RESUMO
Carbon nanotubes (CNTs) filled natural rubber (NR) composites with various CNT contents at 0, 1, 2, 3, 4 and 5 phr were prepared by latex mixing method using glutaraldehyde as curing agent. This work aims to improve the electrical and mechanical properties of CNT filled NR vulcanizates. The CNT dispersion of NR composites was clarified using dispersion grader, optical microscopy and scanning electron microscopy. The electrical properties of NR composites in the existing of CNT networks were studied by following the well-known percolation theory. It was observed that the NR composites exhibited low percolation threshold at 0.98 phr of CNT. Moreover, a three-dimensional network formation of CNT in the NR composites was observed and it is indicated by the t-value of 1.67. The mechanical properties of NR composites in terms of modulus, tensile strength and hardness properties were increased upon the addition of CNT to the optimum mechanical properties at 1 phr of CNT. Therefore, the present work is found the novelty of the study that the conductive rubber latex film can be produced using GA as low-temperature curing agent which enhanced good electrical properties. Moreover, this work is found to be beneficial in case of conductive rubber latex film that requires high modulus at low strain. The additional advantage of this system is the curing process occurs at low-temperature using GA and it can be easily processed.
RESUMO
Novel composite based on rubber and modified bentonite clay (Clay) was investigated. The modified bentonite clay was developed by dispersing in ethanol solutions (Et-OH) using ultrasonic method. The effect of Et-OH on the dispersion of bentonite clay at various mixing temperatures in case of different type of rubber matrix, i.e., natural rubber (NR), epoxidized natural rubber (ENR25, ENR50) on dynamic mechanical rheology, Payne effect, XRD and mechanical properties of rubber composites were studied in detail. The bentonite clay dispersion in Et-OH at a mixing temperature of 80 °C improves the intercalation and exfoliation in rubber chains. Bentonite clay is highly intercalated in ENR 50-Clay composite, which can be confirmed from its superior mechanical properties. The results indicated that sonication of bentonite clay in Et-OH improves the interlayer spacing of bentonite clay by partial intercalation of rubber matrix.
RESUMO
Natural rubber from different Hevea braziliensis clones, namely RRIM600, RRIT251, PB235 and BPM24, exhibit unique properties. The influences of the various fresh natural rubber latex and cream concentrated latex on the non-rubber components related properties were studied. It was found that the fresh natural rubber latex exhibited differences in their particle size, which was attributed to the non-rubber and unique signature of clones which affect various properties. Meanwhile, the cream concentrated latex showed the protein contents, surface tension, and color of creamed latex to be lower than the fresh natural latex. However, TSC, DRC, viscosity, particle size and green strength of concentrated latex were found to be higher than the fresh natural latex. This is attributed to the incorporation of HEC molecules. Also, the rubber particle size distribution in the RRIM600 clone exhibited a large particle size and uniform distribution, showing good mechanical properties when compared to the other clones. Furthermore, the increased green strength in the RRIM600 clone can be attributed to the crystallization of the chain on straining and chain entanglement. These experimental results may provide benefits for manufacturing rubber products, which can be selected from a suitable clone.
RESUMO
Failure in the prevention of cross-transmission from contaminated gloves has been recognized as an important factor that contributes to the spread of several healthcare-associated infections. Ex situ coating process with silver nanoparticles (AgNPs) using Eucalyptus citriodora ethanolic leaf extract as reducing and capping agents to coat glove surfaces has been developed to prevent this mode of transmission. Elemental analysis of coated gloves showed 24.8 Wt% silver densely adhere on the surface. The coated gloves fully eradicated important hospital-acquired pathogens including Gram-positive bacteria, Gram-negative bacteria, and yeasts within 1 h. The coated gloves showed significant reduction, an average of five logs when tested against all standard strains and most clinical isolates (p < 0.01). Following prolonged exposure, the coating significantly reduced the numbers of most adhered pathogenic species, compared with uncoated gloves (p < 0.0001). AgNPs-coated gloves reduced microbial adhesion of mixed-species biofilms. A series of contamination and transmission assays demonstrated no transmission of viable organisms. Biocompatibility analysis confirmed high viability of HaCaT and L929 cells at all concentrations of AgNPs tested. The coated gloves were non-toxic with direct contact with L929 cells. The highly efficacious AgNPs-coated gloves potentially provide additional protection against transmission of healthcare-associated infections.