Degree of conversion and interfacial adaptation of touch-cure resin cement polymerized by self-curing or dual-curing with reduced light.

OBJECTIVES: The first aim of this study was to determine whether there is a difference in degree of conversion (DC) of touch-cure cements polymerized by self-curing with adhesive or dual-curing under reduced light. The second aim was to compare interfacial adaptation of zirconia restoration cemented using touch-cure cements self-cured or dual-cured by reduced light. METHODS: The DC of touch-cure resin cements with adhesive was measured continuously using Fourier transform infrared spectrometry. Experimental groups differed depending on touch-cure cement. Each group had three subgroups of polymerization method. For subgroup 1, the DC was measured by self-curing. For subgroups 2 and 3, the DCs were measured by dual-curing with reduced light penetrating 3 mm and 1 mm zirconia blocks, respectively. For interfacial adaptation evaluation, Class I cavity was prepared on an extracted third molar, and zirconia restoration was fabricated. The restoration was cemented using the same cement. Groups and subgroups for interfacial adaptation were the same as those of the DC measurement. After thermo-cycling, interfacial adaptation at the tooth-restoration interface was evaluated using swept-source optical coherence tomography imaging. RESULTS: The DC of touch-cure cement differed depending on the measurement time, resin cement, and polymerization method (p < 0.05). Interfacial adaptation was different depending on the resin cement and polymerization method (p < 0.05). CONCLUSION: For touch-cure cement, light-curing with higher irradiance presented a higher DC and superior interfacial adaptation than light-curing with lower irradiance or self-curing. CLINICAL RELEVANCE: Although some adhesives accelerate the self-curing of touch-cure cement, light-curing for touch-cure cement is necessary for zirconia cementation.

Comparative analysis of microbiome in coronal and root caries.

BACKGROUND: The global rise in the elderly population has increased the prevalence of root caries. Streptococcus mutans, Lactobacilli and Actinomyces are considered the primary pathogens of dental caries in culture-based studies. This study aimed to investigate bacterial profiles in coronal and root caries lesions and determine the association of specific bacterial genera at each site. METHODS: Dentine samples from carious lesions were collected from 22 extracted teeth using an excavator. Microbial DNA was extracted from the samples using a protocol developed for this study. 16S rRNA gene amplicon sequencing was employed for microbial analysis. PCR amplification targeted the V3-V4 region of the bacterial 16S rRNA, and the amplicon sequencing used an Illumina MiSeq system (2 × 300 bp paired-end reads). Statistical analysis was performed by the Phyloseq and DESeq2 packages in R. RESULTS: In coronal caries, Olsenella, Lactobacillus and Prevotella were the most prevalent genera, comprising approximately 70% of the microbiome community. In the root caries, however, although Olsenella, Prevotella and Lactobacillus remained the dominant genera, they accounted for only half of the microbiome community. This study identified significant differences in alpha diversity indices between the coronal and root caries. LEfSE analysis revealed several unique genera in each caries lesion. CONCLUSION: The microbiome of root caries lesions was richer and more complex than the coronal caries microbiota. The results suggest that lesion-related variations in the oral microflora may be detected in carious dentine.

Analysis of cariogenic biofilms by using a swept-source optical coherence tomography in vitro.

