RESUMO
STATEMENT OF PROBLEM: The biomechanical stability of the implant-prosthesis assembly and its maintenance under function is a determining factor in the success of implant prosthesis rehabilitation, but studies of different angular tapers are lacking. PURPOSE: The purpose of this in vitro study was to evaluate the axial displacement and torque loss of prosthetic abutments with Morse-type connections of different angular tapers after thermomechanical cycling by using microcomputed tomography (µCT) and a digital torque wrench. MATERIAL AND METHODS: Eighteen Ø3.5×11.5-mm implants were embedded in polyvinyl chloride cylinders, and the 3 different types of abutments (n=6) with angular tapers of 11.5 degrees - Alvim Cone Morse (ACM-11.5), 16.0 degrees - Helix Gran Morse (HGM-16), and 24.0 degrees - Nobel Replace Conical Connection (NRC-24) were installed with the torque recommended by the manufacturers. To calculate the axial displacements of the abutments about the implants, zirconia maxillary canine crowns were fabricated using a computer-aided design and computer-aided manufacturing (CAD-CAM) system and cemented onto the abutments. Before and after thermomechanical cycling, the assemblies were scanned using microtomography (micro-CT) to assess axial displacement, and the torque losses were calculated after the abutments were finally unscrewed. A load of 100 N, frequency of 2 Hz, and 106 cycles with temperature variation of 5 °C to 55 °C were used for the thermomechanical cycling. Analysis of variance and the Tukey post hoc test (α=.05) were used for analysis. RESULTS: A significant difference was observed between the abutments for axial displacement, measured after thermomechanical cycling (P=.002). The ACM-11.5 abutment showed the highest mean value (134.1 ±58.7 µm), different from HGM-16 (63.3 ±26.1 µm) (P=.013) and NRC-24 (42.7 ±8.7 µm) (P=.002); the 2 latter groups were similar to each other (P=.618). For the torque losses, no significant difference was found among the abutments (P=.928), but there were significant differences for the thermomechanical cycling (before and after) (P<.001) in that the loss of torque was greater after thermocycling. CONCLUSIONS: The smaller the taper angle of the Morse-type prosthetic abutment, the greater its axial displacement, and the thermomechanical cycling significantly reduced pretorque, regardless of taper.
RESUMO
Background and Objectives: The insertion of the dental implant in the bone is an essential step in prosthetic rehabilitation. The insertion torque has the potential to distort the prosthetic platform, which can cause future biomechanical problems with the continuous action of occlusal forces. The aim of this study is to evaluate different insertion torques in the deformation of tri-channel platform connections through two- and three-dimensional measurements with micro-CT. Materials and Methods: A total of 164 implants were divided into groups (platform diameter and type): 3.5, 3.75, and 4.3 mm NP (narrow platform), and 4.3 mm RP (regular platform). Each implant-platform group was then divided into four subgroups (n = 10) with different torques: T45 (45 Ncm), T80 (80 Ncm), T120 (120 Ncm), and T150 (150 Ncm). The implant-abutment-screw assemblies were scanned and the images obtained were analyzed. Results: A significant difference was observed for the linear and volume measures between the different platforms (p < 0.01) and the different implant insertion torques (p < 0.01). Qualitative analysis suggested a higher deformation resistance for the 3.75 NP compared to the 3.5 NP, and RP was more resistant compared to the NP. Conclusions: The 0.25 mm increment in the implant platform did not increase the resistance to the applied insertion torques; the 4.3 mm implant was significantly stronger compared to the 3.5 mm implant; and the proposed micro-CT analysis was considered valid for both the 2D and 3D analyses of micro-gaps, qualitatively and quantitatively.
