Impact of Residual Compositional Inhomogeneities on the MCT Material Properties for IR Detectors.

HgCdTe is a well-known material for state-of-the-art infrared photodetectors. The interd-iffused multilayer process (IMP) is used for Metal-Organic Chemical Vapor Deposition (MOCVD) of HgCdTe heterostructures, enabling precise control of composition. In this method, alternating HgTe and CdTe layers are deposited, and they homogenize during growth due to interdiffusion, resulting in a near-uniform material. However, the relatively low (350 °C) IMP MOCVD growth temperature may result in significant residual compositional inhomogeneities. In this work, we have investigated the residual inhomogeneities in the IMP-grown HgCdTe layers and their influence on material properties. Significant IMP growth-related oscillations of composition have been revealed in as-grown epilayers with the use of a high-resolution Secondary Ion Mass Spectroscopy (SIMS). The oscillations can be minimized with post-growth annealing of the layers at a temperature exceeding that of growth. The electric and photoelectric characterizations showed a significant reduction in the background doping and an increase in the recombination time, which resulted in dramatic improvement of the spectral responsivity of photoconductors.

Study of HgCdTe (100) and HgCdTe (111)B Heterostructures Grown by MOCVD and Their Potential Application to APDs Operating in the IR Range up to 8 µm.

The trend related to reach the high operating temperature condition (HOT, temperature, T > 190 K) achieved by thermoelectric (TE) coolers has been observed in infrared (IR) technology recently. That is directly related to the attempts to reduce the IR detector size, weight, and power dissipation (SWaP) conditions. The room temperature avalanche photodiodes technology is well developed in short IR range (SWIR) while devices operating in mid-wavelength (MWIR) and long-wavelength (LWIR) require cooling to suppress dark current due to the low energy bandgap. The paper presents research on the potential application of the HgCdTe (100) oriented and HgCdTe (111)B heterostructures grown by metal-organic chemical vapor deposition (MOCVD) on GaAs substrates for the design of avalanche photodiodes (APDs) operating in the IR range up to 8 µm and under 2-stage TE cooling (T = 230 K). While HgCdTe band structure with molar composition xCd < 0.5 provides a very favorable hole-to-electron ionization coefficient ratio under avalanche conditions, resulting in increased gain without generating excess noise, the low level of background doping concentration and a low number of defects in the active layer is also required. HgCdTe (100) oriented layers exhibit better crystalline quality than HgCdTe (111)B grown on GaAs substrates, low dislocation density, and reduction of residual defects which contribute to a background doping within the range ~1014 cm-3. The fitting to the experimentally measured dark currents (at T = 230 K) of the N+-ν-p-P+ photodiodes commonly used as an APDs structure allowed to determine the material parameters. Experimentally extracted the mid-bandgap trap concentrations at the level of 2.5 × 1014 cm-3 and 1 × 1015 cm-3 for HgCdTe (100) and HgCdTe (111)B photodiode are reported respectively. HgCdTe (100) is better to provide high resistance, and consequently sufficient strength and uniform electric field distribution, as well as to avoid the tunneling current contribution at higher bias, which is a key issue in the proper operation of avalanche photodiodes. It was presented that HgCdTe (100) based N+-ν-p-P+ gain, M > 100 could be reached for reverse voltage > 5 V and excess noise factor F(M) assumes: 2.25 (active layer, xCd = 0.22, k = 0.04, M = 10) for λcut-off = 8 µm and T = 230 K. In addition the 4-TE cooled, 8 µm APDs performance was compared to the state-of-the-art for SWIR and MWIR APDs based mainly on III-V and HgCdTe materials (T = 77-300 K).