A peptide-based biological coating for enhanced corrosion resistance of titanium alloy biomaterials in chloride-containing fluids.

Titanium alloys are common materials in the manufacturing of dental and orthopedic implants. Although these materials exhibit excellent biocompatibility, corrosion in response to biological fluids can impact prosthesis performance and longevity. In this work, a PEGylated metal binding peptide (D-K122-4-PEG), derived from bacteria Pseudomonas aeruginosa, was applied on a titanium (Ti) alloy, and the corrosion resistance of the coated alloy specimen was investigated in simulated chloride-containing physiological fluids by electrochemical impedance spectroscopy and micro-electrochemical measurements, surface characterization, and biocompatibility testing. Compared to uncoated specimen, the D-K122-4-PEG-coated Ti alloy demonstrates decreased corrosion current density without affecting the natural passivity. Morphological analysis using atomic force microscopy and scanning electron microscopy confirms a reduction in surface roughness of the coated specimens in the fluids. The D-K122-4-PEG does not affect the binding of HEK-293T cells to the surface of unpolished Ti alloy, nor does it increase the leukocyte activation properties of the metal. D-K122-4-PEG represents a promising coating to enhance the corrosion resistance of Ti alloys in physiological fluids, while maintaining an excellent biocompatibility.

Peptide-based biocoatings for corrosion protection of stainless steel biomaterial in a chloride solution.

In this work, PEGylated D-amino acid K122-4 peptide (D-K122-4-PEG), derived from the type IV pilin of Pseudomonas aeruginosa, coated on 304 stainless steel was investigated for its corrosion resistant properties in a sodium chloride solution by various electrochemical measurements, surface characterization and molecular dynamics simulation. As a comparison, stainless steel electrodes coated with non-PEGylated D-amino acid retroinverso peptide (RI-K122-4) and D-amino acid K122-4 peptide (D-K122-4) were used as control variables during electrochemical tests. It was found that the D-K122-4-PEG coating is able to protect the stainless steel from corrosion in the solution. The RI-K122-4 coating shows corrosion resistant property and should be investigated further, while the D-K122-4 peptide coating, in contrast, shows little to no effect on corrosion. The morphological characterizations support the corrosion resistance of D-K122-4-PEG on stainless steel. The adsorption of D-K122-4 molecules occurs preferentially on Fe2O3, rather than Cr2O3, present on the stainless steel surface.