OBJECTIVE: The objective was to measure the thickness of Streptococcus mutans (S. mutans) biofilms forming in an oral biofilm reactor (OBR) by using a noninvasive swept-source optical coherence tomography (SS-OCT) system at every 4 h time interval until 20 h and analyze the correlations with the amounts of biofilms. METHODS: S. mutans biofilms were formed on square-shaped bovine enamel blocks inside an OBR. Biofilms were analyzed at every 4 h stage (4 h, 8 h, 12 h, 16 h and 20 h) using a SS-OCT system and a laser scanning confocal microscope (LSCM). The amounts of biofilms were measured at each stage by separating the water insoluble glucan (WIG) and bacterial cells. Co-relationships between the SS-OCT measured biofilm thickness and the amounts of adhered biofilms were analyzed. RESULTS: The thickness of biofilms detected on SS-OCT images at 4 h stage was 0.059 ± 0.029 (Av ± SD) mm which increased time-dependently in a linear fashion after 8 h stage and reached to 0.435 ± 0.159 mm at 20 h stage and the correlation coefficient was about 0.89. The amounts of biofilms; bacterial optical density (OD) and WIG concentration increased time-dependently were 0.035 ± 0.008 / mm2 and 10.328 ± 2.492 µg/ mm2 respectively at 20 h stage. Correlation coefficients of 0.66 between 'the amounts of bacteria' and 'biofilm thickness on OCT' and 0.67 between 'the amounts of WIG' and 'biofilm thickness on OCT' were obtained, suggesting that there was a relatively positive correlation between them. CONCLUSION: The SS-OCT can be a useful tool to measure time-dependent growth of biofilms. Further studies are needed in order to assess biofilms using SS-OCT more accurately.

Enhancement of mineral density and mechanical properties in root caries treated with silver diammine fluoride and glass ionomer cement, with emphasis on silver ion distribution.

OBJECTIVES: This study aimed to measure the distribution of silver ion (Ag+), mineral recovery, and nanohardness in carious lesions and comprehensively evaluate the degree of dentin restoration. METHODS: Sixty human teeth with root caries were randomly assigned to the control, silver diammine fluoride (SDF) [Safo], and SDF+Glass ionomer cement (GIC) treatment [Safo+Fuji] groups. Micro-computed tomography (micro-CT) was performed at five time points for each sample before/after treatment to evaluate mineral density within and around carious lesions. Three months following treatment, 12 samples were selected for synchrotron radiation X-ray fluorescence analysis to evaluate Ag+ distribution, while 15 samples were selected for nanoindentation. Data were analyzed using Dunnett's T3 test for micro-CT and Wilcoxon rank sum test with Bonferroni correction (p = 0.017) for nanoindentation. The correlation between hardness and mineral change was analyzed using the Spearman rank correlation coefficient. RESULTS: The Safo and Safo+Fuji groups showed significantly higher mineral recovery rates than did the control group (p < 0.001). In the Safo group, Ag+ accumulated in the deeper layers rather than the superficial layer of caries. In the Safo+Fuji group, Ag+ was found evenly distributed throughout caries, with only a few Ag+ detected in the GIC layer. Hardness in the Safo+Fuji group was significantly higher compared with the Safo group at depths in the range of 10-50 µm. CONCLUSION: In the presence of GICs, SDF exhibited high remineralization capacity when diffusing throughout carious lesions over time. Combined treatment with SDF and GIC could strengthen root dentin even in the presence of caries. CLINICAL SIGNIFICANCE: We found that combination treatment with SDF and GIC could increase mineral density in caries and improve the hardness of the tooth structure compared with fluoride-based agents alone. These findings might pave the way for future clinical trials to determine the therapeutic potential of nanotechnology-based restorative materials.

Effect of water glass treatment for zirconia and silane coupling on bond strength of resin cement.

OBJECTIVE: To evaluate the ability of the water glass treatment to penetrate zirconia and improve the bond strength of resin cement. MATERIAL AND METHODS: Water glass was applied to zirconia specimens, which were then sintered. The specimens were divided into water-glass-treated and untreated zirconia (control) groups. The surface properties of the water-glass-treated specimens were evaluated using surface roughness and electron probe micro-analyser (EPMA) analysis. A resin cement was used to evaluate the tensile bond strength, with2 and without a silane-containing primer. After 24 h in water storage at 37 °C and thermal cycling, the bond strengths were statistically evaluated with t-test, and the fracture surfaces were observed using SEM. RESULTS: The water glass treatment slightly increased the surface roughness of the zirconia specimens, and the EPMA analysis detected the water glass penetration to be 50 µm below the zirconia surface. The application of primer improved the tensile bond strength in all groups. After 24 h, the water-glass-treated zirconia exhibited a tensile strength of 24.8 ± 5.5 MPa, which was significantly higher than that of the control zirconia (17.6 ± 3.5 MPa) (p < 0.05). After thermal cycling, the water-glass-treated zirconia showed significantly higher tensile strength than the control zirconia. The fracture surface morphology was mainly an adhesive pattern, whereas resin cement residue was occasionally detected on the water-glass-treated zirconia surfaces. CONCLUSION: The water glass treatment resulted in the formation of a stable silica phase on the zirconia surface. This process enabled silane coupling to the zirconia and improved the adhesion of the resin cement.

