RESUMO
We investigated the influence of two passivating molecules containing a PâO group on the performance of quasi-2D Dion-Jacobson halide perovskite light-emitting diodes, namely, triphenylphosphine oxide (TPPO) and diphenyl-4-triphenylsilylphenyl phosphine oxide (TSPO1). We found that both passivating molecules lead to increased efficiency compared to control devices, while they had opposite effects on device lifetime, with a decrease observed for TPPO and an increase observed for TSPO1. The two passivating molecules resulted in differences in energy-level alignment, electron injection, film morphology and crystallinity, and ion migration during operation. While TPPO resulted in improved photoluminescence decay times, overall higher maximum external quantum efficiency (EQE) and device lifetime were obtained for TSPO1 compared to TPPO (14.4% vs 12.4% EQE, 341 min vs 42 min T50).
RESUMO
Hybrid organic-inorganic perovskites have attracted great attention as the next generation materials for photovoltaic and light-emitting devices. However, their environment instability issue remains as the largest challenge for practical applications. Recently emerging two-dimensional (2D) perovskites with Ruddlesden-Popper structures are found to greatly improve the stability and aging problems. Furthermore, strong confinement of excitons in these natural quantum-well structures results in the distinct and narrow light emission in the visible spectral range, enabling the development of spectrally tunable light sources. Besides the strong quasi-monochromatic emission, some 2D perovskites composed of the specific organic cations and inorganic layer structures emit a pronounced broadband emission. Herein, we report the light-emitting properties and the degradation of low-dimensional perovskites consisting of the three shortest alkylammonium spacers, mono-ethylammonium (EA), n-propylammonium (PA), and n-butylammonium (BA). While (BA)2PbI4 is known to form well-oriented 2D thin films consisting of layers of corner-sharing PbI6 octahedra separated by a bilayer of BA cations, EA with shorter alkyl chains tends to form other types of lower-dimensional structures. Nevertheless, optical absorption edges of as-prepared fresh EAPbI3, (PA)2PbI4, and (BA)2PbI4 are obviously blue-shifted to 2.4-2.5 eV compared to their 3D counterpart, methylammonium lead iodide (MAPbI3) perovskite, and they all emit narrow excitonic photoluminescence. Furthermore, by carefully optimizing deposition conditions, we have achieved a predominantly 2D structure for (PA)2PbI4. However, unlike (BA)2PbI4, upon exposure to ambient environment, (PA)2PbI4 readily transforms to a different crystal structure, exhibiting a prominently broadband light from â¼500 to 800 nm and a gradual increase in intensity as structural transformation proceeds.
RESUMO
We have investigated lead adsorption on different forms of nanostructured carbon, namely multiwall carbon nanotubes (MWCNT) and reduced graphene oxide (RGO) functionalized with different functional groups (hydroxyl, carboxyl, and amino groups). We found that the same functional group does not result in the same performance trends for different nanostructured carbons. Drastically different behavior was observed for the amino-group functionalization, where a significant improvement is observed for MWCNT, while worse performance compared to non-functionalized material is obtained for RGO. On the other hand, hydroxyl and carboxyl group functionalization improves the lead adsorption regardless of the form of carbon. The best performing RGO sample, namely carboxyl group functionalized one, exhibited maximum lead adsorption capacity of 298.49 mg g-1 which was significantly higher than that of the best performing MWCNT sample (amino-functionalized MWCNT, 58.547 mg g-1).