Preparation of films based on reticulated fish gelatin containing garlic essential oil.

Agro-industrial co-products, such as fish gelatin, stand out for their capacity in forming biopolymeric films, being biocompatible and non-toxic; however, its hydrophilicity poses a challenge. Essential oils, rich in bioactives, attract research interest aiming to enhance the protective barrier of films and enable their application in packaging. This study produced films based on cross-linked Nile tilapia skin gelatin, incorporating garlic essential oil. Gelatin obtained through partial collagen hydrolysis from the fish skin and cross-linked with gallic acid had hydroxyproline content of 10.02 g 100 g-1 and gel strength of 287 g, which were consistent with other studies. Oil extraction used supercritical CO2 as a solvent and ethanol as a cosolvent, following a factorial experimental design, evaluating the extraction temperature (40 °C and 70 °C) and cosolvent ratio (1:1 and 1:3), with three central points. Extraction was successful, with higher yields on a dry basis at 70 °C (88.35 %), using a 1:1 cosolvent ratio. Films incorporated with oil exhibited lower water vapor permeability (WVP) than those with only cross-linked gelatin (1.59 (g m-1 s-1 Pa-1) 1011). The film with the most suitable tensile strength (19.07 MPa), elongation (120.91 %), and WVP (1.09 (g m-1 s-1 Pa-1) 1011) properties contained garlic oil extracted at the central point (55 °C and 1:2). Thermal analysis indicated increased melting temperatures in films with added oil, suggesting low thermal degradation. These results suggest that garlic oil addition can improve the properties of fish gelatin-based films, making them promising for biodegradable packaging.

Chitosan-based nanocapsules by emulsification containing PUFA concentrates from tuna oil.

Chitosan nanocapsules containing polyunsaturated fatty acid (PUFA) concentrates from tuna oil, with EPA + DHA contents around 57% (w w-1), were developed by emulsification process, using different chitosan concentration (1.0%, 1.5%, 2.0%, w v-1) and stirring speed (10,000, 15,000, 20,000 rpm). The effects of these parameters on particle size and zeta potential were evaluated. The physical and oxidative stabilities were used to measure the product quality during storage. Chitosan concentration, stirring speed and its interaction significantly affected (p < 0.05) the particle size. In addition, chitosan concentration significantly affected (p < 0.05) the zeta potential of nanocapsules emulsion. Based on the results of physical and oxidative stabilities, the nanocapsules were stable for 30 days under refrigeration temperature (7 °C), and with 1.5-2% chitosan resulted in improved protection against oil oxidation. The nanocapsules produced with 2% chitosan and 10,000 rpm showed the lowest variations of polydispersity index and nanocapsules size after 30 days of storage (221.8 ± 3.0 nm). These conditions can be considered the most suitable to produce nanocapsules of PUFA concentrates from tuna oil using chitosan as wall material. These nanocapsules showed physical characteristics and oxidative stability, which could enable their application in the food industry, representing an important source of EPA and DHA fatty acids.