Biodegradable PMMA coated Zn-Mg alloy with bimodal grain structure for orthopedic applications - A promising alternative.

The study examines the impact of microstructure and polymethyl methacrylate (PMMA) grafting on the degradability of Zn-Mg alloys. The mechanical properties of a Zn alloy containing 0.68 wt% Mg and extruded at 200 °C are enhanced for degradable load-bearing applications, addressing a crucial need in the field. The material exhibits a bimodal grain size distribution that is random texture, consisting of secondary phases, grains, and sub-grains. With an elongation to failure of 16 %, the yield and ultimate tensile strengths are 325.9 and 414.5 MPa, respectively, and the compressive yield strength is 450.5 MPa. The "grafting-from" method was used to coat a few micrometers thick of PMMA on both bulk and scaffold Zn alloys to mitigate the corrosion rate. The last one is a porous structure, with a porosity of 65.8 %, considered as in the first approach of an orthopedic implant. After being immersed for 720 h, the PMMA-grafted bulk alloy's corrosion rate decreased from 0.43 to 0.25 mm/y. Similarly, the scaffold alloy's corrosion rate reduced from 1.24 to 0.49 mm/y. These results indicate that the method employed could be used for future orthopedic applications.

Use of a Photocleavable Initiator to Characterize Polymer Chains Grafted onto a Metal Plate with the Grafting-from Method.

The thorough characterization of polymer chains grafted through a "grafting-from" process onto substrates based on the determination of number (Mn) and weight (Mw) average molar masses, as well as dispersity (Ɖ), is quite challenging. It requires the cleavage of grafted chains selectively at the polymer-substrate bond without polymer degradation to allow their analysis in solution with steric exclusion chromatography, in particular. The study herein describes a technique for the selective cleavage of PMMA grafted onto titanium substrate (Ti-PMMA) using an anchoring molecule that combines an atom transfer radical polymerization (ATRP) initiator and a UV-cleavable moiety. This technique allows the demonstration of the efficiency of the ATRP of PMMA on titanium substrates and verification that the chains were grown homogeneously.

Effect of Mg Addition and PMMA Coating on the Biodegradation Behaviour of Extruded Zn Material.

Although zinc (Zn) is one of the elements with the greatest potential for biodegradable uses, pure Zn does not have the ideal mechanical or degrading properties for orthopaedic applications. The current research aims at studying the microstructure and corrosion behaviour of pure Zn (used as a reference material) and Zn alloyed with 1.89 wt.% magnesium (Mg), both in their extruded states as well as after being coated with polymethyl methacrylate (PMMA). The grafting-from approach was used to create a PMMA covering. The "grafting-from" method entails three steps: the alkali activation of the alloys, their functionalization with an initiator of polymerization through a phosphonate-attaching group, and the surface-initiated atom transfer radical polymerisation (SI-ATRP) to grow PMMA chains. Electrochemical and immersion corrosion tests were carried out in a simulated body fluid (SBF), and both confirmed the enhanced corrosion behaviour obtained after coating. The electrochemical test revealed a decrease in the degradation rate of the alloy from 0.37 ± 0.14 mm/y to 0.22 ± 0.01 mm/y. The immersion test showed the ability of complete protection for 240 h. After 720 h of immersion, the coated alloy displays minute crevice corrosion with very trivial pitting compared to the severe localized (galvanic and pitting) corrosion type that was detected in the bare alloy.

Monitoring photosynthetic microorganism activity with an electrolyte-gated organic field effect transistor.

Among organic thin film transistors (OTFTs), Organic Electrochemical Transistors (OECTs) have been extensively used for cell monitoring while Electrolyte-Gated Organic Field-Effect Transistors (EGOFETs) have never been described for that kind of application. However, EGOFETs are well adapted for this use because, as well as OECTs, they can operate directly in aqueous solutions such as cells culture media, but they offer much a higher on/off ratio which could lead to better sensitivity. As a proof of concept, we propose herein to monitor the photosynthetic activity of a cyanobacterium (Anabaena flos-aquae) contained within an EGOFET's electrolyte.