Influence of resin-coating techniques on the marginal adaptation and the bond strengths of CAD/CAM-fabricated hybrid ceramic inlays.

This study aimed to evaluate the effects of different resin-coating technique strategies and dual-cure resin luting materials on proximal marginal adaptation and the microtensile bond strengths (µTBSs) of CAD/CAM hybrid ceramic inlays. Extracted human molars were classified into four groups, depending on the coating technique: No coating (None), single coating (1-coating), double coating (2-coating), and flowable resin-coating (Combination). The inlays were bonded with one of the three materials: Panavia V5 (V5), Rely X Ultimate (RXU), and Calibra Ceram (CC). The differences with regard to adaptation were not significant. In the case of µTBS data for V5, no significant differences were observed, whereas for RXU, µTBS values for Combination statistically exceeded those for None and 1-coating. For CC, µTBS values for Combination statistically exceeded those for None, 1-coating, and 2-coating. The coating techniques did not influence the adaptation but influenced the bond strength, and Combination performed the best.

Evaluation of a hydroxyapatite-crosslinked fish gelatin membranes.

Background/purpose: Porcine collagen is widely used in regenerative therapies to generate membranes for bone augmentation. However, porcine or bovine gelatin or collagen is often not appropriate for patients with creed and religious beliefs or for allergic reasons. In this study, we evaluated the potential of fish gelatin to generate membranes. Materials and methods: Fish gelatin and hydroxyapatite (HAp) were used at three different ratios (2:0, 2:1, 2:1.5, and 2:2) to prepare gelatin-hydroxyapatite (G-HAp) membranes via freeze-drying and heat-crosslinking. The surface morphology and cell attachment of G-HAp membranes were observed using scanning electron microscopy and confocal laser microscopy. G-HAp membrane was placed at the bottom of a well plate, and MC3T3-E1 cells were seeded on it. Cell viability and cytotoxicity were tested after 1 and 3 days of culture. Alkaline phosphatase (ALP) and alizarin red staining was performed at 10 and 21 days, respectively. Results: Viability of cells on G-HAp membrane with the gelatin:HAp ratio of 2:1.5 was significantly higher than that on membranes with other gelatin:HAp ratios. ALP and alizarin red staining showed that ALP-positive areas and calcium deposition were the highest on G-HAp membrane with the gelatin:HAp ratio of 2:1. These membranes showed negligible cytotoxicity. Conclusion: Fish-derived G-HAp membranes have the potential to promote osteogenic differentiation of MC3T3-E1 cells with negligible cytotoxicity.

Comparative bonding performance of coronal dentin disks and CAD/CAM resin composite disks for biological restoration: The impact of resin-coating technique.

This study evaluated the bonding performance of coronal dentin disks, designed for biological restoration, and CAD/CAM resin composite disks when bonded to flat dentin surfaces using dual-cure resin cements, with and without a resin-coating (RC) technique. Three distinct groups were established within the non-RC group, each using one of the two types of resin cements in a self-adhesive mode: one-step self-etch adhesive (1-SEA) without light-cure, 1-SEA with light-cure, and a separate group using an alternate cement. Within the RC group, a subgroup was established for each cement. The microtensile bond strength (µTBS) of the disk-dentin beam was tested after 0 and 10,000 thermocycles in a 5°C/55°C. No significant µTBS difference was observed among the non-RC groups. However, when using RC, the µTBSs of coronal dentin disks significantly exceeded those of CAD/CAM resin composite disks. Thermocycle aging did not affect µTBS in any of the bonding methods, except in self-adhesive mode.

Effect of borate, fluoride and strontium ions on biomimetic nucleation of calcium phosphate studied using solid-state nuclear magnetic resonance and X-ray diffraction.