Assuntos
Próteses e Implantes , Humanos , Microtomografia por Raio-X , TorqueRESUMO
The aim of this study was to assess the internal and vertical marginal fit of metallic copings to abutments and the fracture strength of different narrow diameter dental implant/abutments, either submitted to thermomechanical cycling or not. Sixty-four implant/abutments (n=16) were divided into 4 groups according to diameter and abutment type: G3.5-UAC (morse taper implant Ø3.5mm + universal abutment with beveled chamfer finish); G2.9-UAS (morse taper implant Ø2.9mm + universal abutment with shoulder finish); G2.8-AA (morse taper friction implant Ø2.8mm + anatomical abutment) and G2.5-HP (one-piece implant Ø2.5mm with indexed hexagonal platform). Each group was divided into two subgroups (n=8): submitted and not submitted to thermomechanical cycling (TMC). To assess internal and vertical marginal fit of metallic copings, the assemblies were scanned using microtomography (micro-CT) (n=5). The samples were subjected to the compressive strength test on a universal test machine. Group G3.5-UAC showed the highest marginal misfit regardless of TMC (p<0.05). All other groups were similar after TMC. Group G2.8-AA showed the lowest internal misfit both with and without TMC (p<0.05). Group G2.8-AA showed the highest fracture strength, similar only to G2.5-HP without TMC and G3.5-UAC with TMC. The type of abutment affects the internal and marginal fit of metallic copings and the anatomical abutment led to the best internal and marginal coping fit. The narrow diameter dental implant/abutments differ in terms of fracture strength, the strongest assembly was that composed by implant of type V grade titanium without internal threads (friction implant).
Assuntos
Implantes Dentários , Dente Suporte , Projeto do Implante Dentário-Pivô , Análise do Estresse Dentário , Resistência à Flexão , Teste de Materiais , Titânio , ZircônioRESUMO
Abstract The aim of this study was to assess the internal and vertical marginal fit of metallic copings to abutments and the fracture strength of different narrow diameter dental implant/abutments, either submitted to thermomechanical cycling or not. Sixty-four implant/abutments (n=16) were divided into 4 groups according to diameter and abutment type: G3.5-UAC (morse taper implant Ø3.5mm + universal abutment with beveled chamfer finish); G2.9-UAS (morse taper implant Ø2.9mm + universal abutment with shoulder finish); G2.8-AA (morse taper friction implant Ø2.8mm + anatomical abutment) and G2.5-HP (one-piece implant Ø2.5mm with indexed hexagonal platform). Each group was divided into two subgroups (n=8): submitted and not submitted to thermomechanical cycling (TMC). To assess internal and vertical marginal fit of metallic copings, the assemblies were scanned using microtomography (micro-CT) (n=5). The samples were subjected to the compressive strength test on a universal test machine. Group G3.5-UAC showed the highest marginal misfit regardless of TMC (p<0.05). All other groups were similar after TMC. Group G2.8-AA showed the lowest internal misfit both with and without TMC (p<0.05). Group G2.8-AA showed the highest fracture strength, similar only to G2.5-HP without TMC and G3.5-UAC with TMC. The type of abutment affects the internal and marginal fit of metallic copings and the anatomical abutment led to the best internal and marginal coping fit. The narrow diameter dental implant/abutments differ in terms of fracture strength, the strongest assembly was that composed by implant of type V grade titanium without internal threads (friction implant).
Resumo O objetivo deste estudo foi avaliar a adaptação marginal e interna de cópings metálicos em pilares sobre implantes, e a resistência a fratura de diferentes conjuntos de implantes/pilares de diâmetro reduzido, submetidos à ciclagem termomecânica ou não. Sessenta e quatro implantes/pilares (n=16) foram divididos em 04 grupos de acordo com o tipo de pilar e diâmetro do implante: G3.5-UAC (implante cone morse Ø3.5mm + munhão universal com término em chanfro); G2.9-UAS (implante cone morse Ø2.9mm + munhão universal com término em ombro); G2.8-AA (implante cone morse friccional Ø2.8mm + munhão anatômico); e G2.5-HP (implante de corpo único de Ø2.5mm com plataforma hexagonal indexada). Cada grupo foi dividio em dois subgrupos (n=8): submetidos ou não à ciclagem termomecânica (TMC). As amostras foram escaneadas por microtomografia (micro-CT) para avaliar a adaptação interna e marginal vertical dos copings metálicos. As amostras foram submetidas à resistência à compressão em uma maquina de ensaios universal. O grupo G3.5-UAC apresentou os maiores valores de desadaptação marginal independentemente da TMC (p<0,05). Todos os outros grupos foram similares entre si após TMC. O grupo G2.8-AA demonstrou o menor desajuste interno independentemente de TMC (p<0,05). O grupo G2.8-AA demonstrou a maior resistência à fratura, similar apenas ao grupo G2.5-HP sem TMC e G3.5-UAC com TMC. O tipo de pilar influencia a adaptação interna e marginal vertical de copings metálicos. O grupo do pilar anatômico (sem entalhes na superfície) levou à melhor adaptação, enquanto o grupo com plataforma expandida hexagonal e os grupos com munhão universal (com entalhes na superfície) proporcionaram os maiores desajustes (especialmente com termino em chanfro). Os implantes/pilares de diâmetro reduzido diferem em termos de resistencia à fratura, sendo que o conjunto mais resistente foi aquele composto por titânio tipo V e sem roscas internas (implante friccional).
