High-temperature and high-pressure in situ SCC device for synchrotron radiation diffraction experiments and application using an austenitic stainless steel.

Suppressing the stress corrosion cracking (SCC) by reducing the carbon content in austenitic stainless steels is apparently not effective on core shrouds used in boiling water reactors in Japan: trans-granular cracking was found in the shrouds. To clarify the mechanism of the cracking, in situ stress measurements on specimens under stretched conditions in hot water have been attempted in the present study. An in situ device for diffraction measurements at synchrotron radiation facilities has been developed, and in situ experiments have been carried out at SPring-8. The SUS316L steel specimen was solution heat-treated, surface-ground and then placed in the in situ device. Sapphire windows were used for the light path in the device. A sufficient diffracted beam intensity was obtained through two sapphire windows and water. The side-inclination method was used for measuring the stress exerted on the specimen. A 2theta-sin2psi plot showed that a tensile stress was induced. The measured stress value is considered to be the summation of stresses owing to pre-straining, in situ loading and residual stress owing to surface grinding.

"Devil's staircase"-type phase transition in NaV2O5 under high pressure.

The "devil's staircase"-type phase transition in the quarter-filled spin-ladder compound NaV2O5 has been discovered at low temperature and high pressure by synchrotron radiation x-ray diffraction. A large number of transitions are found to successively take place among higher-order commensurate phases with 2a x 2b x zc type superstructures. The observed temperature and pressure dependence of modulation wave number q(c), defined by 1/z, is well reproduced by the axial next nearest neighbor Ising model. The q(c) is suggested to reflect atomic displacements presumably coupled with charge ordering in this system.

XANES study of charge ordering on the spin-Peierls phase transition of alpha'-NAV2O5.

alpha'-NaV2O5 transforms at Tc = 34K, and the origin of the phase transition seems to be caused by the charge order and spin-Peierls mechanism. However the experiments which reveal the existence of charge order are very little. We measured XANES of V atoms which relates to the valence of V. It was found that the valences of V atoms in NaV2O5 were V4.5+ in the high temperature phase by comparing pre-edge and XANES of NaV2O5 with that of LiV2O5 CaV2O5 and V2O5. The analysis of EXAFS also shows the environment of the V4.5+ state.