RESUMO
Highly monodisperse and pure samples of atomically precise gold nanomolecules (AuNMs) are essential to understand their properties and to develop applications using them. Unfortunately, the synthetic protocols that yield a single-sized nanomolecule in a single-step reaction are unavailable. Instead, we observe a polydisperse product with a mixture of core sizes. This product requires post-synthetic reactions and separation techniques to isolate pure nanomolecules. Solvent fractionation based on the varying solubility of different sizes serves well to a certain extent in isolating pure compounds. It becomes tedious and offers less control while separating AuNMs that are very similar in size. Here, we report the versatile and the indispensable nature of using size exclusion chromatography (SEC) as a tool for separating nanomolecules and nanoparticles. We have demonstrated the following: (1) the ease of separation offered by SEC over solvent fractionation; (2) the separation of a wider size range (â¼5-200 kDa or â¼1-3 nm) and larger-scale separation (20-100 mg per load); (3) the separation of closely sized AuNMs, demonstrated by purifying Au137(SR)56 from a mixture of Au329(SR)84, Au144(SR)60, Au137(SR)56, and Au130(SR)50, which could not be achieved using solvent fractionation; (4) the separation of AuNMs protected by different thiolate ligands (aliphatic, aromatic, and bulky); and (5) the separation can be improved by increasing the column length. Mass spectrometry was used for analyzing the SEC fractions.
RESUMO
Ultrastable gold nanomolecule Au144(SCH2CH2Ph)60 upon etching with excess tert-butylbenzenethiol undergoes a core-size conversion and compositional change to form an entirely new core of Au133(SPh-tBu)52. This conversion was studied using high-resolution electrospray mass spectrometry which shows that the core size conversion is initiated after 22 ligand exchanges, suggesting a relatively high stability of the Au144(SCH2CH2Ph)38(SPh-tBu)22 intermediate. The Au144 â Au133 core size conversion is surprisingly different from the Au144 â Au99 core conversion reported in the case of thiophenol, -SPh. Theoretical analysis and ab initio molecular dynamics simulations show that rigid p-tBu groups play a crucial role by reducing the cluster structural freedom, and protecting the cluster from adsorption of exogenous and reactive species, thus rationalizing the kinetic factors that stabilize the Au133 core size. This 144-atom to 133-atom nanomolecule's compositional change is reflected in optical spectroscopy and electrochemistry.
RESUMO
Crystal structure determination has revolutionized modern science in biology, chemistry, and physics. However, the difficulty in obtaining periodic crystal lattices which are needed for X-ray crystal analysis has hindered the determination of atomic structure in nanomaterials, known as the "nanostructure problem". Here, by using rigid and bulky ligands, we have overcome this limitation and successfully solved the X-ray crystallographic structure of the largest reported thiolated gold nanomolecule, Au133S52. The total composition, Au133(SPh-tBu)52, was verified using high resolution electrospray ionization mass spectrometry (ESI-MS). The experimental and simulated optical spectra show an emergent surface plasmon resonance that is more pronounced than in the slightly larger Au144(SCH2CH2Ph)60. Theoretical analysis indicates that the presence of rigid and bulky ligands is the key to the successful crystal formation.
RESUMO
A new aromatic thiolate protected gold nanomolecule Au99(SPh)42 has been synthesized by reacting the highly stable Au144(SCH2CH2Ph)60 with thiophenol, HSPh. The ubiquitous Au144(SR)60 is known for its high stability even at elevated temperature and in the presence of excess thiol. This report demonstrates for the first time the reactivity of the Au144(SCH2CH2Ph)60 with thiophenol to form a different 99-Au atom species. The resulting Au99(SPh)42 compound, however, is unreactive and highly stable in the presence of excess aromatic thiol. The molecular formula of the title compound is determined by high resolution electrospray mass spectrometry (ESI-MS) and confirmed by the preparation of the 99-atom nanomolecule using two ligands, namely, Au99(SPh)42 and Au99(SPh-OMe)42. This mass spectrometry study is an unprecedented advance in nanoparticle reaction monitoring, in studying the 144-atom to 99-atom size evolution at such high m/z (â¼12k) and resolution. The optical and electrochemical properties of Au99(SPh)42 are reported. Other substituents on the phenyl group, HS-Ph-X, where X = -F, -CH3, -OCH3, also show the Au144 to Au99 core size conversion, suggesting minimal electronic effects for these substituents. Control experiments were conducted by reacting Au144(SCH2CH2Ph)60 with HS-(CH2)n-Ph (where n = 1 and 2), bulky ligands like adamantanethiol and cyclohexanethiol. It was observed that conversion of Au144 to Au99 occurs only when the phenyl group is directly attached to the thiol, suggesting that the formation of a 99-atom species is largely influenced by aromaticity of the ligand and less so on the bulkiness of the ligand.
