensionality of the crystal structure and the bonding of atoms in the blocking layer.

Fabrication of High-Temperature Quasi-Two-Dimensional Superconductors at the Interface of a Ferroelectric Ba_{0.8}Sr_{0.2}TiO_{3} Film and an Insulating Parent Compound of La_{2}CuO_{4}.

We report the first observation of superconductivity in a heterostructure consisting of an insulating ferroelectric film (Ba_{0.8}Sr_{0.2}TiO_{3}) grown on an insulating parent compound of La_{2}CuO_{4} with [001] orientation. The heterostructure was prepared by magnetron sputtering on a nonatomically flat surface with inhomogeneities of the order of 1-2 nm. The measured superconducting transition temperature T_{c} is about 30 K. We have shown that superconductivity is confined near the interface region. Application of a weak magnetic field perpendicular to the interface leads to the appearance of the finite resistance. That confirms the quasi-two-dimensional nature of the superconductive state. The proposed concept promises ferroelectrically controlled interface superconductivity which offers the possibility of novel design of electronic devices.

Development of Ferromagnetic Fluctuations in Heavily Overdoped (Bi,Pb)_{2}Sr_{2}CuO_{6+δ} Copper Oxides.

We demonstrate the presence of ferromagnetic (FM) fluctuations in the superconducting and nonsuperconducting heavily overdoped regimes of high-temperature superconducting copper oxides, using (Bi,Pb)_{2}Sr_{2}CuO_{6+δ} (Bi-2201) single crystals. Magnetization curves exhibit a tendency to be saturated in high magnetic fields at low temperatures in the heavily overdoped crystals, which is probably a precursor phenomenon of a FM transition at a lower temperature. Muon spin relaxation detects the enhancement of spin fluctuations at high temperatures below 200 K. Correspondingly, the ab-plane resistivity follows a 4/3 power law in a wide temperature range, which is characteristic of metals with two-dimensional FM fluctuations due to itinerant electrons. As the Wilson ratio evidences the enhancement of spin fluctuations with hole doping in the heavily overdoped regime, it is concluded that two-dimensional FM fluctuations reside in the heavily overdoped Bi-2201 cuprates, which is probably related to the decrease in the superconducting transition temperature in the heavily overdoped cuprates.