RESUMO
Current study provides insight on the feasibility of polylactic acid (PLA) integrated with (1:1 ratio) of essential oils belonging to Ocimum gratissimum (OG) and Mentha spicata (MS) for prevention of major stored insect pests (Sitophilus oryzae and Oryzophilus surinamensis) in Sorghum and Pearl millet. A combination of OG and MS essential oils (1:1) was incorporated into the PLA polymer matrix. Further, SPME analysis of synthesized PLA showed the presence of volatiles corresponding to carvone (6.44 %) and thymol (6.22 %). Synthesized PLA composites were tested against S. oryzae and O. surinamensis using Sorghum and Pearl millets, and insect mortality was equivalent to commercial super bags (CSB). The head space oxygen decreased significantly in CSB and slightly in PLA bags. Thickness of EO blended PLA composite was increased (99 µm), tensile strength (23.94 MPa), WVTR (1.42 g/m2.hr) analysis, significant folding ability, and swelling capacity (0.24 %) showed slight reduction in composite film. TGA showed good thermal stability (334ËC) and XRD displayed the increased crystallinity (38.35 %) in PLAOM films, SEM and FTIR analysis of the synthesized composite films revealed complete homogenization of EO and PLA matrix. In addition, SEM analysis of insects (control & treated) revealed less topology changes in the elytra. Biodegradability study confirmed the weight loss in PLA films. Hence, current approach of using composite EO's with PLA offers sustainable solution for prevention of infestation during storage of millets.
RESUMO
Naturally derived essential oils (EOs) from Ocimum basilicum (OB) and Ocimum gratissimum (OG) were incorporated in polylactic acid (PLA) matrix with concentration of 2.5 % and 5 % respectively by solvent casting method, with an aim to develop insecticidal polymer pouches (insect proof polymer pouches). The major components following GC-MS analysis revealed the presence of EOs as estragole (69.998 %) in OB and thymol (29.843 %) in OG. The developed films with EOs showed remarkable insecticidal activity with 100 % and 80 % mortality rate for OB and OG respectively at 2.5 % concentration against rice weevil (Sitophilus oryzae). While, both OB and OG EOs observed 100 % mortality against pulse beetle (Callosobruchus chinensis) after 96 h exposure in presence of grain conditions and the insecticidal efficacy was equivalent to the commercial hermetic bags (CSB). The physical property of film showed increase in the film thickness in EO-PLA films whereas the mechanical properties of EO-PLA films matrix have increased the polymer flexibility with decreasing tensile strength (TS) and Youngs modulus (EM) as TS OB 5 %, OG 5 % - 15.64 MPa, 17.66 MPa respectively. While, water vapour transmission rate (WVTR) was reduced to 0.015 g/m2.hr, optical characteristics showed slight significant change in colour and FTIR spectra exhibited a change in -OH stretching compared to blank PLA matrix. The surface morphology of the blank and EO embedded PLA films visualized by SEM depicted a complete homogenization of essential oils in the PLA matrix.