RESUMO
The physicochemical properties of gold:thiolate nanomolecules depend on their crystal structure and the capping ligands. The effects of protecting ligands on the crystal structure of the nanomolecules are of high interest in this area of research. Here we report the crystal structure of an all aromatic thiophenolate-capped Au36(SPh)24 nanomolecule, which has a face-centered cubic (fcc) core similar to other nanomolecules such as Au36(SPh-tBu)24 and Au36(SC5H9)24 with the same number of gold atoms and ligands. The results support the idea that a stable core remains intact even when the capping ligand is varied. We also correct our earlier assignment of "Au36(SPh)23" which was determined based on MALDI mass spectrometry which is more prone to fragmentation than ESI mass spectrometry. We show that ESI mass spectrometry gives the correct assignment of Au36(SPh)24, supporting the X-ray crystal structure. The electronic structure of the title compound was computed at different levels of theory (PBE, LDA, and LB94) using the coordinates extracted from the single crystal X-ray diffraction data. The optical and electrochemical properties were determined from experimental data using UV-vis spectroscopy, cyclic voltammetry, and differential pulse voltammetry. Au36(SPh)24 shows a broad electrochemical gap near 2 V, a desirable optical gap of â¼1.75 eV for dye-sensitized solar cell applications, as well as appropriately positioned electrochemical potentials for many electrocatalytic reactions.
RESUMO
Au137(SR)56, a nanomolecule with a precise number of metal atoms and ligands, was synthesized. The composition was confirmed by MALDI and ESI mass spectrometry using three unique ligands (-SCH2CH2Ph, -SC6H13, and -SC4H9) and nano-alloys with Ag and Pd. The electrocatalytic properties were tested for CO2 reduction.
RESUMO
Gold nanomolecules with a precise number of gold atoms and ligands have promise for catalytic, optical, and biomedical applications. For practical applications, it is essential to develop synthetic protocols to prepare monodisperse gold nanomolecules. A typical synthesis yields a number of nanomolecules with discrete numbers of core atoms. Thermochemical treatment in the presence of excess thiol, etching, is known to narrow down the number of discrete nanomolecules, by selective degradation of sizes with lower stability. Au38(SR)24 and Au40(SR)24 are abundantly formed in these etching reactions due to their extraordinary stability to chemical etching. These nanomolecules are of high interest due in part to its stability, X-ray crystallographic structure availability (Au38), and intrinsic chirality arising from the arrangement of the Au-SR interface. However, the synthetic routes typically yield a mixture of Au38 and Au40, demanding extensive separation protocols. Here, we present a synthetic route to prepare either Au38 or Au40 exclusively in the product of etching. This was made possible by conducting a comprehensive mechanistic study starting from single-sized reactant. Au67 on etching yields Au40 exclusively. Au(103-105)(SR)(45-46) on etching also yields Au40 exclusively. Clusters of various sizes smaller than Au67 on etching yield Au38 exclusively. This is the first direct evidence for the exclusive formation of Au38 and Au40 nanomolecules by core size conversion. Mass spectrometry was used to study the core size conversion reactions to understand the mechanism. Au38 and Au40 nanomolecules form via different intermediates, as observed in the mass spectrometry data.
RESUMO
High resolution ESI mass spectrometry of the "22 kDa" nanocluster reveals the presence of a mixture containing Au103(SR)45, Au104(SR)45, Au104(SR)46, and Au105(SR)46 nanoclusters, where R = -CH2CH2Ph. MALDI TOF MS data confirm the purity of the sample and a UV-vis spectrum shows minor features. Au102(SC6H5COOH)44, whose XRD crystal structure was recently reported, is not observed. This is due to ligand effects, because the 102 : 44 composition is produced using aromatic ligands. However, the 103-, 104- and 105-atom nanoclusters, protected by -SCH2CH2Ph and -SC6H13 ligands, are at or near 58 electron shell closing.
RESUMO
The preparation of gold nanomolecules with sizes other than Au(25)(SR)(18), Au(38)(SR)(24), Au(102)(SR)(44), and Au(144)(SR)(60) has been hampered by stability issues and low yields. Here we report a procedure to prepare Au(67)(SR)(35), for either R = -SCH(2)CH(2)Ph or -SC(6)H(13), allowing high-yield isolation (34%, ~10-mg quantities) of the title compound. Product high purity is assessed at each synthesis stage by rapid MALDI-TOF mass-spectrometry (MS), and high-resolution electrospray-ionization MS confirms the Au(67)(SR)(35) composition. Electronic properties were explored using optical absorption spectroscopy (UV-visible-NIR regions) and electrochemistry (0.74 V spacing in differential-pulsed-voltammetry), modes of ligand binding were studied by NMR spectroscopy ((13)C and (1)H), and structural characteristics of the metal atom core were determined by powder X-ray measurements. Models featuring a Au(17) truncated-decahedral inner core encapsulated by the 30 anchoring atoms of 15 staple-motif units have been investigated with first-principles electronic structure calculations. This resulted in identification of a structure consistent with the experiments, particularly, the opening of a large gap (~0.75 eV) in the (2-) charge-state of the nanomolecule. The electronic structure is analyzed within the framework of a superatom shell model. Structurally, the Au(67)(SR)(35) nanomolecule is the smallest to adopt the complete truncated-decahedral motif for its core with a surface structure bearing greater similarity to the larger nanoparticles. Its electronic HOMO-LUMO gap (~0.75 eV) is nearly double that of the larger Au(102) compound and it is much smaller than that of the Au(38) one. The intermediary status of the Au(67)(SR)(35) nanomolecule is also reflected in both its optical and electrochemical characteristics.
RESUMO
A new core size protected completely by an aromatic thiol, Au(36)(SPh)(23), is synthesized and characterized by MALDI-TOF mass spectrometry and UV-visible spectroscopy. The synthesis involving core size changes is studied by MS, and the complete ligand coverage by aromatic thiol group is shown by NMR.