RESUMO
This paper presents a study and comparison of surface effects induced by picosecond and nanosecond laser modification of a Ti6Al4V alloy surface under different ambient conditions: air and argon- and nitrogen-rich atmospheres. Detailed surface characterization was performed for all experimental conditions. Damage threshold fluences for picosecond and nanosecond laser irradiation in all three ambient conditions were determined. The observed surface features were a resolidified pool of molten material, craters, hydrodynamic effects and parallel periodic surface structures. Laser-induced periodic surface structures are formed by multi-mode-beam nanosecond laser action and picosecond laser action. Crown-like structures at crater rims are specific features for picosecond Nd:YAG laser action in argon-rich ambient conditions. Elemental analysis of the surfaces indicated nitride compound formation only in the nitrogen-rich ambient conditions. The constituents of the formed plasma were also investigated. Exploring the impact of process control parameters on output responses has been undertaken within the context of laser modification under different environmental conditions. Parametric optimization of the nanosecond laser modification was carried out by implementing an advanced method based on Taguchi's parametric design and multivariate statistical techniques, and optimal settings are proposed for each atmosphere.
RESUMO
Spatially resolved, time-integrated optical emission spectroscopy was applied for investigation of copper plasma produced by a nanosecond infrared (IR) transversely excited atmospheric (TEA) CO2 laser, operating at 10.6 µm. The effect of surrounding air pressure, in the pressure range 0.1 to 1013 mbar, on plasma formation and its characteristics was investigated. A linear dependence of intensity threshold for plasma formation on logarithm of air pressure was found. Lowering of the air pressure reduces the extent of gas breakdown, enabling better laser-target coupling and thus increases ablation. Optimum air pressure for target plasma formation was 0.1 mbar. Under that pressure, the induced plasma consisted of two clearly distinguished and spatially separated regions. The maximum intensity of emission, with sharp and well-resolved spectral lines and negligibly low background emission, was obtained from a plasma zone 8 mm from the target surface. The estimated excitation temperature in this zone was around 7000 K. The favorable signal to background ratio obtained in this plasma region indicates possible analytical application of TEA CO2 laser produced copper plasma. Detection limits of trace elements present in the Cu sample were on the order of 10 ppm (parts per million). Time-resolved measurements of spatially selected plasma zones were used to find a correlation between the observed spatial position and time delay.