RESUMO
Ni-Mn-based Heusler alloys are known to demonstrate magnetic shape memory and giant magnetocaloric effect (MCE). These effects depend on the phases, crystallographic and magnetic phase transitions, and the crystallographic texture characteristics. These structural characteristics, in turn, are a function of the processing parameters. In the current work, Ni55.5Mn18.8Ga24Si1.7 Heusler alloy was processed by melt-spinning under a helium atmosphere. This process results in a fine microstructure. The ribbon that was produced with a narrower nozzle width, faster wheel speed, and higher cast temperature, indicating a faster cooling rate, had double the magnetic entropy change close to room temperature. However, the other ribbon demonstrated a large entropy change over a broader temperature range, extending its usability. The effect of the melt-spinning process parameters on the developing microstructure, crystallographic structure and texture, transformation temperatures, and the magnetic entropy change were studied to explain the difference in magnetocaloric behavior.
RESUMO
The effects of micro-additions of boron and zirconium on grain-boundary (GB) structure and strength in polycrystalline γ(f.c.c.) plus γ'(L12) strengthened Co-9.5Al-7.5W-X at. % alloys (X = 0-Temary, 0.05B, 0.01B, 0.05Zr, and 0.005B-0.05Zr at. %) are studied. Creep tests performed at 850 °C demonstrate that GB strength and cohesion limit the creep resistance and ductility of the ternary B- and Zr-free alloy due to intergranular fracture. Alloys with 0.05B and 0.005B-0.05Zr both exhibit improved creep strength due to enhanced GB cohesion, compared to the baseline ternary Co-9.5Al-7.5W alloy, but alloys containing 0.01B or 0.05Zr additions displayed no benefit. Atom-probe tomography is utilized to measure GB segregation, where B and Zr are demonstrated to segregate at GBs. A Gibbsian interfacial excess of 5.57 ± 1.04 atoms nm-2 was found for B at a GB in the 0.01B alloy and 2.88 ± 0.81 and 2.40 ± 0.84 atoms nm-2 for B and Zr, respectively, for the 0.005B-0.05Zr alloy. The GBs in the highest B-containing (0.05B) alloy exhibit micrometer-sized boride precipitates with adjacent precipitate denuded-zones (PDZs), whereas secondary precipitation at the GBs is not present in the other four alloys. The 0.05B alloy has the smallest room temperature yield strength, by 6 %, which is attributed to the PDZs, but it exhibits the largest increase in creep strength (with an ~2.5 order of magnitude decrease in the minimum strain rate for a given stress at 850 °C) over the baseline Co-9.5Al-7.5W alloy.
RESUMO
The influence of W on the temporal evolution of gamma' precipitation toward equilibrium in a model Ni-Al-Cr alloy is investigated by three-dimensional atom-probe (3DAP) microscopy and transmission electron microscopy (TEM). We report on the alloys Ni-10 Al-8.5 Cr (at.%) and Ni-10 Al-8.5 Cr-2 W (at.%), which were aged isothermally in the gamma + gamma' two-phase field at 1073 K, for times ranging from 0.25 to 264 h. Spheroidal-shaped gamma' precipitates, 5-15 nm diameter, form during quenching from above the solvus temperature in both alloys at a high number density (approximately 1023 m-3). As gamma' precipitates grow with aging at 1073 K, a transition from spheroidal- to cuboidal-shaped precipitates is observed in both alloys. The elemental partitioning and spatially resolved concentration profiles across the gamma' precipitates are obtained as a function of aging time from three-dimensional atom-by-atom reconstructions. Proximity histogram concentration profiles (Hellman et al., 2000) of the quaternary alloy demonstrate that W concentration gradients exist in gamma' precipitates in the as-quenched and 0.25-h aging states, which disappear after 1 h of aging. The diffusion coefficient of W in gamma' is estimated to be 6.2 x 10-20 m2 s-1 at 1073 K. The W addition decreases the coarsening rate constant, and leads to stronger partitioning of Al to gamma' and Cr to gamma.