Effect of degeneration on the six degree of freedom mechanical properties of human lumbar spine segments.

While the effects of disc degeneration on compression and rotation motions have been studied, there is no data for shear loading. Clinical research has shown that those with low back pain (a potential consequence of degeneration) experience a 75% greater lateral shear force than those without it. Therefore, the aim was to compare the effect of degeneration on spine segment stiffness and phase angle in each of six degree of freedom (6DOF) loading directions. Fourteen intact functional spinal units (FSU) were dissected from human lumbar spines (mean (SD) age 76.2 (11) years, Thompson grades 3 (N = 5, mild), 4 (N = 6, moderate), 5 (N = 3, severe)). Each FSU was tested in ±6DOFs while subjected to a physiological preload, hydration, and temperature (37°C) conditions in a hexapod robot. A one-way ANOVA between degenerated groups was performed on stiffness and phase angle for each DOF. Significant differences in stiffness were found between mild and moderate degenerative groups in lateral shear (p = 0.001), and axial rotation (p = 0.001), where moderate degeneration had decreased stiffness. For phase angle, significant differences were seen in anterior shear (p = 0.017), and axial rotation (p = 0.026), where phase angle for mild degeneration was less than moderate. Trends of stiffness and phase angle changes between degenerative groups were similar within each DOF. Clinically, the identification of the DOFs that are most affected by degeneration could be used in rehabilitation to improve supplemental stabilization of core muscle groups. © 2016 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 34:1399-1409, 2016.

Effect of potting technique on the measurement of six degree-of-freedom viscoelastic properties of human lumbar spine segments.

Polymethyl methacrylate (PMMA) and Wood's Metal are fixation media for biomechanical testing; however, the effect of each potting medium on the measured six degree-of-freedom (DOF) mechanical properties of human lumbar intervertebral discs is unknown. The first aim of this study was to compare the measured 6DOF elastic and viscoelastic properties of the disc when embedded in PMMA compared to repotting in Wood's Metal. The second aim was to compare the surface temperature of the disc when potted with PMMA and Wood's Metal. Six human lumbar functional spinal units (FSUs) were first potted in PMMA, and subjected to overnight preload in a saline bath at 37 °C followed by five haversine loading cycles at 0.1 Hz in each of 6DOF loading directions (compression, left/right lateral bending, flexion, extension, left/right axial rotation, anterior/posterior, and lateral shear). Each specimen was then repotted in Wood's Metal and subjected to a 2-h re-equilibrating preload followed by repeating the same 6DOF tests. Outcome measures of stiffness and phase angle were calculated from the final loading cycle in each DOF and were expressed as normalized percentages relative to PMMA (100%). Disc surface temperatures (anterior, left/right lateral) were measured during potting. Paired t-tests (with alpha adjusted for multiple DOF) were conducted to compare the differences in each outcome parameter between PMMA and Wood's Metal. No significant differences in stiffness or phase angle were found between PMMA and Wood's Metal. On average, the largest trending differences were found in the shear DOFs for both stiffness (approximately 35% greater for Wood's Metal compared to PMMA) and phase angle (approximately 15% greater for Wood's Metal). A significant difference in disc temperature was found at the anterior surface after potting with Wood's Metal compared to PMMA, which did not exceed 26 °C. Wood's Metal is linear elastic, stiffer than PMMA and may reduce measurement artifact of potting medium, particularly in the shear directions. Furthermore, it is easier to remove than PMMA, reuseable, and cost effective.