Three-Dimensional Printing of Molecularly Imprinted Polymers by Digital Light Processing for Copper Ion Sequestration.

Highly structured, molecularly imprinted polymer (MIP) networks for copper(II) ion sequestration have been realized using the additive manufacturing technology. Photopolymerizable formulations with acrylic functional monomers and two different porogens (water and methanol) in different ratios were studied to produce emulsions with 50 vol% of the internal phase. The results of morphological characterization indicate that all MIPs have cauliflower-like multiscale structures that change as a function of the solvent combination and fabrication process. X-ray fluorescence microscopy maps presented a layered structure and homogeneous distribution of copper in the printed MIP. Copper(II) ion adsorption-desorption tests were performed on MIPs prepared using a three-dimensional (3D) printing approach and MIPs prepared by bulk polymerization. Results indicate that the 3D printed MIP is able to absorb copper up to ten times more efficiently than the nonprinted one and the printed MIP with 100% water content has the highest imprint recognition.

Environmentally Benign Fast-Degrading Conductive Composites.

An environmentally benign conductive composite that rapidly degrades in the presence of warm water via enzyme-mediated hydrolysis is described. This represents the first time that hydrolytic enzymes have been immobilized onto eco-friendly conductive carbon sources with the express purpose of degrading the encapsulating biodegradable plastic. Amano Lipase (AL)-functionalized carbon nanofibers (CNF) were compounded with polycaprolactone (PCL) to produce the composite film CNFAL-PCL (thickness ∼ 600 µm; CNFAL = 20.0 wt %). To serve as controls, films of the same thickness were also produced, including CNF-AL5-PCL (CNF mixed with AL and PCL; CNF = 19.2 wt % and AL = 5.00 wt %), CNF-PCL (CNF = 19.2 wt %), ALx-PCL (AL = x = 1.00 or 5.00 wt %), and PCL. The electrical performance of the CNF-containing composites was measured, and conductivities of 14.0 ± 2, 22.0 ± 5, and 31.0 ± 6 S/m were observed for CNFAL-PCL, CNF-AL5-PCL, and CNF-PCL, respectively. CNFAL-PCL and control films were degraded in phosphate buffer (2.00 mg/mL film/buffer) at 50 °C, and their average percent weight loss (Wtavg%) was recorded over time. After 3 h CNFAL-PCL degraded to a Wtavg% of 90.0% and had completely degraded after 8 h. This was considerably faster than CNF-AL5-PCL, which achieved a total Wtavg% of 34.0% after 16 days, and CNF-PCL, which was with a Wtavg% of 7.00% after 16 days. Scanning electron microscopy experiments (SEM) found that CNFAL-PCL has more open pores on its surface and that it fractures faster during degradation experiments which exposes the interior enzyme to water. An electrode made from CNFAL-PCL was fabricated and attached to an AL5-PCL support to form a fast-degrading thermal sensor. The resistance was measured over five cycles where the temperature was varied between 15.0-50.0 °C. The sensor was then degraded fully in buffer at 50 °C over a 48 h period.

Investigation of UV light treatment (254 nm) on the reduction of aflatoxin M1 in skim milk and degradation products after treatment.

This study investigates the reduction of aflatoxin M1 (AFM1) in skim milk by using ultraviolet light at 254 nm and the effects of influencing factors on the efficacy including treatment time (min), depth of samples (mm), contamination level (µg L-1), stirring, temperature, and fat content in milk. The colour and pH of milk samples were measured to evaluate the influence of the treatment on these values. It was found that short-wave ultraviolet radiation (UVC) reduced up to 50% of AFM1 in milk after 20 min of treatment regardless of the initial AFM1 contamination level. Treatment time, depth of samples, and stirring were all found to significantly (P < 0.05) enhance the reduction of AFM1. The milk colour was affected but there was no influence on the pH of milk samples at any duration of UV exposure. It is concluded that UVC light treatment has the potential to reduce AFM1 in milk.

3D-Printed Enzyme-Embedded Plastics.

A simple and environmentally friendly approach toward the thermoplastic processing of rapidly degradable plastic-enzyme composites using three-dimensional (3D) printing techniques is described. Polycaprolactone/Amano lipase (PCL/AL) composite films (10 mm × 10 mm; height [h] = ∼400 µm) with an AL loading of 0.1, 1.0, and 5.0% were prepared via 3D printing techniques that entail direct mixing in the solid state and thermal layer-by-layer extrusion. It was found that AL can tolerate in situ processing temperatures up to 130 °C in the solid-state for 60 min without loss of enzymatic activity. The composites were degraded in phosphate buffer (8 mg/mL, composite to buffer) for 7 days at 37 °C and the resulting average percent total weight loss (WLavg %) was found to be 5.2, 92.9, and 100%, for the 0.1, 1.0, and 5.0% films, respectively. The degradation rates of PCL/AL composites were found to be faster than AL applied externally in the buffer. Thicker PCL/AL 1.0% films (10 mm × 10 mm; h = ∼500 µm) were also degraded over a 7 day period to examine how the weight loss occurs over time with 3.0, 18.1, 36.4, 46.4, and 70.2% weight loss for days 1, 2, 3, 4, and 7, respectively. Differential scanning calorimetry (DSC) analysis shows that the film's percent crystallinity (Dxtal%) increases over time with Dxtal% = 46.5 for day 0 and 53.1% for day 7. Scanning electron microscopy (SEM) analysis found that film erosion begins at the surface and that water can penetrate the interior via surface pores activating the enzymes embedded in the film. Controlled release experiments utilizing dye-loaded PCL/AL/dye (AL = 1.0%; dye = 0.1%) composites were degraded over a 7 day period with the bulk of the dye released by the fourth day. The PCL/AL multimaterial objects containing AL-resistant polylactic acid (PLA) were also printed and degraded to demonstrate the application of this material on more complex structures.

Probing the limits of molecular imprinting: strategies with a template of limited size and functionality.

A series of polymers molecularly imprinted with the general anaesthetic propofol were synthesized using both semi- and non-covalent approaches. The polymers were evaluated with respect to template rebinding in both aqueous and organic media. In aqueous media, the observed propofol binding in these polymer systems was largely hydrophobic and non-specific in nature. In non-polar solvents such as hexane, electrostatic (hydrogen bonding) interactions dominate resulting in some selectivity. The implication of these results, in conjunction with those obtained using structures of similar size in other studies, is that propofol, a template possessing limited functionality and size, appears to define the lower limit for template size and degree of functionalization that can be used for the creation of ligand-selective recognition sites in molecularly imprinted polymers. Furthermore, studies with alternative ligands indicate that the steric crowding of a ligand's functionality to the polymer contributes to the extent of polymer-ligand recognition.