Impact of try-in paste removal on the fatigue behavior of bonded lithium disilicate ceramics.

This in vitro study assessed the effectiveness of three cleaning protocols (air-water spray, 37% phosphoric acid, or Ivoclean) on lithium disilicate restorations' fatigue behavior after try-in paste application, compared to a clean condition. Lithium disilicate discs (IPS e.max CAD, Ivoclar) with Ø-= 12 mm and 1 mm thickness were prepared from prefabricated CAD-CAM blocks, polished, subjected to CAD-CAM milling topography simulation and crystallization. After, etching with 5% hydrofluoric acid and the application of try-in paste (Variolink try-in paste shade white; load of 2.5 N for 5 min) was performed. Discs that received try-in paste were divided into three groups according to the removal protocol: SPRAY - air-water spray for 30 s; HPO - active application of 37% phosphoric acid for 60 s; IVOC - application of Ivoclean for 20 s. Control group (CTRL group) did not receive the try-in paste application. Half of the specimens (n= 15) were tested in the baseline condition (24 h up to 7 days), and the others underwent 25,000 thermal cycles (5 - 55 °C) + 210 days of distilled water storage (37 °C). Additional specimens (n= 3) underwent monotonic testing (1 mm/min). Fatigue testing involved a cyclic fatigue approach (20 Hz, initial load = 100 N - 5000 cycles, step size = 50 N - 10,000 cycles) until a visible crack appeared. Fractographic and topographic analyses were performed. Fatigue data were statistically analyzed with two-way ANOVA, Kaplan-Meier log-rank (Mantel-Cox), and independent t-test (α= 0.05). In the baseline condition, the IVOC group resulted in a superior fatigue behavior compared to the CTRL and SPRAY groups, but similar to the HPO group. The HPO and SPRAY presented a similar fatigue behavior to the CTRL group. It was noticed a decrease in fatigue behavior after aging, which resulted in all the cleaning protocols leading to similar fatigue behavior compared to the CTRL group. On the SPRAY group surface, try-in pastes remnants were noticed. In summary, despite a detrimental impact at baseline conditions, all tested cleaning protocols seem proper to remove the try-in paste from the ceramic's surface in the long-term evaluation.

Influence of coloring techniques on the surface characteristics and color stability of a monolithic zirconia ceramic.

STATEMENT OF PROBLEM: The color of monolithic zirconia restorations is obtained by presintering or postsintering coloring techniques. However, studies on the differences in surface characteristics and their influence on color stability are lacking. PURPOSE: The purpose of this in vitro study was to evaluate the influence of shading and staining techniques for a zirconia ceramic on the surface characteristics and colorimetric parameters (color difference, translucency, and whiteness index) after exposure to coffee or red wine and then polishing. MATERIAL AND METHODS: Ceramic disks (N=30; Ø10×1mm) were allocated into 3 groups: preshaded-shaded by the manufacturer (IPS e.max ZirCAD MT, shade A2); manually shaded-unshaded zirconia (IPS e.max ZirCAD MT, bleaching shade-BL) colored by the brushing technique, before sintering; stained-unshaded zirconia (IPS e.max ZirCAD MT BL) colored by the staining technique, after sintering. Spectrophotometric color assessments ensured the same initial perceived color (Vita Classical A2) for specimens included in the study (∆E00<1.77 acceptability threshold). Surface characteristics were assessed by scanning electron microscopy and atomic force microscopy. The specimens were immersed in coffee (n=5) or red wine (n=5) for 12 and 24 days and subsequently polished. The data were statistically and descriptively analyzed for color differences (∆E00), translucency parameters (TP00), and whiteness indexes for dentistry (WID), considering acceptability and perceptibility thresholds. RESULTS: The shaded groups found an irregular ceramic surface with uniformly sized zirconia crystals. The stained group found a glass-covered smoother surface. Significant alterations in color parameters (∆E00, TP00, WID) were observed with immersion in pigmenting beverages (P<.001) both after 12 days, and after 24 days. The shaded specimens had greater color alterations after immersion but benefited from the polishing procedure, which reduced color differences below an acceptable threshold in comparison with the baseline. Stained specimens had lower color alterations after immersion, but the polishing protocol was detrimental as it whitened the ceramic by subsurface exposure. CONCLUSIONS: The coloring technique influences the surface characteristics of zirconia ceramic and also the color parameters after exposure to colored beverages and polishing.

