A Novel Method to Enhance the Mechanical Properties of Polyacrylonitrile Nanofiber Mats: An Experimental and Numerical Investigation.

This study addresses the challenge of enhancing the transverse mechanical properties of oriented polyacrylonitrile (PAN) nanofibers, which are known for their excellent longitudinal tensile strength, without significantly compromising their inherent porosity, which is essential for effective filtration. This study explores the effects of doping PAN nanofiber composites with varying concentrations of polyvinyl alcohol (PVA) (0.5%, 1%, and 2%), introduced into the PAN matrix via a dip-coating method. This approach ensured a random distribution of PVA within the nanofiber mat, aiming to leverage the synergistic interactions between PAN fibers and PVA to improve the composite's overall performance. This synergy is primarily manifested in the structural and functional augmentation of the PAN nanofiber mats through localized PVA agglomerations, thin films between fibers, and coatings on the fibers themselves. Comprehensive evaluation techniques were employed, including scanning electron microscopy (SEM) for morphological insights; transverse and longitudinal mechanical testing; a thermogravimetric analysis (TGA) for thermal stability; and differential scanning calorimetry (DSC) for thermal behavior analyses. Additionally, a finite element method (FEM) analysis was conducted on a numerical simulation of the composite. Using our novel method, the results demonstrated that a minimal concentration of the PVA solution effectively preserved the porosity of the PAN matrix while significantly enhancing its mechanical strength. Moreover, the numerical simulations showed strong agreement with the experimental results, validating the effectiveness of PVA doping in enhancing the mechanical properties of PAN nanofiber mats without sacrificing their functional porosity.

Mechanical and Thermal Characterization of Annealed Oriented PAN Nanofibers.

Polyacrylonitrile (PAN) nanofibers have extensive applications as filters in various fields, including air and water filtration, biofluid purification, and the removal of toxic compounds and hazardous pollutants from contaminated water. This research focuses on investigating the impacts of annealing on the mechanical and thermal characteristics of oriented PAN nanofibers produced through the electrospinning of a PAN solution. The nanofiber mats were subjected to annealing temperatures ranging from 70 °C to 350 °C and characterized using a tensile test machine, thermogravimetry, differential scanning calorimetry, and scanning electron microscopy (SEM). The study aimed to examine the tensile strength in the transverse and longitudinal directions, Young's modulus, and glass transition temperatures of PAN nanofiber mats. The results indicate that, upon annealing, the diameter of the nanofibers decreased by approximately 20%, while the tensile strength increased in the longitudinal and transverse directions by 32% and 23%, respectively. Furthermore, the annealing temperature influenced the glass transition temperature of the nanofiber mats, which exhibited a 6% decrease at 280 °C, while the degradation temperature showed a slight increase of 3.5% at 280 °C. The findings contribute to a better understanding of the effects of annealing on PAN nanofiber mats, facilitating their potential for various filtration applications.

Microstructure and Mechanical Properties of Inverse Nanocomposite Made from Polylactide and Hydroxyapatite Nanoparticles.

Polymer nanocomposites have been extensively researched for a variety of applications, including medical osteoregenerative implants. However, no satisfactory solution has yet been found for regeneration of big, and so-called critical, bone losses. The requirement is to create a resorbable material which is characterised by optimum porosity, sufficient strength, and elastic modulus matching that of the bone, thus stimulating tissue regrowth. Inverse nanocomposites, where the ceramic content is larger than the polymer content, are a recent development. Due to their high ceramic content, they may offer the required properties for bone implants, currently not met by polymer nanocomposites with a small number of nanoparticles. This paper presents inverse nanocomposites composed of bioresorbable nano crystalline hydroxyapatite (HAP NPs) and polylactide (PLLA), produced by cryomilling and a warm isostatic pressing method. The following compositions were studied: 25%, 50%, and 75% of HAP NPs by volume. The mechanical properties and structure of these composites were examined. It was discovered that 50% volume content was optimal as far as compressive strength and porosity are concerned. The inverse nanocomposite with 50% nanoceramics volume displayed a compressive strength of 99 ± 4 MPa, a contact angle of 50°, and 25% porosity, which make this material a candidate for further studies as a bioresorbable bone implant.