Plate-type hollow black TiO2 (HL/BT) with a high NIR reflectance was fabricated for the first time as a LiDAR-detectable black material. A TiO2 layer was formed on commercial-grade glass by using the sol-gel method to obtain a plate-type structure. The glass template was then etched with hydrofluoric acid to form a hollow structure, and blackness was further achieved through NaBH4 reduction, which altered the oxidation state of TiO2 to black TixO2x-1 or Ti4+ to Ti3+ and Ti2+. The blackness of the HL/BT material was maintained by a novel approach that involved etching prior to reduction. The thickness of the TiO2 layer was controlled to maximize the NIR reflectance when applied as paint. The HL/BT material with a thickness of 140 nm (HL/BT140) showed a blackness (L*) of 13.3 and high NIR reflectance of 23.6% at a wavelength of 905 nm. This is attributed to the effective light reflection at the interface created by the TiO2 layer and the hollow structure. Plate-type HL/BT140 provides excellent spreadability, durability, and thermal stability in practical paint applications compared with sphere-type materials due to the higher contacting area to the applied surface, making it suitable for use as a LiDAR-detectable inorganic black pigment in autonomous environments.
RESUMO
The use of plate-like materials to induce a percolation gel-like effect in electrorheological (ER) fluids is sparsely documented. Hence, we dispersed plate-like materials, namely natural mica, synthetic mica, and glass, as well as their pulverized particles, in various concentrations in silicone oil to form ER fluids. Subsequently, the rheological properties of the fluids were evaluated and compared to identify the threshold concentration for percolating a gel-like state. The shear stress and viscoelastic moduli under zero-field conditions confirmed that plate-like materials can be used to induce percolation gel-like effects in ER fluids. This is because of the high aspect ratio of the materials, which enhances their physical stability. In practical ER investigations, ER fluids based on synthetic mica (30.0 wt%) showed the highest yield stress of 516.2 Pa under an electric field strength of 3.0 kV mm-1. This was attributed to the formation of large-cluster networks and additional polarization induced by the ions. This study provides a practical approach for developing a new type of gel-like ER fluid.