Investigating the exciton dynamics in InGaN/GaN core-shell nanorods using time-resolved cathodoluminescence.

This study examines the exciton dynamics in InGaN/GaN core-shell nanorods using time-resolved cathodoluminescence (TRCL), which provides nanometer-scale lateral spatial and tens of picoseconds temporal resolutions. The focus is on thick (>20 nm) InGaN layers on the non-polar, semi-polar and polar InGaN facets, which are accessible for study due to the unique nanorod geometry. Spectrally integrated TRCL decay transients reveal distinct recombination behaviours across these facets, indicating varied exciton lifetimes. By extracting fast and slow lifetime components and observing their temperature trends along with those of the integrated and peak intensity, the differences in behaviour were linked to variations in point defect density and the degree and density of localisation centres in the different regions. Further analysis shows that the non-polar and polar regions demonstrate increasing lifetimes with decreasing emission energy, attributed to an increase in the depth of localisation. This investigation provides insights into the intricate exciton dynamics in InGaN/GaN nanorods, offering valuable information for the design and development of optoelectronic devices.

Quantitative analysis of carbon impurity concentrations in GaN epilayers by cathodoluminescence.

In this work, a technique for quantifying carbon doping concentrations in GaN:C/AlGaN buffer structures using cathodoluminescence (CL) is presented. The method stems from the knowledge that the blue and yellow luminescence intensity in CL spectra of GaN varies with the carbon doping concentration. By calculating the blue and yellow luminescence peak intensities normalised to the peak GaN near-band-edge intensity for GaN layers of known carbon concentrations, calibration curves that show the change in normalised blue and yellow luminescence intensity with carbon concentration in the 1016 - 1019 cm-3 range were derived at both room temperature and 10 K. The utility of such calibration curves was then examined by testing against an unknown sample containing multiple carbon-doped GaN layers. The results obtained from CL using the normalised blue luminescence calibration curves are in close agreement with those from secondary-ion mass spectroscopy (SIMS). However,the method fails when applying calibration curves obtained from the normalised yellow luminescence likely due to the influence of native VGa defects acting in this luminescence region. Although this work shows that indeed CL can be used as a quantitative tool to measure carbon doping concentrations in GaN:C, it is noted that the intrinsic broadening effects innate to CL can make it difficult to differentiate between the intensity variations in thin ( < 500 nm) multilayered GaN:C structures such as the ones studied in this work.