OBJECTIVES: Apatite minerals can have various anions and cations in their crystal structure in addition to phosphate ion (PO4³â») and calcium ion (Ca2+). The aim of this study is to investigate effects of the borate, fluoride and strontium ions on biomimetic nucleation of calcium phosphate. METHODS: Nano-crystalline hydroxyapatite (H-Ap) was obtained from a supersaturated buffered solution containing 4.12 mM HPO42- and 5.88 mM Ca2+ (H-Ap). Four additives were used in solid solution methods: (i) 0.588 mM F- (F-Ap), (ii) 5.88 mM Sr2+ (Sr-Ap), (iii) 4.12 mM BO33- (BO3-Ap), and (iv) a surface pre-reacted glass ionomer (S-PRG) filler eluate that contained 0.17 mM Sr2+, 0.588 mM F-, 11.1 mM BO33-- (SPRG-Ap). Apatite crystallization was investigated using a solid-state magic-angle spinning NMR spectroscopy and X-ray diffraction (XRD) with the Rietveld analysis. RESULTS: A 2D 1H-31P heteronuclear-correlation NMR showed F- ion incorporation in the apatite structure of the F-Ap and SPRG-Ap. The peaks on the 31P axis of the F-Ap, Sr-Ap, and BO3-Ap were different from that of the H-Ap, and the full width at half maximum increased in the following order: H-Ap∼F-Ap∼BO3-Ap< SPRG-Ap< Sr-Ap, suggesting the incorporation of the F-, Sr2+ and BO33-. The incorporation of F and BO3 was further confirmed by 19F and 11B NMR. The XRD revealed that Sr2+ was preferentially incorporated into the CaII site. SIGNIFICANCE: The F-, Sr2+ and BO33-ions might be involved in modifying the crystallization of apatite precipitation, producing a variety of apatite. S-PRG filler that release these ions may have an effect on remineralization, i.e., the reformation of apatite lost due to caries.

Influence of surface pre-reacted glass-ionomer (S-PRG) filler eluate on collagen morphology, remineralization, and ultimate tensile strength of demineralized dentin.

OBJECTIVE: To evaluate the effect of ions released from surface pre-reacted glass-ionomer (S-PRG) filler on collagen morphology, remineralization, and ultimate tensile strength (UTS) of demineralized dentin. MATERIALS AND METHODS: Bovine incisor root dentins were demineralized with EDTA and divided into three treatment groups: 1) water (control); 2) S-PRG filler eluate; 3) 125 ppm sodium fluoride (NaF). After a 3-min treatment, the specimens were stored in simulated body fluid (SBF) for 3 months. Collagen morphology and remineralization were assessed using transmission electron microscopy (TEM), scanning electron microscopy (SEM), and Fourier-transform infrared spectroscopy (FTIR). Additionally, ultimate tensile strength (UTS) was measured. RESULTS: TEM and SEM demonstrated that S-PRG induced more effective remineralization compared to NaF, while the control group exhibited faint mineral deposition with collagen degradation. S-PRG displayed the most homogenous mineral deposition in collagen fibrils, along with closure of interfibrillar spaces. Extensive mineral precipitation was observed within dentinal tubules in the S-PRG group. In addition, S-PRG filler eluate demonstrated significantly higher phosphate-to-amide ratio and UTS compared to NaF and control groups (p < 0.05). CONCLUSIONS: Ion released from S-PRG filler positively influenced collagen morphology, remineralization, and ultimate tensile strength of demineralized dentin. CLINICAL SIGNIFICANCE: S-PRG filler enhances remineralization and improve the biomechanics of demineralized dentin.

Molecular Epidemiology of Respiratory Syncytial Virus during 2019-2022 and Surviving Genotypes after the COVID-19 Pandemic in Japan.