Evaluation paste removal method and bond strength between resin cement and lithium disilicate ceramic: An in vitro study.

STATEMENT OF PROBLEM: After the use of evaluation paste, residue can remain on the bonding surface. However, how adhesion to lithium disilicate ceramic is affected is unclear. PURPOSE: The purpose of this in vitro study was to determine the effectiveness of lithium disilicate cleaning after contamination with an evaluation paste and before the application of a resin cement. MATERIAL AND METHODS: Rectangular lithium disilicate (IPS e.max CAD) specimens were obtained with a simulated milled surface, crystallized, etched with 5% hydrofluoric (HF) acid, and contaminated with an evaluation paste. The cleaning methods tested were air-water spray (SPRAY), 37% phosphoric acid (HPO), ultrasonic bath (ULT), cleaning paste (IVOC), and a conventional surface treatment (HF + silane-HF+SIL). The control (CTRL) group was not contaminated. After silane had been applied, resin cement cylinders were fabricated and light polymerized. Half of the cylinders (n=56) were tested for microshear bond strength at baseline (24 hours), and the other half after 210 days of water storage and 25 000 thermal cycles. Surface roughness, failure analysis, scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS) were performed. Statistical analysis was performed with the Kruskal-Wallis and Mann-Whitney tests for surface roughness and the 2-way ANOVA and Bonferroni post hoc tests for bond strength (α=.05). RESULTS: At baseline, only SPRAY did not restore the bond strength compared with CTRL. After aging, the bond strengths of SPRAY and IVOC were lower than of CTRL (P<.05); no significant difference was found between CTRL, HPO, ULT, and HF+SIL (P>.05). EDS demonstrated the presence of carbon in the SPRAY and ULT groups, probably remnants of the evaluation paste. SEM analysis identified such remnants in the SPRAY group only. CONCLUSIONS: For optimal bond strength between lithium disilicate and resin cement after evaluation paste use, cleaning the ceramic surface with 37% phosphoric acid, ultrasonic bath, or with hydrofluoric acid worked best.

Influence of height discrepancy between pulp chamber floor and crestal bone in the mechanical fatigue performance of endodontically-treated teeth restored with resin composite endocrowns.

OBJECTIVE: To explore and characterize the effect of the discrepancy between crestal bone height (CB) and pulp chamber floor (PCF) in the fatigue performance of endodontically-treated teeth rehabilitated with an endocrown restoration. MATERIALS AND METHODS: A total of 75 human molars free of defects, caries history or cracks were selected, then endodontically treated and randomly allocated into 5 groups (N = 15) according to the difference between PCF and CB, as follows: PCF 2 mm above, PCF 1 mm above, PCF leveled, PCF 1 mm below and PCF 2 mm below. Endocrown restorations were made with composite resin (Tetric N-Ceram, shade B3, Ivoclar) in 1.5 mm thickness and luted with a resin cement (Multilink N, Ivoclar) onto the dental elements. Monotonic testing was performed to define the fatigue parameters, and a cyclic fatigue test was used until failure of the assembly. The collected data were submitted to statistical survival analysis (Kaplan-Meier followed by Mantel-Cox and Weibull), fractographic analysis and finite element analysis (FEA) were performed as complementary analyzes. RESULTS: The PCF 2 mm below and PCF 1 mm below groups presented the best results regarding fatigue failure load (FFL) and number of cycles for failure (CFF) (p < 0.05), but presented no difference between each other (p > 0.05). The PCF leveled and PCF 1 mm above groups presented no statistical difference between them (p > 0.05), but performed better than the PCF 2 mm above group (p < 0.05). The rate of favorable failures of PCF 2 mm above, PCF 1 mm above, PCF leveled, PCF 1 mm below and PCF 2 mm below groups were 91.7%, 100%, 75%, 66.7% and 41.7%, respectively. FEA showed different stress magnitudes according to the pulp-chamber design. CONCLUSION: The insertion level of the dental element to be rehabilitated with an endocrown interferes in the mechanical fatigue performance of the set. The discrepancy between the CB height and the PCF has a direct effect, where the higher the PCF in relation to the CB, the greater the risk of mechanical failure of the restored dental element.

Pigmentation techniques of a 4YSZ: Effect on the fatigue mechanical behavior of a 4YSZ adhesively luted onto dentin analog.