Assuntos
Implantes Dentários , Titânio , Zircônio , Teste de Materiais , Dente Suporte , Análise do Estresse Dentário , Projeto do Implante Dentário-Pivô , Resistência à FlexãoRESUMO
The aim of this study was to assess the influence of different methods for generating geometric models on stress values and distributions of endodontically treated teeth using a three-dimensional finite element analysis (3D-FEA). An endodontically treated human maxillary canine restored with glass fiber post and ceramic-fused-to-metal crown was scanned by microcomputed tomography and three-dimensionally reconstructed. Based on the microcomputed tomography images, 2 geometric models were generated and divided into the following groups: Group GCAD - only the root dentine was reconstructed based on a microcomputed tomography image while the remaining structures were generated by GCAD software simulation, and Group GTC - the whole assembly was obtained from scanning and rehabilitated by microcomputed tomography. Loading of 180N at 45° of the tooth long axis was applied on the lingual surface of the incisal third and the models were supported by a periodontal ligament fixed into the 3 axes of the Cartesian system (x=y=z=0). von Mises stress (VMS) were calculated. Differences in stress value and distribution between the generation methods of the geometric models were found. The lowest ratio difference in GTC/GCAD was for resin cement and core. Thus, the method for generation of the geometric model in finite element analysis was found to influence the research results, suggesting better results for GCAD method(AU)
O objetivo deste estudo foi avaliar a influência de diferentes métodos para a geração de modelos geométricos em valores de tensões e distrubuições de dentes tratados endodônticamente, utilizando-se uma análise tridimensional de elementos finitos (3D-FEA). Canino superior humano tratado endodonticamente, restaurado com pino de fibra de vidro e coroa metalocerâmica foi escaneado por meio de microtomografia computadorizada e reconstruído tridimensionalmente. Baseadas nas imagens de microtomografia computadorizada, foram gerados 2 modelos geométricos e divididos nos seguintes grupos: grupo GCAD-apenas a dentina radicular foi reconstruída baseada na imagem obtida por meio de microtomografia computadorizada, enquanto as estruturas remanescentes foram geradas por simulação de software de CAD, e grupo GTC-todo conjunto inteiro foi obtido do escaneamento e reabilitado pela microtomografia computadorizada. O carregamento de 180N em 45° do longo eixo do dente foi aplicado na superfície lingual do terço incisal e os modelos foram suportados por um ligamento periodontal fixado nos 3 eixos do sistema cartesiano (x = y = z = 0). Tensões equivalents de von Mises (VMS) foram calculados. Foram encontradas diferenças no valor de tensões e distribuição entre os métodos de geração dos modelos geométricos. A menor razão entre GTC/GCAD foi para o cimento de resinoso e núcleo. Assim, verificou-se que o método de geração do modelo geométrico na análise de elementos finitos influenciou os resultados da pesquisa, sugerindo melhores resultados para o método GCAD(AU)
Assuntos
Desenho Assistido por Computador , Dente não Vital , Análise de Elementos FinitosRESUMO
Aim: This study evaluated the mechanical behavior of implant-supported crowns obtained by different fabrication technique after thermomechanical cycling. Methods: Thirty-two external hexagon dental implants were divided into four groups (n=10): CC conventional casting with torch; EI electromagnetic induction casting; PL plasma casting; and CAD-CAM milling through computer-aided design and computer-aided manufacturing. Vickers microhardness of the specimens were made before and after the thermomechanical cycling, and then subjected to fracture load. Fracture pattern was evaluated. Results: No significant difference was observed comparing the microhardness before and after thermomechanical cycling. CAD-CAM group presented significant lower microhardness than the other groups. No significant statistical difference was showed on fracture load between the groups. The CAD-CAM and PL presented lower number of failure by plastic deformation. Conclusion: The manufacturing techniques affected the mechanical behavior and the failure pattern of implant-supported crowns tested
