Room-temperature, atmospheric-pressure microsputtering of dense, electrically conductive, sub-100 nm gold films.

In this study, we investigate the effects of deposition parameters (i.e. gas flow rates, bias voltages, and nozzle-to-substrate separation) on the microstructure of <100 nm thick gold deposits made with a room-temperature, atmospheric-pressure, ion-drag microsputterer. Without resorting to the use of vacuum or substrate heating, optimization of the printing process yields dense, continuous deposits (96.5% coverage) with low electrical resistivity (45 µΩ cm). Using statistical analysis, we developed a simple model that provides insight into the dynamics of such a printing method; based on this model, we identify electrostatic effects as the most important factor that influences the deposition process.

Enhanced coupling of broadband light into amorphous silicon via periodic nanoplasmonic arrays.

Achieving enhanced coupling of solar radiation over the full range of the silicon absorption spectrum up to the bandgap is essential for increased efficiency of solar cells, especially thin film versions. While many designs for enhancing trapping of radiation have been explored, detailed measurements of light scattering inside silicon cells is still lacking. Here, we demonstrate experimentally and computationally that plasmonic-assisted localized and traveling modes can efficiently couple red and infrared radiation into ultrathin amorphous silicon (a-Si) layers. Utilizing patterned periodic arrays of aluminum nanostructures on thin a-Si, we perform specular and diffuse reflectivity and transmission measurements over a broad spectrum. Based on these results, we are able to separate parasitic absorption in aluminum plasmonic arrays from enhanced light absorption in the 200 nm thick amorphous silicon layer, as compared to a blank silicon layer. We discover a very efficient near-infrared a-Si absorption mechanism that occurs at the transition from the radiative to evanescent diffractive coupling, analogous to earlier surface-enhanced infrared studies. These results represent a direct demonstration of enhanced radiation coupling into silicon due to large angle scattering and show a path forward to improved ultrathin solar cell efficiency.

Identification of intrinsic and reflex contributions to human ankle stiffness dynamics.

We have examined dynamic stiffness at the human ankle using position perturbations which were designed to provide a wide-bandwidth input with low average velocity. A parallel-cascade, nonlinear system identification technique was used to separate overall stiffness into intrinsic and reflex components. Intrinsic stiffness was described by a linear, second-order system similar to that demonstrated previously. Reflex stiffness dynamics were more complex, comprising a delay, a unidirectional rate-sensitive element and then lowpass dynamics. Reflex mechanisms were found to be most important at frequencies of 5-10 Hz. The gain and dynamics of reflex stiffness varied strongly with the parameters of the perturbation, the gain decreasing as the mean velocity of the perturbation increased. Under some conditions, torques generated by reflex mechanisms were of the same magnitude as those from intrinsic mechanisms. It is concluded that reflex stiffness can be large enough to be important functionally, but that its effects will depend strongly upon the particular conditions.