RESUMO
In the present work, we take the influences of activated slip systems and the orientation spread into account to predict the cup height using analytical earing models and compare the predicted results with experimental results. The effect of boundary conditions of the various stress states and the work hardening exponents are compared and discussed for profile of single crystals. A stress ratio of -0.3 and a hardening exponent of 0.3 are selected for the prediction of earing profiles. The combination of activation of the single slip systems and orientation spread provides the best prediction of deep-drawing profiles. With further consideration of the orientation spread, an increase in the total orientation leads to peak-broadening, i.e., broad and smooth ears. Furthermore, the difference of the height between the maximum and minimum value of cup profiles is reduced because of the orientation spread. The profile for C is found with single ear at 45°, while the other components individually reveal double ears at 35° and 50° for S, at 15° and 45° for B, at 0° and 90° for Cube, at 5° and 90° for r-Cube, and at 15° and 90° for G. Herein, simple analytical earing models are proposed to understand the effects of slip systems and the orientation spread. The deep-drawing profiles are predicted with six major texture components.
RESUMO
In this study, 22Cr25NiWCuCo(Nb) heat-resistant steel specimens with high Cr and Ni contents were adopted to investigate the effect of Nb content on thermal and precipitation behavior. Differential scanning calorimetry profiles revealed that the melting point of the 22Cr25NiWCuCo(Nb) steel specimens decreased slightly with the Nb content. After heat treatment at 1200 °C for 2 h, the precipitates dissolved in a Nb-free steel matrix. In addition, the Z phase (CrNb(C, N)) and MX (Nb(C, N), (Cr, Fe)(C, N), and NbC) could be observed in the Nb-containing steel specimens. The amount and volume fraction of the precipitates increased with the Nb content, and the precipitates were distributed heterogeneously along the grain boundary and inside the grain. Even when the heat treatment duration was extended to 6 h, the austenitic grain size and precipitates became coarser; the volume fraction of the precipitates also increased at 1200 °C. The Z phase, rather than the MX phase, became the dominant precipitates at this temperature.
RESUMO
In this study, 2205 duplex stainless steel (DSS) was employed to enhance the antibacterial properties of material through silver doping. The results demonstrated that silver-doped 2205 DSS produces an excellent bacteria-inhibiting effect against Escherichia coli and Staphylococcus aureus. The antibacterial rates were 100% and 99.5%, respectively. Because the mutual solubility of silver and iron is very low in both the solid and liquid states, a silver-rich compound solidified and dispersed at the ferrite/austenite interface and the ferrite, austenite, and secondary austenite phases in silver-doped 2205 DSS. Doping 2205 DSS with silver caused the Creq/Nieq ratio of ferrite to decrease; however, the lower Creq/Nieq ratio promoted the rapid nucleation of γ2-austenite from primary α-ferrite. After 12h of homogenisation treatment at 1200 °C, the solubility of silver in the γ-austenite and α-ferrite phases can be increased by 0.10% and 0.09%, respectively. Moreover, silver doping was found to accelerate the dissolution of secondary austenite in a ferrite matrix during homogenisation.