Assuntos
Prostodontia , Implantes Dentários , Desenho Assistido por ComputadorRESUMO
INTRODUCTION: Endodontically treated teeth have an increased risk of biomechanical failure because of significant loss of tooth structure. The biomechanical behavior of endodontically treated teeth restored was evaluated using different extensions of endocrowns inside the pulp chamber by in vitro and 3-dimensional finite element analysis (FEA). METHODS: Thirty mandibular human molars were endodontically treated. Standardized endocrown preparations were performed, and the teeth were randomly divided into 3 groups (n = 10) according to different endocrown extensions inside the pulp chamber: G-5 mm, a 5-mm extension; G-3 mm, a 3-mm extension; and G-1 mm, a 1-mm extension. After adhesive cementation, all specimens were subjected to thermocycling and dynamic loading. The survival specimens were subjected to fracture resistance testing at a crosshead speed of 1 mm/min in a universal testing machine. All fractured specimens were subjected to fractography. Data were analyzed by 1-way analysis of variance and the Tukey post hoc test (P < .05). Stress distribution patterns in each group were analyzed using FEA. Qualitative analyses were performed according to the von Mises criterion. RESULTS: After dynamic loading, a survival rate of 100% was observed in all groups. For static loading, statistically significant differences among the groups were observed (P < .05) (G-5 mm = 2008.61 N, G-3 mm = 1795.41 N, and G-1 mm = 1268.12 N). Fractography showed a higher frequency of compression curls for G-5 mm and G-3 mm than for G-1 mm. FEA explained the results of fracture strength testing and fractography. CONCLUSIONS: Greater extension of endocrowns inside the pulp chamber provided better mechanical performance.
Assuntos
Coroas , Cimentação/métodos , Coroas/efeitos adversos , Planejamento de Prótese Dentária , Falha de Restauração Dentária , Restauração Dentária Permanente/efeitos adversos , Restauração Dentária Permanente/métodos , Análise do Estresse Dentário , Análise de Elementos Finitos , Humanos , Técnicas In Vitro , Dente Molar/cirurgia , Dente não Vital/diagnóstico por imagem , Microtomografia por Raio-XRESUMO
OBJECTIVE: This study aimed to evaluate the fracture load and pattern of customized and non-customized zirconia abutments with Morse-taper connection. METHODS: 18 implants were divided into 3 groups according to the abutments used: Zr - with non-customized zirconia abutments; Zrc - with customized zirconia abutments; and Ti - with titanium abutments. To test their load capacity, a universal test machine with a 500-kgf load cell and a 0.5-mm/min speed were used. After, one implant-abutment assembly from each group was analyzed by Scanning Electron Microscopy (SEM). For fractographic analysis, the specimens were transversely sectioned above the threads of the abutment screw in order to examine their fracture surfaces using SEM. RESULTS: A significant difference was noted between the groups (Zr=573.7±11.66N, Zrc=768.0±8.72N and Ti=659.1±7.70N). Also, the zirconia abutments fractured while the titanium abutments deformed plastically. Zrc presented fracture loads significantly higher than Zr (p=0.009). All the zirconia abutments fractured below the implant platform, starting from the area of contact between the abutment and implant and propagating to the internal surface of the abutment. All the zirconia abutments presented complete cleavage in the mechanical test. Fractography detected differences in the position and pattern of fracture between the two groups with zirconia abutments, probably because of the different diameters in the transmucosal region. SIGNIFICANCE: Customization of zirconia abutments did not affect their fracture loads, which were comparable to that of titanium and much higher than the maximum physiological limit for the anterior region of the maxilla.
