Improving the Performance of Polymer Solar Cells with Benzo[ghi]perylenetriimide-Based Small-Molecules as Interfacial Layers.

In this study, we prepared three benzo[ghi]perylenetriimide (BPTI) conjugated molecules as electron-transporting surface-modifying layers for polymer solar cells (PSCs). These three BPTI derivatives differed in the nature of their terminal functionalities, featuring butylamine (C3NH2), propylammonium iodide (C3NH3I), and butyldimethylamine (C3DMA) units, respectively. We evaluated the optoelectronic properties of PTB7-Th: PC71BM blends modified with these interfacial layers, as well as the performance of resulting PSCs. We used UV-Vis spectroscopy, atomic force microscopy, surface energy analysis, ultraviolet photoelectron spectroscopy, and photoelectric flow measurements to examine the phenomena behind the changes in the optoelectronic behavior of these blend films. The presence of a BPTI derivative changed the energy band alignment at the ZnO-active layer interface, leading to the ZnO film behaving more efficiently as an electron-extraction electrode. Modifying the ZnO surface with the BPTI-C3NH3I derivative resulted in a best power conversion efficiency (PCE) of 10.2 ± 0.53% for the PTB7-Th:PC71BM PSC (cf. PCE of the control device of 9.1 ± 0.13%). In addition, modification of a PM6:Y6:PCBM PSC with the BPTI-C3NH3I derivative increased its PCE from 15.6 ± 0.25% to 16.5 ± 0.18%. Thus, BPTI derivatives appear to have potential as IFLs when developing high-performance PSCs, and might also be applicable in other optoelectronic devices.

Realizing Broadband NIR Photodetection and Ultrahigh Responsivity with Ternary Blend Organic Photodetector.

With the advancement of portable optoelectronics, organic semiconductors have been attracting attention for their use in the sensing of white and near-infrared light. Ideally, an organic photodiode (OPD) should simultaneously display high responsivity and a high response frequency. In this study we used a ternary blend strategy to prepare PM6: BTP-eC9: PCBM-based OPDs with a broad bandwidth (350-950 nm), ultrahigh responsivity, and a high response frequency. We monitored the dark currents of the OPDs prepared at various PC71BM blend ratios and evaluated their blend film morphologies using optical microscopy, atomic force microscopy, and grazing-incidence wide-angle X-ray scattering. Optimization of the morphology and energy level alignment of the blend films resulted in the OPD prepared with a PM6:BTP-eC9:PC71BM ternary blend weight ratio of 1:1.2:0.5 displaying an extremely low dark current (3.27 × 10-9 A cm-2) under reverse bias at -1 V, with an ultrahigh cut-off frequency (610 kHz, at 530 nm), high responsivity (0.59 A W-1, at -1.5 V), and high detectivity (1.10 × 1013 Jones, under a reverse bias of -1 V at 860 nm). Furthermore, the rise and fall times of this OPD were rapid (114 and 110 ns), respectively.