To evaluate the changes in respiratory syncytial virus (RSV) collected between 2019 and 2022, we analyzed RSV-A and RSV-B strains from various prefectures in Japan before and after the COVID-19 pandemic. RT-PCR-positive samples collected from children with rapid test positivity at outpatient clinics in 11 prefectures in Japan were sequenced for the ectodomain of the G gene to determine the genotype. Time-aware phylogeographic analyses were performed using the second hypervariable region (HVR) of the G gene from 2012 to 2022. Of 967 samples, 739 (76.4%) were found to be RSV-positive using RT-PCR. RSV peaked in September 2019 but was not detected in 2020, except in Okinawa. Nationwide epidemics occurred with peaks in July 2021 and 2022. The genotype remained the same, ON1 for RSV-A and BA9 for RSV-B during 2019-2022. Phylogeographic analysis of HVR revealed that at least seven clusters of RSV-A had circulated previously but decreased to two clusters after the pandemic, whereas RSV-B had a single monophyletic cluster over the 10 years. Both RSV-A and RSV-B were transferred from Okinawa into other prefectures after the pandemic. The RSV epidemic was suppressed due to pandemic restrictions; however, pre-pandemic genotypes spread nationwide after the pandemic.

Effect of Attenuated Light Through Translucent Zirconia on the Interfacial Adaptation and Polymerization of Resin Cements.

PURPOSE: The first objective was to determine if dual-curing of resin cement with reduced light could affect interfacial adaptations of zirconia restoration. The second objective was to examine whether cement type and pretreatment method of universal adhesive affected interfacial adaptation. The final objective was to compare the polymerization degree of cement under different reduced-light conditions. MATERIALS AND METHODS: Inlay cavities were prepared on extracted third molars. Translucent zirconia restorations were milled using Katana UTML (Kuraray Noritake) in three groups with restoration thicknesses of 1, 2, and 3 mm, respectively. Each group had three subgroups using different cementation methods. For subgroup 1, restorations were cemented with self-adhesive cement. For subgroup 2, universal adhesive was applied and light cured. After the restoration was seated with conventional resin cement, light curing was performed. For subgroup 3, after adhesive was applied, the restoration was seated with conventional resin cement. Light curing was performed for the adhesive and cement simultaneously. After thermocycling, interfacial adaptation at the restoration-tooth interface was investigated using swept-source optical coherence tomography imaging. Finally, polymerization shrinkage of the cement was measured using a linometer and compared under the conditions of different zirconia thicknesses and light-curing durations. RESULTS: Interfacial adaptation varied signficantly depending on the zirconia thickness, pretreatment, polymerization mode and cements used (p < 0.05). The effects of the adhesive and polymerization shrinkage differed signficantly, depending on the reduced light under the zirconia (p < 0.05). CONCLUSION: Lower curing-light irradiance may lead to inferior adaptation and lower polymerization of the cement. Polymerization of resin cement can differ depending on the light irradiance and exposure duration.

In vitro performance of an autocured universal adhesive system in bonding to dentin.

BACKGROUND: The successful integration of resin-based dental adhesives significantly impacts restorative dentistry, providing efficient and aesthetically pleasing caries treatments. Among various adhesives, one-step self-etching adhesives (1-SEAs) have gained popularity due to their simplicity and short application time. However, concerns have been raised regarding their bonding performance and marginal adaptation characteristics, which differ from two-step self-etching adhesives (2-SEAs) and three-step etch-and-rinse adhesives. Additionally, light-cured bonding materials may encounter challenges in deep cavities and inaccessible areas, necessitating extended light irradiation time. Autocured bonding materials are a potential solution, but limited comparative studies have been conducted on their performance. METHODS: In this in vitro study, we evaluated a new autocured universal bonding material (Bondmer Lightless 2) and compared the results with recent light-cured bonding materials. Microshear bond strength (µSBS) tests were performed on 25 human molars using five different combinations of adhesives and composite resins: Bondmer Lightless 2 with Estelite Bulk Fill Flow (BE group), Bondmer Lightless 2 with a prototype composite resin (BO group), Prime&Bond Universal with SDR flow + (PS group), Scotchbond Universal with Filtek Bulk Fill (SF group), and G-Premio Bond with Gracefil BulkFlo (GG group). The bond strengths and failure modes were assessed using a universal testing machine and scanning electron microscope (SEM), respectively. Marginal adaptation was evaluated using swept-source optical coherence tomography (SS-OCT) and confocal laser scanning microscopy (CLSM) on 40 sound bovine maxillary incisors. RESULTS: The µSBS test showed no significant differences in bond strength among the tested groups. Most failure modes were observed at the bond interface between the adhesive and the dentin. The autocured bonding material demonstrated significantly higher marginal adaptation (SI%) than PS, SF, and GG. The CLSM images corresponded with gaps observed in the SS-OCT images, indicating improved marginal sealing in the autocured group. CONCLUSIONS: The new autocured universal bonding material exhibited comparable bond strength to a conventional light-cured material while demonstrating a superior marginal adaptation level. This finding suggested that the autocured material could be a valuable alternative, especially when extended light irradiation would pose a challenge. Further clinical studies would be warranted to evaluate the performance of the autocured bonding material in actual restorative dental practice.