Assuntos
Projeto do Implante Dentário-Pivô , Falha de Restauração Dentária , Zircônio/química , Materiais Dentários/química , Análise do Estresse Dentário , Teste de Materiais , Microscopia Eletrônica de Varredura , Estresse Mecânico , Titânio/químicaRESUMO
The use of zirconia abutments has increased because of aesthetics, but sometimes customization is necessary and its effect is unclear. This study evaluated the marginal fit and torque loss of customized and non-customized aesthetic zirconia abutments associated with Morse taper implants before and after thermomechanical cycling. Twenty-four implant/abutment/crown sets were divided into three groups (N = 8): Zr - non-customized zirconia abutments, Zrc - customized zirconia abutments, and Ti - titanium abutments. The ceramic crowns of the upper canines were made. All of the abutments were tightened with 15-N.cm torque, and the crowns were cemented on the abutments. The misfits and torque loss were measured before and after thermomechanical cycling. The marginal fit was evaluated in two planes throughout 10 different slices, 30 measurements for each face (i.e., buccal, palatal, mesial and distal) and 120 measurements for each sample. A load of 100N, a frequency of 2Hz and 1000,000 cycles with temperature variation of 5°-55°C were used for thermomechanical cycling. Thermomechanical cycling significantly decreased the marginal misfit only with the Zrc (p = 0.002), and the Ti was significantly different from the Zr and Zrc before and after thermomechanical cycling. Thermomechanical cycling did not affect the torque losses of the groups, but a significant difference between the Zr and Zrc (p = 0.0345) before cycling was noted. Customization of zirconia abutments does not significantly affect torque loss and marginal misfit after thermomechanical cycling suggesting that they can be safe for clinical utilization.
Assuntos
Teste de Materiais , Temperatura , Torque , ZircônioRESUMO
Aim: The aim of this study was to evaluate fracture toughness by indentation method of three dental ceramics processed by heat pressing. The ceramics evaluated were fluorapatite glass ceramic (ZIR), glass ceramic containing leucite (POM) and leucite-reinforced glass ceramic (EMP). Materials and methods: Ninety disks (13mm of diameter x 4mm of thickness) and nine rectangular specimens (25x4x2mm) were made to evaluate, respectively, microhardness/fracture toughness (n=30) and elastic modulus (n=3). Samples were obtained by pressing ceramic into refractory molds. After polishing, Vickers microhardness was evaluated under 4,904N load for 20s. Elastic modulus was measured by impulse excitation technique. Data from microhardness and elastic modulus were used to calculate fracture toughness, after measuring crack length under 19,6N load applied for 20s. Results were evaluated by ANOVA and Tukey´s test. Results: Microhardness (VHN) of POM (637.9±53.6) was statistically greater (p<0.05) than ZIR (593.0±14.3), followed by EMP (519.1±21.5); no significant difference (p=0.206) was noted for elastic modulus (GPa) (ZIR: 71.5±9.0; POM: 67.3±4.4; EMP: 61.7±2.3). Fracture toughness (MPa/m) of POM (0.873±0.066) was statistically lower (p<0.05) than ZIR (0.977±0.021) and EMP (0.965±0.035). Conclusion: The results suggest that fluorapatite glass ceramic (ZIR) and leucite-reinforced glass ceramic (EMP) processed by heat pressing presented greater fracture toughness, improving clinical prognosis of metal free restorations
Assuntos
Porcelana Dentária , Módulo de Elasticidade , Testes de DurezaRESUMO
