New glass compositions containing high concentrations of Tb3+ ions were developed aiming at the production of magneto-optical (MO) fibers. This work reports on the structural and MO properties of a new glass composition based on (100 - x)(41GeO2-25B2O3-4Al2O3-10Na2O-20BaO) - xTb4O7. Morphological analysis (HR-TEM) of the sample with the highest concentration of Tb3+ ions confirmed the homogeneous distribution of Tb3+ ions and the absence of nanoclusters. All the samples presented excellent thermal stability against crystallization (ΔT > 100 °C). An optical fiber was manufactured by a fiber drawing process. The UV-Vis spectra of the glasses showed Tb3+ electronic transitions and optical windows varying from 0.4 to 1.6 µm. The magneto-optical properties and the paramagnetic behaviors of the glasses were investigated using Faraday rotation experiments. The Verdet constant (VB) values were calculated at 500, 650, 880, 1050, 1330, and 1550 nm. The maximum VB values obtained at 650 and 1550 nm for the glass with x = 18 mol% were -128 and - 17.6 rad T-1 m-1, respectively. The VB values at 500 and 1550 nm for the optical fiber containing 8 mol% of Tb4O7 were - 110.2 and - 9.5 rad T-1 m-1, respectively, while the optical loss at around 880 nm was 6.4 dB m-1.

Label-Free Ultrasensitive and Environment-Friendly Immunosensor Based on a Silica Optical Fiber for the Determination of Ciprofloxacin in Wastewater Samples.

Emerging contaminants, including pharmaceutical compounds, are receiving research attention as a result of their widespread presence in effluents and wastewater treatment plants (WWTPs). The antibiotic ciprofloxacin (CIP) is extensively employed to treat infections in animal and human medicine. Both CIP and its metabolites are common contaminants found in WWTPs. In this study, a label-free ultrasensitive U-bent optical fiber-based immunosensor for the determination of CIP in wastewater samples was developed using the properties of the conducting polymer polyaniline (PANI). The anti-CIP immunoglobulin G (IgG) was deposited on a silica optical fiber surface previously functionalized with PANI. Scanning electron microscopy and micro-Raman spectroscopy were used to investigate the surface of the immunosensor. The analysis of CIP in wastewater was performed without the use of an organic solvent or sample preparation steps, with only the sample dilution in saline buffer (pH = 7.4). The linear range for CIP was from 0.01 to 10,000 ng L-1. The detection limit was 3.30 × 10-3 ng L-1 and the quantification limit was 0.01 ng L-1. The immunosensor provided a high average recovery of 91% after spiking wastewater samples with CIP at a concentration of 9,100 ng L-1. The method was applied in triplicate to wastewater samples from Quebec (Canada), obtaining concentrations of 549 and 267 ng L-1. A comparison with a reference method showed no significant difference (t-test at 95% confidence). The new technique developed is selective, allowing a quantitative analysis of CIP in wastewater.

Simple, fast and environmentally friendly method to determine ciprofloxacin in wastewater samples based on an impedimetric immunosensor.

In this study an impedimetric immunosensor was developed in order to determine ciprofloxacin (CIP) in wastewater samples, an emergent contaminant widely found in wastewater. To achieve this, an anti-ciprofloxacin antibody was immobilized on the surface of a printed carbon electrode. Then, the developed immunosensor was applied in wastewater samples from Université Laval residences (Québec, Canada) through the load transfer resistance (R ct) using [Fe(CN)6]3-/4- as a redox probe, and the average CIP concentration was found to be 2.90 × 10-4 µg mL-1. The observed R ct changes presented a linear relationship from CIP concentrations of 10-5 to 1.0 µg mL-1, with detection and quantification limits of 2.50 × 10-6 and 7.90 × 10-6 µg mL-1, respectively. The immunosensor presented high selectivity and repeatability, as well as a good recovery rate in wastewater samples (97%). Significant interference with other compounds was not observed. The proposed method requires only 30 µL of sample without the use of organic solvents or preceding sample preparation and/or extraction techniques. Moreover, the method is fast: only 20 min of incubation followed by 2 min of analysis time was sufficient to obtain the CIP concentration. The method's estimated cost is U$ 2.00 per sample.

Experimental and Theoretical Study of SbPO4 under Compression.

SbPO4 is a complex monoclinic layered material characterized by a strong activity of the nonbonding lone electron pair (LEP) of Sb. The strong cation LEP leads to the formation of layers piled up along the a axis and linked by weak Sb-O electrostatic interactions. In fact, Sb has 4-fold coordination with O similarly to what occurs with the P-O coordination, despite the large difference in ionic radii and electronegativity between both elements. Here we report a joint experimental and theoretical study of the structural and vibrational properties of SbPO4 at high pressure. We show that SbPO4 is not only one of the most compressible phosphates but also one of the most compressible compounds of the ABO4 family. Moreover, it has a considerable anisotropic compression behavior, with the largest compression occurring along a direction close to the a axis and governed by the compression of the LEP and the weak interlayer Sb-O bonds. The strong compression along the a axis leads to a subtle modification of the monoclinic crystal structure above 3 GPa, leading from a 2D to a 3D material. Moreover, the onset of a reversible pressure-induced phase transition is observed above 9 GPa, which is completed above 20 GPa. We propose that the high-pressure phase is a triclinic distortion of the original monoclinic phase. The understanding of the compression mechanism of SbPO4 can aid to improve the ion intercalation and catalytic properties of this layered compound.