The Effect of Bonding Strategy and Aging on Adhesion to Primary Enamel: An In-Vitro Study.

PURPOSE: Resin composites are commonly used in pediatric dentistry, but there is limited evidence on adhesion to primary teeth, especially primary enamel. In this study, three bonding strategies were assessed - one-step self-etch (1-SE), two-step self-etch (2-SE), and three-step etch-and-rinse (3-ER) - by measuring the immediate and aged microshear bond strength (µSBS) to sound primary enamel. MATERIALS AND METHODS: 120 extracted human primary molars with sound buccal surfaces were used for µSBS testing. Six adhesive protocols (two per bonding strategy) were selected and µSBS was measured either after 24 h or 10,000 thermal cycles (n = 10). Confocal laser scanning microscopy (CLSM) and scanning electron microscopy (SEM) were used to determine failure modes. Furthermore, 18 primary molars were etched using the different adhesive protocols (n = 3) for the measurement of surface roughness (Sa) using CLSM and morphological analysis using SEM. RESULTS: After 24 h, there was no significant difference in µSBS between 1-SE and 2-SE strategies (p = 0.96), but the 2-SE strategy yielded significantly higher µSBS after thermocycling (p < 0.001). The highest µSBS was obtained using the 3-ER strategy regardless of aging (p < 0.001). The 3-ER strategy clearly exposed enamel prisms and resulted in the highest Sa (p < 0.001). In contrast, if SE strategies were used, enamel prisms were barely recognizable, and Sa was not significantly different from baseline (p > 0.95). CONCLUSION: The 3-ER strategy is optimal for bonding to primary enamel. The etching effect of SE strategies is weaker, resulting in lower µSBS. Thermocycling revealed that the bonding durability of the 1-SE strategy is inferior to that of to multi-step strategies.

Effect of an In-Office Bleaching Agent with Surface Pre-Reacted Glass-Ionomer Filler on the Enamel Surface: A In-Vitro Study.

In-office bleaching with high concentrations of hydrogen peroxide (H2O2) agents causes undesirable alterations in the enamel. Surface pre-reacted glass-ionomer (S-PRG) filler is a functional material known for its acid-neutralizing and demineralization-inhibition properties. This study evaluates the effect of S-PRG filler incorporation in H2O2-based bleaching on the enamel surface. Bovine enamel surfaces were bleached using a bleaching paste formulated with a liquid (35% H2O2) and a powder containing 5% or 10% S-PRG filler. The surface roughness and the Vickers microhardness of the treated enamel surfaces were evaluated. The enamel surfaces were observed under a scanning electron microscope (SEM) and analyzed using energy dispersive X-ray (EDX) technology. The surfaces were challenged by citric acid and observed by SEM. The specimens bleached with the paste containing the S-PRG filler showed lower enamel surface roughness and higher microhardness values than did those bleached with the plain paste (0% S-PRG filler); meanwhile, there were no significant differences between the 5% or 10% S-PRG filler groups. The S-PRG filler groups showed enamel surface morphologies similar to those of the non-bleached enamel, according to SEM observation, and EDX analysis detected the presence of fluoride and strontium ions. The S-PRG filler groups showed a higher resistance to erosion. The S-PRG filler mitigated the detrimental effects of bleaching agents on the enamel surface and provided resistance to erosion.