OBJECTIVE: The aim of this study was to analyze failure modes and misfit of abutments with reduced diameter for both cement and screw retentions after cyclic loading. MATERIAL AND METHODS: Forty morse-taper abutment/implant sets of titanium were divided into four groups (N = 10): G4.8S-4.8 abutment with screw-retained crown; G4.8C-4.8 abutment with cemented crown; G3.8S-3.8 abutment with screw-retained crown; and G3.8C-3.8 abutment with cemented crown. Copings were waxed on castable cylinders and cast by oxygen gas flame and injected by centrifugation. After, esthetic veneering ceramic was pressed on these copings for obtaining metalloceramic crowns of upper canine. Cemented crowns were cemented on abutments with provisional cement (Temp Bond NE), and screw-retained crowns were tightened to their abutments with torque recommended by manufacturer (10 N cm). The misfit was measured using a stereomicroscope in a 10× magnification before and after cyclic loading (300,000 cycles). Tests were visually monitored, and failures (decementation, screw loosening and fractures) were registered. Misfit was analyzed by mixed linear model while failure modes by chi-square test (α = 0.05). RESULTS: Cyclic loading affected misfit of 3.8C (P ≤ 0.0001), 3.8S (P = 0.0055) and 4.8C (P = 0.0318), but not of 4.8S (P = 0.1243). No differences were noted between 3.8S with 4.8S before (P = 0.1550) and after (P = 0.9861) cyclic loading, but 3.8C was different from 4.8C only after (P = 0.0015) loading. Comparing different types of retentions at the same diameter abutment, significant difference was noted before and after cyclic loading for 3.8 and 4.8 abutments. Analyzing failure modes, retrievable failures were present at 3.8S and 3.8C groups, while irretrievable were only present at 3.8S. CONCLUSIONS: The cyclic loading decreased misfit of cemented and screw-retained crowns on reduced diameter abutments, and misfit of cemented crowns is greater than screw-retained ones. Abutments of reduced diameter failed more than conventional.
Assuntos
Parafusos Ósseos , Coroas , Dente Suporte , Cimentos Dentários , Projeto do Implante Dentário-Pivô , Falha de Restauração Dentária , Análise do Estresse Dentário , HumanosRESUMO
Dental ceramics have been widely used because of aesthetic, but wear is still questioned. There are relates that ceramic surface is prone to degradation by acidulated fluoride, that can increase wear rates. The aim of this study was to evaluate the effect of neutral and acidulated fluoride gel, used as preventive agents for professional use, at wear and compression strength of dental ceramics IPS e.max ZirPress (ZIR), IPS Empress Esthetic (EMP) e IPS Inline POM (POM). For this, 30 crowns and 30 disks were obtained by heat-pressing. Crowns and disks were submitted to two-body wear test at machine of mechanical loading, simulating occlusion, lateral movement and disocclusion. It was performed 300,000 cycles at 1Hz frequency under 20N load, to simulate 1 year of mastication. Samples were totally immersed during the test and were divided into three groups according to the gel used for immersion (n=10): control, neutral (sodium fluoride 2%) and acidulated (acidulated phosphate fluoride 1.23%). Samples (crowns and disks) were analyzed for vertical height loss after the test using, respectively, profile projector and stereomicroscope. Roughness of worn surface of crowns and disks was evaluated by laser confocal microscopy. Data of height loss and roughness were evaluated by two-way ANOVA and Bonferroni's test. A crown/disk of each group was analyzed by scanning electronic microscopy. After wear resistance tests, crowns were cemented to their abutments and submitted to compressive load at 30° angulation and 1mm/min speed. Type of failures was compared by qui-square test. Ceramic EMP worn less while ZIR worn more. Control gel worn more at crowns while acidulated gel worn more at disks. Surface roughness of samples tested at acidulated gel was significantly lower. Type of failures found at compression resistance tests was affected by ceramic type, but not by gel used. The results suggest that ceramic and fluoride gel affect wear and roughness of worn surface while type of failure is only affected by ceramic.
