Design of a multi-walled carbon nanotube field emitter with micro vacuum gauge.

The variation of vacuum level inside a field emission device when electron is emitted from multi-walled carbon nanotubes (MWCNTs) by electric field was measured where MWCNT gauge packaged with a vacuum device was used to measure the degree of a vacuum until the end of the vacuum device life. It was found that the electrical properties of MWCNTs altered with the degree of a vacuum. We fabricated MWCNT gauge which were printed and pasted by the screen printer. In this paper, we report the successful detection of the ionization of gases in vacuum state.

Detection of a CO and NH3 gas mixture using carboxylic acid-functionalized single-walled carbon nanotubes.

Carbon nanotubes (CNT) are extremely sensitive to environmental gases. However, detection of mixture gas is still a challenge. Here, we report that 10 ppm of carbon monoxide (CO) and ammonia (NH3) can be electrically detected using a carboxylic acid-functionalized single-walled carbon nanotubes (C-SWCNT). CO and NH3 gases were mixed carefully with the same concentrations of 10 ppm. Our sensor showed faster response to the CO gas than the NH3 gas. The sensing properties and effect of carboxylic acid group were demonstrated, and C-SWCNT sensors with good repeatability and fast responses over a range of concentrations may be used as a simple and effective detection method of CO and NH3 mixture gas.

Sensing properties of polyethylenimine coated carbon nanotubes in oxidized oil.

Chemical detection is still a continuous challenge when it comes to designing single-walled carbon nanotube (SWCNT) sensors with high selectivity, especially in complex chemical environments. A perfect example of such an environment would be in thermally oxidized soybean oil. At elevated temperatures, oil oxidizes through a series of chemical reactions that results in the formation of monoacylglycerols, diacylglycerols, oxidized triacylglycerols, dimers, trimers, polymers, free fatty acids, ketones, aldehydes, alcohols, esters, and other minor products. In order to detect the rancidity of oxidized soybean oil, carbon nanotube chemiresistor sensors have been coated with polyethylenimine (PEI) to enhance the sensitivity and selectivity. PEI functionalized SWCNTs are known to have a high selectivity towards strong electron withdrawing molecules. The sensors were very responsive to different oil oxidation levels and furthermore, displayed a rapid recovery of more than 90% in ambient air without the need of heating or UV exposure.

Exploring the chemical sensitivity of a carbon nanotube/green tea composite.

Single-walled carbon nanotubes (SWNTs) possess unique electronic and physical properties, which make them very attractive for a wide range of applications. In particular, SWNTs and their composites have shown a great potential for chemical and biological sensing. Green tea, or more specifically its main antioxidant component, epigallocatechin gallate (EGCG), has been found to disperse SWNTs in water. However, the chemical sensitivity of this SWNT/green tea (SWNT/EGCG) composite remained unexplored. With EGCG present, this SWNT composite should have strong antioxidant properties and thus respond to reactive oxygen species (ROS). Here we report on fabrication and characterization of SWNT/EGCG thin films and the measurement of their relative conductance as a function of H(2)O(2) concentrations. We further investigated the sensing mechanism by Fourier transform infrared (FTIR) spectroscopy and field-effect transistor measurements (FET). We propose here that the response to H(2)O(2) arises from the oxidation of EGCG in the composite. These findings suggest that SWNT/green tea composite has a great potential for developing simple resistivity-based sensors.

Synthesis of carbon-nitrogen nanostructures by hot isostatic pressure apparatus and their field emission properties.

Carbon-nitrogen (CN) nanofibers were synthesized in argon-nitrogen gas mixture at 75 MPa by high isostatic pressure (HIP) apparatus using a graphite resistive heater. The CN nanofibers were grown in random with the diameter of about 200 nm and the length over 5 microm. The structures obtained can be divided bamboo-like, spring-like, and bead necklace-like CN nanofibers. The nitrogen content of up to 8.4% was found in CN nanofibers by EELS analysis. Field emission results showed that the density of field emitters and the field enhancement factors changed by surface treatments and that CN nanofibers contained glass frit. The screen-printed CN nanofiber had a turn-on field of 2 V/microm.

Synthesis of double-walled carbon nanotubes by catalytic chemical vapor deposition and their field emission properties.

Double-walled carbon nanotubes (DWCNTs) were synthesized by catalytic chemical vapor deposition using Fe-Mo/MgO as a catalyst at 1000 degrees C under the mixture of methane and hydrogen gas. The nanotubes were purified by acid but were not damaged. Thermogravimetric analysis revealed the purity of the tubes to be about 90%. The high-resolution transmission electron microscopy image showed that DWCNTs have inner tube diameters of 1.4-2.6 nm and outer tube diameters of 2.3-3.4 nm. We observed radial breathing modes in Raman spectra, which are related to the diameter of inner nanotubes. The purified DWCNTs were mixed with organic vehicles and glass frit, and then they were screen-printed on glass substrate coated with indium tin oxide. The field emission properties of the screen-printed DWCNT films were examined by varying the amount of glass frit ingredient within the DWCNT paste. The results showed that DWCNT emitters had good emission properties such as turn-on field of 1.33-1.78 V/microm and high brightness. When the applied anode voltage was gradually increased, current density and brightness became saturated. We also observed DWCNTs adsorbed on the anode plate; they were DWCNTs peeled off from the cathode plate for field emission measurement.