A series of highly flexible and environmentally friendly composites based on polydimethylsiloxane (PDMS) filled with 200 nm size ferroelectric BaTiO3 (BTO) particles at different concentrations (from 7 to 23 vol %) have been fabricated by a simple dispersion method. The dielectric, piezoelectric, and ultrasonic properties have been studied. The ferroelectric state of BTO was confirmed by differential scanning calorimetry and ultrasonic spectroscopy. The addition of BTO into PDMS strongly affects the dielectric properties of the composites. At low temperatures close to 160 K, the PDMS matrix exhibits a dielectric anomaly related to a dynamic glass transition, which shifts to higher temperatures as the BTO content increases due to the strong interaction between polymer chains and nanoparticles. Ultrasonic measurements demonstrate the appearance of a piezoelectric voltage signal on a thin plate of the composite with the highest available filler concentration (23 vol %) under longitudinal stress applied by a 10 MHz ultrasonic wave. As a result, at room temperature, the detected signal is characterized by output voltage and specific stored energy values of 10 mV and 367.3 MeV/m2, respectively, followed by a further increase with cooling to 35 mV at 150 K. The proposed BTO/PDMS composite system is thus a potential candidate for nanogenerators, namely, a simple, flexible, and lead-free device converting high-frequency (10 MHz) mechanical vibrations into electrical voltage.
RESUMO
The dielectric/electric properties of the Ni@C (carbon-coated Ni)/epoxy composites and Ni@C/MWCNTs (multi-walled carbon nanotubes)/epoxy composites loaded with fixed MWCNTs amount just below the percolation threshold (0.09 vol.%) and Ni@C at different concentrations up to 1 vol.% were investigated in broad frequency (20 Hz-40 GHz) and temperature (30 K-500 K) regions. In composites with the only Ni@C nanoparticles, the electrical percolation threshold was determined between 10 and 15 vol.%. Above the percolation threshold the dielectric permittivity (ε') and the electrical conductivity (σ) of the composites loaded with Ni@C only are high enough, i.e., ε' = 105 and σ = 0.6 S/m at 100 Hz for composites with 30 vol.% Ni@C, to be used for electromagnetic shielding applications. The annealing to 500 K was proved to be an effective and simple tool to decrease the percolation threshold in epoxy/Ni@C composites. For hybrid composites series an optimal concentration of Ni@C (0.2 vol.%) was determined, leading to the conductivity absolute values several orders of magnitude higher than that of a composite filled with MWCNTs only. The synergy effects of using both fillers have been discussed. Below room temperature the electrical transport is mainly governed by epoxy resin compression in all composites, while the electron tunnelling was observed only in hybrid composites below 200 K. At higher temperatures (above 400 K), in addition to the nanoparticles redistribution effects, the electrical conductivity of epoxy resin makes a significant contribution to the total composite conductivity. The dielectric relaxation spectroscopy allows estimating the nanoparticles distributions in polymer matrix and could be used as the non-destructive and fast alternate to microscopy techniques for general polymer composite fabrication control.
RESUMO
The electrical properties of epoxy/MWCNT (multi-walled carbon nanotubes)/MnFe2O4 hybrid composites loaded with MWCNTs (below, 0.09 vol.%, and above, 0.58 vol.%, percolation threshold) and varying concentrations of MnFe2O4 up to 10 vol.% were studied in a wide frequency range (20 Hz-40 GHz) at different temperatures (20 K-500 K). At low frequencies, the dielectric permittivity and the electrical conductivity of composites with fixed amounts of MWCNT are strongly dependent on MnFe2O4 content. For MWCNT concentrations above the percolation threshold (i.e., 0.58 vol.%), the electrical conductivity highly decreases with the increase of the MnFe2O4 fraction. In contrast, for the epoxy/MWCNT just below the onset of electrical conductivity (0.09 vol.% of MWCNTs), there exists an optimal concentration of MnFe2O4 inclusions (i.e., 0.025 vol.%), leading to a dramatic increase of the electrical conductivity by three orders of magnitude. The electrical transport in composites is mainly governed by electron tunneling at lower temperatures (below 200 K), and it is highly impacted by the matrix conductivity at higher temperatures (above 400 K). The electrical properties were discussed in terms of the Maxwell-Wagner relaxation and distributions of relaxation times. A non-invasive platform based on dielectric relaxation spectroscopy was proposed for enhancing the synergetic effect coursed by using multiple nanoinclusions in polymer composites just below the percolation threshold.