Assuntos
Coroas , Porcelana Dentária/análise , Fluoretos/química , Teste de Materiais , Cerâmica , Propriedades de SuperfícieRESUMO
Objetivo: O objetivo deste estudo foi avaliar a resistência ao desgaste de duas resinas compostas contra ligas alternativas. Materiais e Métodos: Quinze amostras de corpo cônico foram obtidas das resinas Z250 e charisma (CHA). As amostras foram divididas em três grupos de acordo com o disco da liga a ser utilizada como antagonista: NíquelCromo (Ni-Cr), Cobalto-Cromo (Co-Cr) e titânio comercialmente puro (Ti cp). Os testes de desgaste foram realizados na velocidade de 265 ciclos/minuto e distância de 10mm, totalizando 40.000 ciclos. Antes e após os testes de desgaste, as amostras foram pesadas e tiveram seu perfil desenhado em projetor de perfil para avaliar a perda de peso e de altura, respectivamente. Resultados: Para a perda de peso e de altura, o desgaste de Z250 foi menor do que CHA para o antagonista de Co-Cr, mas maior para o Ti cp. CHA apresenta superfície mais regular, sem fendas, e aspecto semelhante para todos os antagonistas. Z250 apresentou algumas fendas, principalmente contra Ti cp e Ni-Cr. Conclusão: Baseado nos resultados deste estudo, concluiu-se que CHA é mais apropriada contra Ti cp, e Z250 para associação com liga de Co-Cr enquanto qualquer resina composta pode ser utilizada contra Ni-Cr. (AU)
Objective: The aim of the present study was to evaluate wear resistance of two composites resins against alternative alloys. Material and Methods: Fifteen stylus tips samples of composite resin were obtained for each resin Z250 and charisma (CHA). Samples were divided into three groups according to the disk of alloy to be used as antagonist: NickelChromium (Ni-Cr), Cobalt- Chromium (Co-Cr) and commercially pure titanium (cp Ti). Wear tests were performed at a speed of 265 cycles/min and distance of 10mm, in a total of 40,000 cycles. Before and after wear tests, samples were weighed and had their profile designed in an optical comparator to evaluate weight and height loss, respectively. Results: For weight and height loss, wear of Z250 was lower than CHA for Co-Cr antagonist, but greater for cp Ti. CHA presents a more regular surface without cracks and similar aspect for all antagonists. Z250 showed some cracks, mainly against cp Ti and Ni-Cr. Conclusion: Within the results of the present study, it was concluded that CHA is suitable against cp Ti, and Z250 for association with Co-Cr alloy while any composite resin can be used against Ni-Cr.(AU)
Assuntos
Resinas Compostas , Ligas Dentárias , Desgaste de Restauração DentáriaRESUMO
This study aimed to verify marginal fit and the effect of cement film thickness standardization on retention of provisional crowns made with prefabricated acrylic cylinders on abutments, using two temporary luting agents subjected or not to mechanical cycling. Provisional crowns were made from bis-acryl (Luxatemp Fluorescence) or methyl methacrylate (Duralay) resins on acrylic cylinders and marginal fit and cement film thickness were evaluated. For retention evaluation, crowns were cemented with two temporary luting agents: non-eugenol zinc oxide (Tempbond NE) or calcium hydroxide-based (Hydcal) cements and subjected to tensile strength in a universal testing machine. After cleaning, debonded crowns were cemented again, subjected to mechanical cycling and retention was reassessed. The results of marginal fit and cement film thickness were analyzed by Student's t-test while retention of cements before and after mechanical cycling was analyzed using a mixed linear model. Methyl methacrylate crowns presented greater marginal misfit (p=0.001) and occlusal cement film thickness (p=0.003) than the bis-acryl ones. No difference was observed at axial cement film thickness (p=0.606). Resins (p=0.281) did not affect crown retention, but luting agents (p=0.029) and mechanical cycling (p=0.027) showed significant effects. The only significant interaction was mechanical cycling*luting agents, which means that luting agents were differently affected by mechanical cycling (p=0.002). In conclusion, the results showed that bis-acryl resin associated to calcium-hydroxide luting agent provided the best retention and lower cement thickness.
