RESUMO
Background: The aim of this study was to determine if there is a correlation between fluoride release, surface hardness, and diametral tensile strength of restorative glass ionomer cements (GICs). Material and Methods: Conventional (Riva Self Cure) and resin-modified (Riva Light Cure) GICs were used. Thirty-four samples (ø 6 x 3 mm) were prepared for each cement. The kinetics of fluoride release (n=4) was evaluated over 28 days using a fluoride-selective electrode (ISE 4010-C00). The analysis of surface hardness (n=10) was performed using a microhardness tester (Shimadzu HMV-2000, Japan) with a Knoop indenter and a load of 25 gf for 30 seconds. The diametral tensile strength test (n=10) was conducted on a universal testing machine at a speed of 0.75 mm/min. Fluoride release data were analyzed by two-way repeated measures ANOVA and Bonferroni post hoc test, while independent t-test was used for other analyses (α=0.05). Results: Overall, the groups showed higher fluoride release until day 7 and a progressive decrease until day 28. On day 1 and day 21, Riva Self Cure showed a higher level of release than Riva Light Cure (p=0.026). Riva Light Cure showed higher diametral tensile strength (p<0.0001) and surface hardness (p=0.034) than Riva Self Cure. A negative correlation was found, indicating that higher fluoride release is associated with lower surface hardness and diametral tensile strength. Conclusion: Fluoride release and mechanical performance are related properties of GICs, and these properties exhibit different values depending on the type of material. Resin-modified GIC release less fluoride but exhibit better mechanical performance compared to conventional GIC. Key words:Diametral Tensile Strength, Fluoride, Glass Ionomer Cement, Surface Hardness.