RESUMO
The dielectric properties of epoxy/MWCNT (multi-walled carbon nanotubes)/MgO hybrid composites with a fixed MWCNT amount of 0.12 vol.% (0.2 wt.%) and varying MgO concentrations up to 3 vol.% were investigated in broad frequency (20-40 GHz) and temperature (20-500 K) ranges. The composites with up to 2 vol.% MgO nanoparticles concentration showed a significant increase of DC conductivity in relation to their non MgO-containing counterparts. The optimal content of MgO was found, i.e., 0.46 vol.%, which gave up to 2.5 orders of magnitude larger DC conductivity than those of the samples prepared without MgO additives. Using various amounts of MgO, it is possible to predictably vary the broadband electromagnetic properties of the composites, even entirely eliminating the electrical percolation. Electrical transport at different temperatures can be substantially controlled by the addition of given amounts of MgO. The broadband properties are discussed in terms of the distribution of relaxation times, which are proven to be an effective, noninvasive, and simple tool for checking composite fabrication issues, such as the distribution of MWCNT aggregates within the epoxy matrix.
RESUMO
Electromagnetic and thermal properties of a non-conventional polymer nanocomposite based on thermoplastic Polylactic acid (PLA, Ingeo™) filled, in different weight percentage, with multi-walled carbon nanotubes (MWCNTs), graphene nanoplatelets (GNPs), as well as a mixture of both fillers (MWCNTs/GNPs), are analyzed. The combination of notable electrical, thermal, and electromagnetic (EM) properties of the carbon fillers, in concentrations above the percolation threshold, together with the good processability of the PLA matrix gives rise to innovative filaments for 3D printing. In particular, the shielding efficiency (SE) in the frequency range 26-37 GHz of samples increases from 0.20 dB of unfilled PLA up to 13.4 dB for composites containing MWCNTs and GNPs, corresponding to 4% and 95% of SE, respectively. The thermal conductivity of the PLA loaded with 12 wt % of GNPs is 263% higher than that of the unfilled polymer, whereas an improvement of about 99% and 190% is detected for the PLA matrix loaded with MWCNTs and both fillers, respectively. The EM and thermal characterization is combined with a morphological investigation allowing us to correlate the dispersion states of the fillers within the polymer matrix with the observed EM and thermal properties. The EM and thermal characteristics exhibited by the nanocomposites make them suitable for packaging applications of electronic devices with electromagnetic interference (EMI) shielding and thermal dissipation features.
RESUMO
The limitation of poor mechanical stability and difficulties in printing electrically conductive components can be overcome owing to the recent introduction of nanotechnology into the field of additive manufacturing (AM) and the consequent development of nonconventional polymer nanocomposites suitable for 3D printing. In the present work, different weight percentages (up to 6 wt % in total) of carbon-based nanostructures-multiwalled carbon nanotubes (MWCNTs), graphene nanoplatelets (GNPs), and a combination of both fillers (MWCNTs/GNPs)-were incorporated into poly(lactic) acid (PLA, Ingeo™) in an attempt to overcome several limitations of conventional 3D manufacturing based on insulating materials. Solution blending and melt mixing were the two fabrication methods adopted for preparation of the samples under test. A comparison of the morphological, rheological, and electrical properties of the resulting nanocomposites was carried out. Moreover, for the same weight concentrations, the influence of physical and geometrical features (i.e., functionalization and aspect ratio) of the embedded fillers was also investigated. Rheological methods were applied to control the quality of fillers dispersion in PLA matrix. The rheological percolation threshold was considered as reference in order to evaluate the internal structure of nanodispersions. TEM visualization, combined with rheological characterizations, was used for efficient control of the nanofiller dispersion. DC characterization revealed that lower electrical percolation thresholds and higher values of electrical conductivity were achieved using fillers with a larger aspect ratio and melt mixing, respectively. Moreover, given the possibility of obtaining complex and appropriate shapes for electromagnetic compatibility (EC) applications, electromagnetic (EM) response of the nanocomposites at the highest filler concentration was investigated in GHz and THz regions. It was found that the electromagnetic shielding efficiency (EMI) of nanocomposites strongly depended on the aspect ratio of the nanofillers, whereas the type of processing technique did not have a significant effect. Therefore, a careful choice of methods and materials must be made to address the final application for which these materials and further 3D printed architectures are designed.