OBJECTIVE: To characterize the effect of pigmentation techniques on the fatigue behavior of a 4YSZ ceramic adhesively luted onto dentin analog (glass fiber-reinforced epoxy resin). METHODS: 4YSZ ceramic discs (Ø= 10 mm, 1 mm thickness) were allocated into 5 groups: Ctrl - unshaded (IPS e.max ZirCAD MT BL); Manuf - shaded by the manufacturer (IPS e.max ZirCAD MT A2); Brush - unshaded pigmented, pre-sintering, using a brush; Stain - unshaded pigmented, post-sintering, during glaze application; Brush+Stain - combination of both techniques. Color assessments ensured the same perceived color (Vita Classical A2). Dentin analog discs (Ø= 10 mm, 2.5 mm thickness) were obtained, paired with the 4YSZ discs, and adhesively luted using a resin cement. Cyclic fatigue testing (n = 15) was run (20 Hz; 10,000 cycles/step, initial load 200 N; step-size 100 N up to 700 N; then 50 N until specimen failure). Fractographic, roughness and topography analyses were performed. RESULTS: No statistical (p > 0.05) detrimental influence were observed for fatigue outcomes (Ctrl = Manuf = Brush = Stain = Brush+Stain). However, the Brush+Stain technique induced inferior statistical (p < 0.05) fatigue performance compared to Stain. All failures were radial cracks with origin at the ceramic intaglio surface. The staining technique triggered statistically higher roughness (p < 0.05). Uniformly sized zirconia crystals were seen in the Ctrl, Manuf and Brush groups, and a smooth vitreous surface with encrusted pigments in the Stain and Brush+Stain groups. SIGNIFICANCE: Pigmentation techniques (Vita Classical A2 shade) have no detrimental effect on the mechanical fatigue properties of 4YSZ ceramic adhesively luted onto dentin analog.

Effect of pigmentation techniques on the fatigue mechanical behavior of a translucent zirconia for monolithic restorations.

This study aims to characterize the effect of pre- and/or post-sintering pigmentation techniques on the fatigue behavior of a 4YSZ ceramic (4 mol% yttrium stabilized zirconia). First, 4YSZ ceramic discs (IPS e.max ZirCAD, 15 mm diameter, and 1.2 mm thickness) were obtained and allocated according to the 'pigmentation technique' factor into 5 groups: Ctrl - unshaded ceramic disc (IPS e.max ZirCAD BL); Manuf - ceramic discs shaded by the manufacturer at block formation (IPS e.max ZirCAD MT A2); Brush - unshaded ceramic disc pigmented in the pre-sintered stage using a brush; Stain - unshaded ceramic disc pigmented in the post-sintering stage using a stain glaze (shade A2); Brush + Stain - combination of Brush and Stain techniques. The specimens were sintered and analyzed by a spectrophotometer (VITA Easyshade) for color differences (ΔE00 calculated according to CIEDE, 2000) to ensure that they present the same perceived color (ΔE00 ≤ 1.77, acceptability threshold). The specimens (n = 15) were submitted to biaxial flexural fatigue testing using a cyclic fatigue method (frequency of 20 Hz; 10,000 cycles per step; initial stress of 200 MPa; and step-size of 25 MPa) until specimen fracture. Fatigue strength (FS) and number of cycles until failure (CFF) were recorded with statistical purposes. Fractographic, complementary topography, elemental and roughness analyses were performed. The Ctrl shown the highest FS, CFF, and survival rates compared to the other conditions (p < 0.05), being only statistically similar to Brush. Stain showed the lowest FS, CFF and survival rates (p < 0.05). The Manuf and Brush + Stain shown intermediary performance. In regards of Weibull moduli, Brush shown the lowest values (lowest structural reliability), for both FS and CFF, being only statistically similar to Manuf. Topography analysis shown a uniform size of zirconia crystals in Ctrl, Manuf and Brush. In addition, a smooth glassy surface with some spots of impregnated pigment was observed in the groups where glaze was applied (Stain and Brush + Stain). This finding was corroborated by elemental analysis. Despite that, Stain and Brush + Stain presented the roughest surface (p < 0.05). In summary, the pigmentation techniques used to provide a Vita classical A2 color shade have a detrimental effect on the mechanical fatigue properties of a 4YSZ ceramic, except for the technique performed with the brush in the block pre-sintering stage. Despite this, the brush technique presents great variability in mechanical performance, resulting in lower structural reliability.