Filler Mixed Into Adhesives Does Not Necessarily Improve Their Mechanical Properties.

OBJECTIVES: To investigate the influence of filler type/loading on the micro-tensile fracture strength (µTFS) of adhesive resins, as measured 'immediately' upon preparation and after 1-week water storage ('water-stored'). METHODS: The morphology and particle-size distribution of three filler particles, referred to as 'Glass-S' (Esschem Europe), 'BioUnion' (GC), and 'CPC_Mont', were correlatively characterized by SEM, TEM, and particle-size analysis. These filler particles were incorporated into an unfilled adhesive resin ('BZF-29unfilled', GC) in different concentrations to measure the 'immediate' µTFS. After 1-week water storage, the 'water-stored' µTFS of the experimental particle-filled adhesive resins with the most optimum filler loading, specific for each filler type, was measured. In addition, the immediate and water-stored µTFS of the adhesive resins of three experimental two-step universal adhesives based on the same resin matrix but varying for filler type/loading, coded as 'BZF-21' (containing silica and bioglass), 'BZF-29' (containing solely silica), and 'BZF-29_hv' (highly viscous with a higher silica loading than BZF-29), and of the adhesive resins of the gold-standard adhesives OptiBond FL ('Opti-FL', Kerr) and Clearfil SE Bond 2 ('C-SE2', Kuraray Noritake) was measured along with that of BZF-29unfilled (GC) serving as control/reference. Statistics involved one-way and two-way ANOVA followed by post-hoc multiple comparisons (α<0.05). RESULTS: Glass-S, BioUnion, and CPC_Mont represent irregular fillers with an average particle size of 8.5-9.9 µm. Adding filler to BZF-29unfilled decreased µTFS regardless of filler type/loading. One-week water storage reduced µTFS of all adhesive resins except BZF-21, with the largest reduction in µTFS recorded for BZF-29unfilled. Among the three filler types, the µTFS of the 30 wt% Glass-S and 20 wt% BioUnion filled adhesive resin was not significantly different from the µTFS of BZF-29unfilled upon water storage. CONCLUSIONS: Adding filler particles into adhesive resin did not enhance its micro-tensile fracture strength but appeared to render it less sensitive to water storage as compared to the unfilled adhesive resin investigated.

Influence of airborne particle abrasion on dentin bonding effectiveness of a 2-step universal adhesive.

OBJECTIVE: To determine the effect of airborne particle abrasion (APA) on micro-tensile bond strength (µTBS) to dentin using different air-abrasion/polishing powders. METHODS: The bonding effectiveness of G2 Bond Universal (G2B), used in etch-and-rinse (E&R) and self-etch mode (SE), was tested on bur-cut dentin and dentin air abraded/polished using six different powders (aluminum oxide 29 µm (AO29) and 53 µm (AO53), aluminum trihydroxide (AT), sodium bicarbonate (SB), sodium bicarbonate soft (SBsoft) and bioactive glass (BG); Velopex). Adhesive-composite resin specimens were immersed in distilled water at 37 °C for one week and cut into microspecimens. Half of the specimens were subjected to 50,000 thermocycles (aged). Immediate and aged µTBS to dentin were measured. Statistical analysis was performed using linear mixed-effects (LME) modeling (p < 0.05). RESULTS: Comparing the aged bond strengths to air-abraded/polished dentin with bur-cut dentin, pretreatment with SB and SBsoft in combination with G2B used in E&R mode, and BG air polishing in combination with both application modes (E&R, SE), resulted in a significantly higher bond strength. Dentin bond strength was only significantly lower when air abraded with AO29 and using G2B in SE mode. Aging did not significantly influence bond strength for both application modes (E&R, SE), except for AO29 and AT-treated dentin, where bond strengths decrea sed significantly using G2B in SE mode. In general, G2B reached significantly higher bond strengths on air-abraded/polished dentin in E&R mode than in SE mode. CONCLUSION: Air-abrasion/polishing did not impair dentin bond strength using G2B, except when dentin was air abraded with AO29 and using G2B in SE mode. Air polishing positively influenced the bond strength to dentin in specific groups. CLINICAL SIGNIFICANCE: APA is safe concerning bonding to dentin. The E&R application mode is preferred using G2B as adhesive on air-abraded/polished dentin. Air polishing with BG positively influenced dentin bond strength for both application methods.

Bonding performance of experimental HEMA-free two-step universal adhesives to low C-factor flat dentin.

OBJECTIVES: Experimental two-step universal adhesives (2-UAs) providing a particle-filled hydrophobic adhesive resin with a significant film thickness to hydrophobically seal the adhesive interface were designed and synthesized. This study aimed to characterize their interfacial interaction with dentin, to determine whether the 2-UA formulations achieve durable bonding to low C-factor flat dentin and to measure their water sorption. METHODS: Bonding effectiveness of 2-UAs that combine a 10-MDP-based primer with hydrophobic adhesive resins differing only for filler (BZF-21, BZF-29, and BZF-29_hv) were comparatively investigated with the commercial adhesive Clearfil SE Bond 2 (C-SE2, Kuraray Noritake). Adhesive-dentin interfaces were characterized with TEM. Adhesive-resin disks were immersed in distilled water at 37 °C for 1 week, 6 months and 1 year to measure water sorption and solubility. 'Immediate' and 'aged' micro-tensile bond strength (µTBS) of the adhesives applied in etch-and-rinse (E&R) and self-etch (SE) bonding mode to low C-factor flat dentin were measured. Statistical analyses involved linear mixed-effects (LME) modelling and Kruskal-Wallis testing (p < 0.05). RESULTS: TEM revealed that E&R hybrid layers were more sensitive to aging than SE hybrid layers. Lower water sorption was recorded for all UAs compared with C-SE2. The immediate µTBS of BZF-21 and BZF-29 was not significantly different from that of C-SE2. The 1-year aged µTBS of all 2-UAs was significantly lower than that of C-SE2, except for BZF-29 applied in E&R mode. A significant reduction in µTBS upon 1-year aging was recorded for BZF-21 and BZF-29 applied in E&R mode. A significant difference in µTBS between E&R and SE bonding modes was recorded for all adhesives except BZF-21. SIGNIFICANCE: Experimental 2-UAs with a hydrophobic adhesive-resin design produced± 20-µm thick adhesive-resin layers, absorbed less water and resulted in bonding performance that was more aging-resistant when applied in SE than in E&R bonding mode. The silica-filled BZF-29 2-UA revealed the most comparable bonding performance with C-SE2 in a low C-factor condition (flat dentin).