Monazite-Type SmPO4 as Potential Nuclear Waste Form: Insights into Radiation Effects from Ion-Beam Irradiation and Atomistic Simulations.

Single-phase monazite-type ceramics are considered as potential host matrices for the conditioning of separated plutonium and minor actinides. Sm-orthophosphates were synthesised and their behaviour under irradiation was investigated with respect to their long-term performance in the repository environment. Sintered SmPO4 pellets and thin lamellae were irradiated with 1, 3.5, and 7 MeV Au ions, up to fluences of 5.1 × 1014 ions cm-2 to simulate ballistic effects of recoiling nuclei resulting from α-decay of incorporated actinides. Threshold displacement energies for monazite-type SmPO4 subsequently used in SRIM/TRIM simulations were derived from atomistic simulations. Raman spectra obtained from irradiated lamellae revealed vast amorphisation at the highest fluence used, although local annealing effects were observed. The broadened, but still discernible, band of the symmetrical stretching vibration in SmPO4 and the negligible increase in P-O bond lengths suggest that amorphisation of monazite is mainly due to a breaking of Ln-O bonds. PO4 groups show structural disorder in the local environment but seem to behave as tight units. Annealing effects observed during the irradiation experiment and the distinctively lower dose rates incurred in actinide bearing waste forms and potential α-radiation-induced annealing effects indicate that SmPO4-based waste forms have a high potential for withstanding amorphisation.

Influence of extreme conditions on the formation and structures of caesium uranium(VI) arsenates.

Four new uranyl arsenates, Cs2[(UO2)(As2O7)] (1), α-Cs[(UO2)(HAs2O7)] (2), ß-Cs[(UO2)(HAs2O7)] (3), Cs[(UO2)(HAs2O7)]·0.17H2O (4), were synthesized by high-temperature/high pressure (HT/HP) reactions at 900 °C and 3 GPa. These phases were subsequently characterised structurally as well as chemically. We demonstrated that compound 1 can also be obtained at ambient pressure. Compounds 1, 2, and 4 are based on two-dimensional (2D) anionic layers with two different topological types. The layers possess a similar composition, [(UO2)(As2O7)](2-) in 1 and [(UO2)(HAs2O7)](-) in 2 and 4. However, the presence of hydrogen in 2 and 4 leads to a change in coordination modes of the pyroarsenate groups. There are additional 0.17 H2O molecules per formula unit in 4, which cause slight distortions of the layers in 4. All these layers can be simplified to a common net, which is typical of autunite-like layered compounds. Compound 3 is a polymorph of compound 2, but the structural arrangements in these two are significantly different. The structure of 3 is based upon a three-dimensional (3D) framework, in which UO7 is coordinated by arsenate groups in order to form uranyl anion sheets, and UO6 is located within the interlayers. Bond valance analysis proved the presence of OH(-) groups in compounds 2, 3, and 4, respectively, and water molecules in 4. The Raman analyses enabled the study of the local environments of the arsenate and the uranyl groups within the investigated phases, respectively. It turned out that the applied HT/HP synthesis method strongly affects the crystal chemistry as well as the observed structural features of all obtained compounds.

Chemical and structural evolution in the Th-SeO3(2-)/SeO4(2-) system: from simple selenites to cluster-based selenate compounds.

While extensive success has been gained in the structural chemistry of the U-Se system, the synthesis and characterization of Th-based Se structures are widely unexplored. Here, four new Th-Se compounds, α-Th(SeO3)2, ß-Th(SeO3)2, Th(Se2O5)2, and Th3O2(OH)2(SeO4)3, have been obtained from mild hydrothermal or low-temperature (180-220 °C) flux conditions and were subsequently structurally and spectroscopically characterized. The crystal structures of α-Th(SeO3)2 and ß-Th(SeO3)2 are based on ThO8 and SeO3 polyhedra, respectively, featuring a three-dimensional (3D) network with selenite anions filling in the Th channels along the a axis. Th(Se2O5)2 is a 3D framework composed of isolated ThO8 polyhedra interconnected by [Se2O5](2-) dimers. Th3O2(OH)2(SeO4)3 is also a 3D framework constructed by octahedral hexathorium clusters [Th6(µ3-O)4(µ3-OH)4](12+), which are interlinked by selenate groups SeO4(2-). The positions of the vibrational modes associated with both Se(IV)O3(2-) and Se(VI)O4(2-) units, respectively, were determined for four compounds, and the Raman spectra of α- and ß-Th(SeO3)2 are compared and discussed in detail.

Performance of DFT+U method for prediction of structural and thermodynamic parameters of monazite-type ceramics.

We performed a density functional theory (DFT) study of the monazite-type ceramics using DFT+U method, where the Hubbard U parameters are derived ab initio, with the main goal in testing the predictive power of this computational method for modeling of f-electron materials that are of interest in nuclear waste management. We show that DFT+U approach with PBEsol as the exchange-correlation functional significantly improves description of structures and thermodynamic parameters of lanthanide-bearing oxides and monazites over commonly used standard DFT (PBE) approach. We found that it is essential to use the Hubbard U parameter derived for a given element and a given structure to reproduce the structural parameters of the measured materials. We obtained exceptionally good description of the structural parameters with U parameter derived using the linear response approach of Cococcioni and de Gironcoli (Phys. Rev. B 2005, 71, 035105). This shows that affordable methods, such as DFT+U with a clever choice of exchange-correlation functional and the Hubbard U parameter can lead to a good description of f-electron materials.

High-temperature phase transitions, spectroscopic properties, and dimensionality reduction in rubidium thorium molybdate family.

Four new rubidium thorium molybdates have been synthesized by high-temperature solid-state reactions. The crystal structures of Rb8Th(MoO4)6, Rb2Th(MoO4)3, Rb4Th(MoO4)4, and Rb4Th5(MoO4)12 were determined using single-crystal X-ray diffraction. All these compounds construct from MoO4 tetrahedra and ThO8 square antiprisms. The studied compounds adopt the whole range of possible structure dimensionalities from zero-dimensional (0D) to three-dimensional (3D): finite clusters, chains, sheets, and frameworks. Rb8Th(MoO4)6 crystallizes in 0D containing clusters of [Th(MoO4)6](8-). The crystal structure of Rb2Th(MoO4)3 is based upon one-dimensional chains with configuration units of [Th(MoO4)3](2-). Two-dimensional sheets occur in compound Rb4Th(MoO4)4, and a 3D framework with channels formed by thorium and molybdate polyhedra has been observed in Rb4Th5(MoO4)12. The Raman and IR spectroscopic properties of these compounds are reported. Temperature-depended phase transition effects were observed in Rb2Th(MoO4)3 and Rb4Th(MoO4)4 using thermogravimetry-differential scanning calorimetry analysis and high-temperature powder diffraction methods.