The present study examines the high-temperature (500-800 °C) oxidation behavior of Fe-10Cr-(3,5) Al alloys and studies the effect of nanocrystalline structure and Al content on their resistance to oxidation. The nanocrystalline (NC) alloy powder was synthesized via planetary ball milling. The prepared NC alloy powder was consolidated using spark plasma sintering to form NC alloys. Subsequently, an annealing of the NC alloys was performed to transform them into microcrystalline (MC) alloys. It was observed that the NC alloys exhibit superior resistance to oxidation compared to their MC counterparts at high temperatures. The superior resistance to oxidation of the NC alloys is attributed to their considerably finer grain size, which enhances the diffusion of those elements to the metal-oxide interface that forms the protective oxide layer. Conversely, the coarser grain size in MC alloys limits the diffusion of the oxide-forming components. Furthermore, the Fe-10Cr-5Al alloy showed greater resistance to oxidation than the Fe-10Cr-3Al alloy.
RESUMO
Structural changes during the deformation-induced synthesis of nanocrystalline Fe-10Cr-3Al alloy powder via high-energy ball milling followed by annealing and rapid consolidation by spark plasma sintering were investigated. Reduction in crystallite size was observed during the synthesis, which was associated with the lattice expansion and rise in dislocation density, reflecting the generation of the excess grain boundary interfacial energy and the excess free volume. Subsequent annealing led to the exponential growth of the crystallites with a concomitant drop in the dislocation density. The rapid consolidation of the as-synthesized nanocrystalline alloy powder by the spark plasma sintering, on the other hand, showed only a limited grain growth due to the reduction of processing time for the consolidation by about 95% when compared to annealing at the same temperature.