Electrodeposited Ni(x)Co(3-x)O4 nanostructured films as bifunctional oxygen electrocatalysts.

Nanostructured Ni(x)Co(3-x)O4 films serve as effective electrocatalysts for both the oxygen reduction and oxygen evolution reactions in alkaline electrolyte.

Recrystallized arrays of bismuth nanowires with trigonal orientation.

We demonstrate methods to improve the crystalline-quality of free-standing Bi nanowires arrays on a Si substrate and enhance the preferred trigonal orientation for thermoelectric performance by annealing the arrays above the 271.4 °C Bi melting point. The nanowires maintain their geometry during melting due to the formation of a thin Bi-oxide protective shell that contains the molten Bi. Recrystallizing nanowires from the melt improves crystallinity; those cooled rapidly demonstrate a strong trigonal orientation preference.

Graphene-Ni-α-MnO2 and -Cu-α-MnO2 nanowire blends as highly active non-precious metal catalysts for the oxygen reduction reaction.

Graphene-like carbon-Ni-α-MnO(2) and -Cu-α-MnO(2) blends can serve as effective catalysts for the oxygen reduction reaction with activities comparable to Pt/C.

In situ transmission electron microscopy observation of pulverization of aluminum nanowires and evolution of the thin surface Al2O3 layers during lithiation-delithiation cycles.

Lithiation-delithiation cycles of individual aluminum nanowires (NWs) with naturally oxidized Al(2)O(3) surface layers (thickness 4-5 nm) were conducted in situ in a transmission electron microscope. Surprisingly, the lithiation was always initiated from the surface Al(2)O(3) layer, forming a stable Li-Al-O glass tube with a thickness of about 6-10 nm wrapping around the NW core. After lithiation of the surface Al(2)O(3) layer, lithiation of the inner Al core took place, which converted the single crystal Al to a polycrystalline LiAl alloy, with a volume expansion of about 100%. The Li-Al-O glass tube survived the 100% volume expansion, by enlarging through elastic and plastic deformation, acting as a solid electrolyte with exceptional mechanical robustness and ion conduction. Voids were formed in the Al NWs during the initial delithiation step and grew continuously with each subsequent delithiation, leading to pulverization of the Al NWs to isolated nanoparticles confined inside the Li-Al-O tube. There was a corresponding loss of capacity with each delithiation step when arrays of NWs were galvonostatically cycled. The results provide important insight into the degradation mechanism of lithium-alloy electrodes and into recent reports about the performance improvement of lithium ion batteries by atomic layer deposition of Al(2)O(3) onto the active materials or electrodes.

New multi-electron high capacity anodes based on nanoparticle vanadium phosphides.

Nanoscale vanadium phosphides can serve as new high capacity anodes in alkaline aqueous electrolytes. Competing corrosion reaction(s) are mitigated with the novel use of an anion exchange membrane providing for capacities as high as 2800 mAh g(-1) @ 100 mA g(-1) discharge rate.

Epitaxial electrodeposition of ZnO on Au(111) from alkaline solution: exploiting amphoterism in Zn(II).

The amphoteric nature of ZnO is used to produce the material from strongly alkaline solution. The solution pH is lowered globally to produce ZnO powder, and it is lowered locally at a Au(111) surface to produce epitaxial films. ZnO powder is precipitated from a solution of 10 mM Zn(II) in 0.25 M NaOH by simply adding 1 M HNO3 to the solution. For the film electrodeposition, the local pH at the electrode surface is decreased by electrochemically oxidizing the ascorbate dianion. The chemically precipitated ZnO powder grows with a sea urchin-like nanostructure, whereas the electrodeposited films have a columnar structure. ZnO electrodeposited onto a Au(111) single crystal has a ZnO(0001)[1011]//Au(111)[110] orientation relationship.