Assuntos
Coroas , Implantes Dentários para Um Único Dente , Prótese Dentária Fixada por Implante , Humanos , Técnicas In VitroRESUMO
Abstract: This study aimed to verify marginal fit and the effect of cement film thickness standardization on retention of provisional crowns made with prefabricated acrylic cylinders on abutments, using two temporary luting agents subjected or not to mechanical cycling. Provisional crowns were made from bis-acryl (Luxatemp Fluorescence) or methyl methacrylate (Duralay) resins on acrylic cylinders and marginal fit and cement film thickness were evaluated. For retention evaluation, crowns were cemented with two temporary luting agents: non-eugenol zinc oxide (Tempbond NE) or calcium hydroxide-based (Hydcal) cements and subjected to tensile strength in a universal testing machine. After cleaning, debonded crowns were cemented again, subjected to mechanical cycling and retention was reassessed. The results of marginal fit and cement film thickness were analyzed by Student's t-test while retention of cements before and after mechanical cycling was analyzed using a mixed linear model. Methyl methacrylate crowns presented greater marginal misfit (p=0.001) and occlusal cement film thickness (p=0.003) than the bis-acryl ones. No difference was observed at axial cement film thickness (p=0.606). Resins (p=0.281) did not affect crown retention, but luting agents (p=0.029) and mechanical cycling (p=0.027) showed significant effects. The only significant interaction was mechanical cycling*luting agents, which means that luting agents were differently affected by mechanical cycling (p=0.002). In conclusion, the results showed that bis-acryl resin associated to calcium-hydroxide luting agent provided the best retention and lower cement thickness.
Resumo: O objetivo deste estudo foi avaliar a adaptação marginal e o efeito da espessura da camada de cimento na retenção de coroas provisórias fixadas sobre os pilares com o auxílio de cilindros acrílicos pré-fabricados, utilizando dois cimentos provisórios submetidos ou não à ciclagem mecânica. Coroas provisórias foram confeccionadas com resina bis-acrilíca (Luxatemp Flourescence) ou resina à base de metil metacrilato (Duralay) sobre os cilindros, para posterior avaliação da influência das diferentes resinas na adaptação marginal e na espessura da linha do cimento. Para a avaliação da resistência à tração, as coroas foram cimentadas com dois cimentos provisórios: à base de óxido de zinco sem eugenol (Temp Bond NE) ou hidróxido de cálcio (Hydcal) e submetidas ao teste de tração em máquina universal de ensaio. Após o ensaio, as coroas foram limpas e novamente cimentadas para serem submetidas à ciclagem mecânica e posterior avaliação da resistência à tração. Os resultados obtidos para adaptação marginal e espessura do cimento foram analisados pelo teste t de Student, enquanto os resultados de resistência à cimentação antes e após a ciclagem mecânica foram analisados pelo modelo linear de efeitos mistos. As coroas confeccionadas com a resina de metil metacrilato apresentaram maiores valores para desadaptação marginal (p=0,001) e espessura do cimento (p=0,003) na parede oclusal quando comparadas com as coroas de resina bis-acrílica. Não houve diferença na espessura do cimento (p=0,606) na parede axial das coroas provisórias. As diferentes resinas não afetaram a resistência à cimentação das coroas (p=0,281), mas os diferentes cimentos (p=0,029) e a ciclagem mecânica (p=0,027) mostraram efeitos significantes. A única interação significante foi ciclagem mecânica ?#61482; agente cimentante, o que significa que os cimentos foram diferentemente afetados pela ciclagem mecânica (p=0,002). Em conclusão, a associação resina bis-acrílíca e cimento de hidróxido de cálcio proporcionou melhor resistência à tração e menor espessura de cimento.
Assuntos
Humanos , Coroas , Implantes Dentários para Um Único Dente , Prótese Dentária Fixada por Implante , Técnicas In VitroRESUMO
PURPOSE: The aim of the present study was to evaluate if a smaller morse taper abutment has a negative effect on the fracture resistance of implant-abutment connections under oblique compressive loads compared to a conventional abutment. MATERIALS AND METHODS: Twenty morse taper conventional abutments (4.8 mm diameter) and smaller abutments (3.8 mm diameter) were tightened (20 Ncm) to their respective implants (3.5 × 11 mm) and after a 10 minute interval, implant/abutment assemblies were subjected to static compressive test, performed in a universal test machine with 1 mm/min displacement, at 45° inclination. The maximum deformation force was determined. Data were statistically analyzed by student t test. RESULTS: Maximum deformation force of 4.8 mm and 3.8 mm abutments was approximately 95.33 kgf and 95.25 kgf, respectively, but no fractures were noted after mechanical test. Statistical analysis demonstrated that the evaluated abutments were statistically similar (P=.230). CONCLUSION: Abutment measuring 3.8 mm in diameter (reduced) presented mechanical properties similar to 4.8 mm (conventional) abutments, enabling its clinical use as indicated.