RESUMO
Photocatalytic CO2 reduction to CO under unassisted (unbiased) conditions was recently demonstrated using heterostructure catalysts that combine p-type GaN with plasmonic Au nanoparticles and Cu nanoparticles as cocatalysts (p-GaN/Al2O3/Au/Cu). Here, we investigate the mechanistic role of Cu in p-GaN/Al2O3/Au/Cu under unassisted photocatalytic operating conditions using Cu K-edge X-ray absorption spectroscopy and first-principles calculations. Upon exposure to gas-phase CO2 and H2O vapor reaction conditions, the composition of the Cu nanoparticles is identified as a mixture of CuI and CuII oxide, hydroxide, and carbonate compounds without metallic Cu. These composition changes, indicating oxidative conditions, are rationalized by bulk Pourbaix thermodynamics. Under photocatalytic operating conditions with visible light excitation of the plasmonic Au nanoparticles, further oxidation of CuI to CuII is observed, indicating light-driven hole transfer from Au-to-Cu. This observation is supported by the calculated band alignments of the oxidized Cu compositions with plasmonic Au particles, where light-driven hole transfer from Au-to-Cu is found to be thermodynamically favored. These findings demonstrate that under unassisted (unbiased) gas-phase reaction conditions, Cu is found in carbonate-rich oxidized compositions rather than metallic Cu. These species then act as the active cocatalyst and play an oxidative rather than a reductive role in catalysis when coupled with plasmonic Au particles for light absorption, possibly opening an additional channel for water oxidation in this system.
RESUMO
Electron energy-loss spectroscopy (EELS) can measure similar information to x-ray, UV-Vis, and IR spectroscopies but with atomic resolution and increased scattering cross-sections. Recent advances in electron monochromators have expanded EELS capabilities from chemical identification to the realms of synchrotron-level core-loss measurements and to low-loss, 10-100 meV excitations, such as phonons, excitons, and valence structures. EELS measurements are easily correlated with electron diffraction and atomic-scale real-space imaging in a transmission electron microscope (TEM) to provide detailed local pictures of quasiparticle and bonding states. This perspective provides an overview of existing high-resolution EELS (HR-EELS) capabilities while also motivating the powerful next step in the field-ultrafast EELS in a TEM. Ultrafast EELS aims to combine atomic-level, element-specific, and correlated temporal measurements to better understand spatially specific excited-state phenomena. Ultrafast EELS measurements also add to the abilities of steady-state HR-EELS by being able to image the electromagnetic field and use electrons to excite photon-forbidden and momentum-specific transitions. We discuss the technical challenges ultrafast HR-EELS currently faces, as well as how integration with in situ and cryo measurements could expand the technique to new systems of interest, especially molecular and biological samples.