RESUMO
Ultrathin carbon nanomembranes (CNMs) are two-dimensional materials (2DM) of a few nm thickness with sub-nm intrinsic pores that mimic the biofiltration membranes found in nature. They enable highly selective, permeable, and energy-efficient water separation and can be produced at large scales on porous substrates with tuned properties. The present work reports the mechanical performance of such CNMs produced by p-nitrobiphenyl phosphonic acid (NBPS) or polyvinylbiphenyl (PVBP) and their composite membranes of microporous supporting substrates, which constitute indispensable information for ensuring their mechanical stability during operation. Measuring the nanomechanical properties of the ultrathin material was achieved by atomic force microscopy (AFM) on membranes both supported on flat substrates and suspended on patterned substrates ("composite membrane"). The AFM analysis showed that the CNMs presented Young's modulus in the range of 2.5-8 GPa. The composite membranes' responses were investigated by tensile testing in a micro-tensile stage as a function of substrate thickness and substrate pore density and diameter, which were found to affect the mechanical properties. Thermogravimetric analysis was used to investigate the thermal stability of composite membranes at high temperatures. The results revealed the structural integrity of CNMs, while critical parameters governing their mechanical response were identified and discussed.
RESUMO
Successful ways of fully exploiting the excellent structural and multifunctional performance of graphene and related materials are of great scientific and technological interest. New opportunities are provided by the fabrication of a novel class of nanocomposites with a nanolaminate architecture. In this work, by using the iterative lift-off/float-on process combined with wet depositions, we incorporated cm-size graphene monolayers produced via Chemical Vapour Deposition into a poly (methyl methacrylate) (PMMA) matrix with a controlled, alternate-layered structure. The produced nanolaminate shows a significant improvement in mechanical properties, with enhanced stiffness, strength and toughness, with the addition of only 0.06 vol% of graphene. Furthermore, oxygen and carbon dioxide permeability measurements performed at different relative humidity levels, reveal that the addition of graphene leads to significant reduction of permeability, compared to neat PMMA. Overall, we demonstrate that the produced graphene-PMMA nanolaminate surpasses, in terms of gas barrier properties, the traditional discontinuous graphene-particle composites with a similar filler content. Moreover, we found that the gas permeability through the nanocomposites departs from a monotonic decrease as a function of relative humidity, which is instead evident in the case of the pure PMMA nanolaminate. This work suggests the possible use of Chemical Vapour Deposition graphene-polymer nanolaminates as a flexible gas barrier, thus enlarging the spectrum of applications for this novel material.
RESUMO
The use of graphene in a form of discontinuous flakes in polymer composites limits the full exploitation of the unique properties of graphene, thus requiring high filler loadings for achieving- for example- satisfactory electrical and mechanical properties. Herein centimetre-scale CVD graphene/polymer nanolaminates have been produced by using an iterative 'lift-off/float-on' process and have been found to outperform, for the same graphene content, state-of-the-art flake-based graphene polymer composites in terms of mechanical reinforcement and electrical properties. Most importantly these thin laminate materials show a high electromagnetic interference (EMI) shielding effectiveness, reaching 60 dB for a small thickness of 33 µm, and an absolute EMI shielding effectiveness close to 3·105 dB cm2 g-1 which is amongst the highest values for synthetic, non-metallic materials produced to date.
RESUMO
Aerogels have attracted significant attention recently due to their ultra-light weight porous structure, mechanical robustness, high electrical conductivity, facile scalability and their use as gas and oil absorbers. Herein, we examine the multi-functional properties of hybrid aerogels consisting of reduced graphene oxide (rGO) integrated with hexagonal boron nitride (hBN) platelets. Using a freeze-drying approach, hybrid aerogels are fabricated by simple mixing with various volume fractions of hBN and rGO up to 0.5/0.5 ratio. The fabrication method is simple, cost effective, scalable and can be extended to other 2D materials combinations. The hybrid rGO/hBN aerogels (HAs) are mechanically robust and highly compressible with mechanical properties similar to those of the pure rGO aerogel. We show that the presence of hBN in the HAs enhances the gas absorption capacities of formaldehyde and water vapour up to ~ 7 and > 8 times, respectively, as compared to pure rGO aerogel. Moreover, the samples show good recoverability, making them highly efficient materials for gas absorption applications and for the protection of artefacts such as paintings in storage facilities. Finally, even in the presence of large quantity of insulating hBN, the HAs are electrically conductive, extending the potential application spectrum of the proposed hybrids to the field of electro-thermal actuators. The work proposed here paves the way for the design and production of novel 2D materials combinations with tailored multi-functionalities suited for a large variety of modern applications.
RESUMO
Poly(methyl methacrylate) (PMMA) is a glassy engineering polymer that finds extensive use in a number of applications. Over the past decade, thin films of PMMA were combined with graphene or other two-dimensional materials for applications in the area of nanotechnology. However, the effect of size upon the mechanical behavior of this thermoplastic polymer has not been fully examined. In this work, we adopted a homemade nanomechanical device to assess the yielding and fracture characteristics of freestanding, ultrathin (180-280 nm) PMMA films of a loaded area as large as 0.3 mm2. The measured values of Young's modulus and yield strength were found to be broadly similar to those measured in the bulk, but in contrast, all specimens exhibited a quite surprisingly high strain at failure (>20%). Detailed optical examination of the specimens during tensile loading showed clear evidence of craze development which however did not lead to premature fracture. This work may pave the way for the development of glassy thermoplastic films with high ductility at ambient temperatures.
RESUMO
Graphene is susceptible to morphological instabilities such as wrinkles and folds, which result from the imposition of thermo-mechanical stresses upon cooling from high temperatures and/ or under biaxial loading. A particular pattern encountered in CVD graphene is that of mosaic formation. Although it is understood that this pattern results from the severe biaxial compression upon cooling from high temperatures, it has not been possible to create such a complex pattern at room temperature by mechanical loading. Herein, we have managed by means of lateral wrinkling induced by tension and Euler buckling resulting from uniaxial compression upon unloading, to create such patterns in exfoliated graphene. We also show that these patterns can be used as channels for trapping or administering fluids at interstitial space between graphene and its support. This opens a whole dearth of new applications in the area of nano-fluidics but also in photo-electronics and sensor technologies.