Phosphate glasses via coacervation route containing CdFe2O4 nanoparticles: structural, optical and magnetic characterization.

CdFe2O4 nanoparticles of around 3.9 nm were synthesized using the coprecipitation method and protected by a silica layer. The nanoparticles were mixed with a coacervate and transformed into phosphate glasses with 1, 4 and 8% in mass of nanoparticles by the melt-quenching method. TEM images confirm that the nanoparticles were successfully incorporated into the matrix without inducing crystallization. 31P NMR and Raman spectral analyses show that new P-O-Si bonds are formed in the glasses containing nanoparticles. The glass transition increases as a function of the nanoparticle content due to an increase in the connectivity of the phosphate glass chains. The UV-Vis spectra show bands at 415 and 520 nm assigned to Fe3+ ions and at 1025 nm, characteristic of Fe2+ ions, indicating that some of the nanoparticles dissolve during the melting process. The sample with 8% CdFe2O4 presents a paramagnetic behavior. The glasses obtained are transparent, non-hygroscopic and possess enormous thermal stability which is important for the production of optical devices.

Optical sensor platform based on cellulose nanocrystals (CNC) - 4'-(hexyloxy)-4-biphenylcarbonitrile (HOBC) bi-phase nematic liquid crystal composite films.

The preparation of composite materials has gained tremendous attention due to the potential synergy of the combined materials. Here we fabricate novel thermal/electrical responsive photonic composite films combining cellulose nanocrystals (CNC) with a low molecular weight nematic liquid crystal (NLC), 4'-(hexyloxy)-4-biphenylcarbonitrile (HOBC). The obtained composite material combines both intense structural coloration of photonic cellulose and thermal and conductive properties of NLC. Scanning electron microscopy (SEM) results confirmed that liquid crystals coated CNC films maintain chiral nematic structure characteristic of CNC film and simultaneously, transversal cross-section scanning electron microscopy images indicated penetration of liquid crystals through the CNC layers. Investigated composite film maintain NLC optical properties being switchable as a function of temperature during heating/cooling cycles. The relationship between the morphology and thermoresponsive in the micro/nanostructured materials was investigated by using transmission optical microscopy (TOM). Conductive response of the composite films was proved by Electrostatic force microscopy (EFM) measurement. Designed thermo- and electro-responsive materials open novel simple pathway of fabrication of CNC-based materials with tunable properties.

Influence on the oxidative potential of a heavy-duty engine particle emission due to selective catalytic reduction system and biodiesel blend.

Although the particulate matter (PM) emissions from biodiesel fuelled engines are acknowledged to be lower than those of fossil diesel, there is a concern on the impact of PM produced by biodiesel to human health. As the oxidative potential of PM has been suggested as trigger for adverse health effects, it was measured using the Electron Spin Resonance (OP(ESR)) technique. Additionally, Energy Dispersive X-ray Fluorescence Spectroscopy (EDXRF) was employed to determine elemental concentration, and Raman Spectroscopy was used to describe the amorphous carbon character of the soot collected on exhaust PM from biodiesel blends fuelled test-bed engine, with and without Selective Catalytic Reduction (SCR). OP(ESR) results showed higher oxidative potential per kWh of PM produced from a blend of 20% soybean biodiesel and 80% ULSD (B20) engine compared with a blend of 5% soybean biodiesel and 95% ULSD (B5), whereas the SCR was able to reduce oxidative potential for each fuel. EDXRF data indicates a correlation of 0.99 between concentration of copper and oxidative potential. Raman Spectroscopy centered on the expected carbon peaks between 1100cm(-1) and 1600cm(-1) indicate lower molecular disorder for the B20 particulate matter, an indicative of a more graphitic carbon structure. The analytical techniques used in this study highlight the link between biodiesel engine exhaust and increased oxidative potential relative to biodiesel addition on fossil diesel combustion. The EDXRF analysis confirmed the prominent role of metals on free radical production. As a whole, these results suggest that 20% of biodiesel blends run without SCR may pose an increased health risk due to an increase in OH radical generation.

Bulk photochromism in a tungstate-phosphate glass: a new optical memory material?

In this work, we present a new photochromic tungstate based glass which have both absorption coefficient and refractive index modified under laser exposure. The photosensitive effect is superficial under ultraviolet (UV) irradiation but occurs in the entire volume of the glass under visible irradiation. The effect can be obtained in any specific point inside the volume using an infrared femtosecond laser. In addition, the photosensitive phenomenon can be erased by specific heat treatment. This glass can be useful to substitute actual data storage supports and is a promising material for 3-dimensional (3D) and holographic optical storage.