Impact of Thermally Reducing Temperature on Graphene Oxide Thin Films and Microsupercapacitor Performance.

In this work, a thermally reduced graphene oxide (TRGO) thin film on microscopic glass was prepared using spray coating and atmospheric pressure chemical vapour deposition. The structure of TRGO was analysed using X-ray diffraction (XRD) spectroscopy, scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy (EDS), Fourier transform infrared (FTIR) spectroscopy, and ultraviolet-visible spectroscopy (UV-Vis) suggesting a decrease in oxygen functional groups (OFGs), leading to the restacking, change in colour, and transparency of the graphene sheets. Raman spectrum deconvolution detailed the film's parameters, such as the crystallite size, degree of defect, degree of amorphousness, and type of defect. The electrochemical performance of the microsupercapacitor (µ-SC) showed a rectangular cyclic voltammetry shape, which was maintained at a high scan rate, revealing phenomenal electric double-layer capacitor (EDLC) behaviour. The power law and Trasatti's analysis indicated that low-temperature TRGO µ-SC is dominated by diffusion-controlled behaviour, while higher temperature TRGO µ-SC is dominated by surface-controlled behaviour.

Novel Thermally Reduced Graphene Oxide Microsupercapacitor Fabricated via Mask-Free AxiDraw Direct Writing.

We demonstrate a simple method to fabricate all solid state, thermally reduced graphene oxide (TRGO) microsupercapacitors (µ-SCs) prepared using the atmospheric pressure chemical vapor deposition (APCVD) and a mask-free axiDraw sketching apparatus. The Fourier transform infrared spectroscopy (FTIR) shows the extermination of oxygen functional groups as the reducing temperature (RT) increases, while the Raman shows the presence of the defect and graphitic peaks. The electrochemical performance of the µ-SCs showed cyclic voltammetry (CV) potential window of 0-0.8 V at various scan rates of 5-1000 mVs-1 with a rectangular shape, depicting characteristics of electric double layer capacitor (EDLC) behavior. The µ-SC with 14 cm-2 (number of digits per unit area) showed a 46% increment in capacitance from that of 6 cm-2, which is also higher than the µ-SCs with 22 and 26 cm-2. The TRGO-500 exhibits volumetric energy and power density of 14.61 mW h cm-3 and 142.67 mW cm-3, respectively. The electrochemical impedance spectroscopy (EIS) showed the decrease in the equivalent series resistance (ESR) as a function of RT due to reduction of the resistive functional groups present in the sample. Bode plot showed a phase angel of -85° for the TRGO-500 µ-SC device. The electrochemical performance of the µ-SC devices can be tuned by varying the RT, number of digits per unity area, and connection configuration (parallel or series).