Achieving excitation wavelength-power-dependent colorful luminescence via multiplexing of dual lanthanides in fluorine oxide particles for multilevel anticounterfeiting.

The optical characteristics of multimode luminescent materials like multimode luminescence (photoluminescence, afterglow, thermoluminescence) and a multi-excitation source (light, thermal, mechanical force) play crucial roles in optical data storage and readout, document security and anticounterfeiting. A higher level of advanced anticounterfeiting may rely on multimode anticounterfeiting materials that can realize multicolor luminescence. Here, a highly integrated multimode and multicolor Y7O6F9:Er3+,Eu3+ material is developed through multiplexing of dual lanthanides in fluorine oxide particles. In photoluminescence and photoluminescence/up-conversion luminescence modes, the material Y7O6F9:Er3+,Eu3+ has the characteristic of excitation wavelength and power dependence. In the photoluminescence mode, under excitation at 254 nm and 365 nm, Y7O6F9:Er3+ and Y7O6F9:Eu3+ showed bright red and green emissions, respectively. In the photoluminescence/up-conversion mode, under the increased excitation power from 0.2 to 2.0 W cm-2, the color of luminescence emission can be finely tuned from red to orange, yellow and green. Taking this unique excitation wavelength-power-dependent luminescence property into account, a multilevel anticounterfeiting device with the Lily pattern was designed. The device readily integrates the advantages of the excitation wavelength-dependent photoluminescence emissions and excitation power-dependent photoluminescence emissions in one overall device. These findings offer unique insight for designing highly integrated multimode, multicolor luminescence materials and advanced anticounterfeiting technology toward a wide variety of applications, particularly multilevel anticounterfeiting devices.

Insights into blue-light activated red-emitting persistent luminescence from Pr3+-doped phosphors.

In recent years, a series of persistent luminescence materials excitable by blue light have been developed and widely used in many fields such as optical information storage, AC-LEDs, anti-counterfeiting and bio-imaging. However, it is still a long-standing challenge to develop a superior red-emitting persistent phosphor that can be efficiently excited by blue light. In this work, a novel blue-light excited red-emitting persistent phosphor CaCd2Ga2Ge3O12:Pr3+ was successfully synthesized by using a solid-state method, showing excellent luminescence properties. Moreover, the phase purity, crystal structure, photoluminescence spectra, afterglow emission spectra, and three-dimensional thermoluminescence spectrum were successfully investigated. Under 294 nm excitation, photoluminescence spectra show a single orange emission and a series of peaks centered at 492, 537, 568, 614 and 664 nm, which correspond to the 3P0 → 3H4, 3P0 → 3H5, 3P2 → 3H6, 1D2 → 3H4, and 3P0 → 3F2 transitions of Pr3+, respectively. Interestingly, after blue light excitation, the afterglow luminescence exhibits red long emission, which is attributed to the 1D2 → 3H4 transition of Pr3+. Through thermoluminescence spectra and three-dimensional thermoluminescence spectra, we analyze the reasons for the different colors of photoluminescence and afterglow luminescence. The results imply that there are two types of traps, and the depth of shallow traps and deep traps is calculated to be 0.684 and 0.776 eV, respectively. It is worth noting that the photoluminescence is attributed to the 4f2 → 4f5d and f → f transitions of Pr3+, and the afterglow luminescence is ascribed to a tunneling-related process and the transition of electrons from the valence band to the conduction band. The obtained red-emitting persistent phosphors provide a promising pathway toward AC-LEDs, multi-cycle bio-imaging and other fields.