Use of Yarn and Carded Jute as Epoxy Matrix Reinforcement for the Production of Composite Materials for Application in the Wind Sector: A Preliminary Analysis for the Manufacture of Blades for Low-Intensity Winds.

The development of wind turbines for regions with low wind speeds imposes a challenge to the expansion of the corresponding energy generation capacity. The present work consists of an evaluation of the potential carded jute fiber and jute yarn to be used in the construction of a wind blade for regions of low wind intensity. The fibers used were supplied by Company Textile of Castanhal (Castanhal-Para-Brazil) and used in the study without chemical treatment in the form of single-filament fibers and yarns with a surface twist of 18.5°. The composites were produced through the resin infusion technique and underwent tensile and shear tests using 120-Ohm strain gauges and a blade extensometer to obtain the Young's modulus. In the analysis of the results, the ANOVA test was applied with a 0.05 significance level, followed by Tukey's test. The results showed that long, aligned jute fibers can be a good option for laminated structures applied in composites for small wind turbine blades.

Comparison of Young's Modulus of Continuous and Aligned Lignocellulosic Jute and Mallow Fibers Reinforced Polyester Composites Determined Both Experimentally and from Theoretical Prediction Models.

Mechanical properties of composites reinforced with lignocellulosic fibers have been researched in recent decades. Jute and mallow fibers are reinforcement alternatives, as they can contribute to increase the mechanical strength of composite materials. The present work aims to predict the Young's modulus with application of continuous and aligned lignocellulosic fibers to be applied as reinforcement in polyester matrix. Fibers were manually separated and then arranged and aligned in the polyester matrix. Composites with addition 5, 15, and 25 vol% jute and mallow fibers were produced by vacuum-assisted hand lay-up/vaccum-bagging procedure. Samples were tested in tensile and the tensile strength, elasticity modulus, and deformation were determined. Results showed that the intrinsic Young's modulus of the fibers was set at values around 17.95 and 11.72 GPa for jute and mallow fibers, respectively. Statistical analysis showed that composites reinforced with 15 and 25 vol% jute and mallow presented the highest values of tensile strength and Young's modulus. The incorporation of 25 vol% of jute and mallow fibers increased the matrix Young's modulus by 534% and 353%, respectively, effectively stiffening the composite material. Prediction models presented similar values for the Young's modulus, showing that jute and mallow fibers might be used as potential reinforcement of polymeric matrices.