In vitro remineralization assessment of enamel subsurface lesions using different percentages of surface reaction-type pre-reacted glass-ionomer containing gum-based material.

OBJECTIVE: To identify the remineralization activity of enamel subsurface lesions using different percentages of surface pre-reacted glass-ionomer (S-PRG) filler containing gum-base material. METHODS: Gum extracts from gum-base materials containing 0wt%, 5wt%, and 10wt% S-PRG filler were prepared as GE0, GE5, and GE10, respectively. A total of 50 bovine enamel specimens were used, and the polished enamel surface of a 3 × 3 mm2 window area was exposed. The specimens were then subjected to a demineralization solution for seven days to create a subsurface enamel lesion. Remineralization was then conducted for seven days using a protocol whereby the specimens were immersed three times a day in prepared gum extracts (0wt%, 5wt%, and 10wt%) and artificial saliva of pH 7 (Control) for 20 min at 37 °C. Thereafter, remineralization assessment was performed by using Swept Source Optical Coherence Tomography (SS-OCT) and micro-computed tomography (µCT). Surface morphology and elemental analysis were conducted by scanning electron microscopy (SEM) and energy-dispersive X-ray spectrometry (EDS). RESULTS: The depths of the demineralized lesions in the GE5 and GE10 groups were significantly lower than those of the Control and the GE0 groups. SEM observations of the enamel surface morphology of the GE5 and GE10 groups indicated remineralization with S-PRG filler-related elements present. CONCLUSION: The GE5 and GE10 S-PRG filler containing gum-base materials showed significantly improved surface remineralization and reduced demineralization of the enamel lesions. EDS analysis suggested that the released ions from the S-PRG filler might be responsible for surface remineralization. CLINICAL SIGNIFICANCE: The S-PRG filler containing gum-base material may have a significant remineralization effect and improve the surface morphology of enamel subsurface lesions.

Noninvasive diagnostic method using optical coherence tomography detected a vulnerable dentin enamel junction created by phosphoric acid etching.

To investigate the influence of phosphoric acid etching on the dentin enamel junction (DEJ) using optical coherence tomography (OCT). Human teeth were assigned to four groups: 1. control, no additional treatment (CT); 2. The primer of "SE Bond2" was applied (SE), 3. "Enamel Conditioner" was applied (EC), 4. "K-etchant syringe" was applied (KE). After treatment, the DEJ was observed using a laser microscope (CLSM), OCT, and scanning electron microscopy (SEM). Additionally, an ultimate tensile strength (UTS) test at the DEJ was performed. No cracks were observed by CLSM. In contrast, cracks were observed all samples by SEM. Additionally, OCT revealed a white line along the DEJ in all KE specimens and some EC specimens. The UTS test showed a significant difference between CT and KE. This study found that phosphoric acid etching may cause excessive demineralization and weaken the DEJ. This fragility was observed using a non-invasive diagnostic method using OCT.

The bleaching effect of office bleaching agents containing S-PRG filler evaluated by pH value and electron spin resonance.

OBJECTIVES: Surface reaction-type pre-reacted glass-ionomer (S-PRG) filler releases six types of ions with a neutralizing ability. This study evaluated the effect of S-PRG filler incorporation in an H2O2-based bleaching material on the bleaching efficacy, pH, and reaction state. MATERIALS AND METHODS: The experimental bleaching material was formulated by the addition of 5% or 10% S-PRG fillers to the powder part. The stained bovine teeth were treated with the prepared bleaching paste. Commission internationale de l'éclairage (CIE) L*a*b* color space values were recorded before and after bleaching, and the color difference (ΔE) and whiteness index (WID) were calculated. Moreover, the used bleaching formulations were assessed for their pH values and reaction state by evaluating the oxidation state of manganese (Mn+2) using electron spin resonance (ESR). RESULTS: The results of ΔE and WID showed that the addition of S-PRG filler increased the bleaching effect, but there was no significant difference between the groups with 5% and 10% S-PRG filler. A significant increase in pH in S-PRG filler groups (5% pH 6.7, 10% pH 6.8) was found compared to the 0% group (pH 4.8). ESR measurements showed that the signal emitted from Mn+2 decreased over time. The S-PRG filler groups showed a significantly higher reduction in Mn+2 compared to the 0% group, with no significant difference between the 5% and 10% S-PRG groups. CONCLUSIONS: S-PRG filler addition resulted in improved bleaching efficacy, higher reaction rate, and pH values that are close to neutral. CLINICAL RELEVANCE: S-PRG filler addition may be effective on the bleaching outcome of H2O2-based materials.

Polymerization shrinkage of light-cured conventional and bulk-fill composites -The effect of cavity depth and post-curing.

Volumetric shrinkage (VS) of conventional, bulk-fill, and core build-up resin-based composites (RBCs) of various thickness (1-5 mm) was measured using the modified bonded-disk method with confocal laser scanning microscopy. Additionally, the bottom-to-top ratio of Vickers hardness (%VH) was measured. Conventional RBCs exhibited significantly higher VS than bulk-fill and core build-up RBCs (p<0.05). As specimen thickness increased, VS relative to volume (%VS) and difference in VS at each depth (VSdepth) decreased. For conventional RBCs, there was a significant drop in VSdepth between 1 mm and 2 mm (p<0.05), and another drop was observed between 3 mm and 4 mm (p<0.05) where %VH decreased below 90%. For bulk-fill and core build-up RBCs, VSdepth decreased significantly between 2 mm and 3 mm (p<0.05), but %VH exceeded 90% even in 5 mm deep cavities. These results indicated that post-curing contributed to lower shrinkage in deeper layers, and that conventional RBCs were not adequately polymerized at the depth of over 3 mm.

Factors associated with viral RNA shedding and evaluation of potential viral infectivity at returning to school in influenza outpatients after treatment with baloxavir marboxil and neuraminidase inhibitors during 2013/2014-2019/2020 seasons in Japan: an observational study.

BACKGROUND: This study assessed the differences in daily virus reduction and the residual infectivity after the recommended home stay period in Japan in patients infected with influenza and treated with baloxavir (BA), laninamivir (LA), oseltamivir (OS), and zanamivir (ZA). METHODS: We conducted an observational study on children and adults at 13 outpatient clinics in 11 prefectures in Japan during seven influenza seasons from 2013/2014 to 2019/2020. Virus samples were collected twice from influenza rapid test-positive patients at the first and second visit 4-5 days after the start of treatment. The viral RNA shedding was quantified using quantitative RT-PCR. Neuraminidase (NA) and polymerase acidic (PA) variant viruses that reduce susceptibility to NA inhibitors and BA, respectively, were screened using RT-PCR and genetic sequencing. Daily estimated viral reduction was evaluated using univariate and multivariate analyses for the factors such as age, treatment, vaccination status, or the emergence of PA or NA variants. The potential infectivity of the viral RNA shedding at the second visit samples was determined using the Receiver Operator Curve based on the positivity of virus isolation. RESULTS: Among 518 patients, 465 (80.0%) and 116 (20.0%) were infected with influenza A (189 with BA, 58 with LA, 181 with OS, 37 with ZA) and influenza B (39 with BA, 10 with LA, 52 with OS, 15 with ZA). The emergence of 21 PA variants in influenza A was detected after BA treatment, but NA variants were not detected after NAIs treatment. Multiple linear regression analysis showed that the daily viral RNA shedding reduction in patients was slower in the two NAIs (OS and LA) than in BA, influenza B infection, aged 0-5 years, or the emergence of PA variants. The residual viral RNA shedding potentially infectious was detected in approximately 10-30% of the patients aged 6-18 years after five days of onset. CONCLUSIONS: Viral clearance differed by age, type of influenza, choice of treatment, and susceptibility to BA. Additionally, the recommended homestay period in Japan seemed insufficient, but reduced viral spread to some extent since most school-age patients became non-infectious after 5 days of onset.