Silica infiltration in partially stabilized zirconia: Effect of hydrothermal aging on mechanical properties.

It aimed to evaluate if silica infiltration might influence the hydrothermal degradation of zirconia by determining: the phases formed, hardness, microstructure, and flexural strength of a 3Y-TZP. Yttria partially stabilized zirconia discs (1.2 mm thickness x 13 mm diameter) (InCeram YZ, Vita Zanhfabrik) were produced and assigned into 6 groups, considering 2 factors: silica infiltration in 2 levels (as-sintered or infiltration) and hydrothermal aging (LTD-Low Temperature Degradation) in 3 levels (baseline, aging at 132 °C for 35 h or 140 h). All the groups were subjected to the biaxial flexural test (n = 30), and Vickers hardness (n = 42). Weibull analysis was performed to determine the Weibull moduli (m) and characteristic strenghts (σ0). The specimens were characterized by scanning electron microscopy (SEM) to evaluate microstructure and X-ray diffraction (XRD) for phases percentages determination. For as-sintered condition: there was saturation of the amount of monoclinic zirconia after 35 h of hydrothermal aging, with 66% of monoclinic zirconia formed on the surface. LTD generated a progressive reduction in hardness over time; flexural strength was increased by the 35-h treatment (baseline: 974 MPa; 35 h: 1161.5 MPa), but, the 140 °C treatment was deleterious (698.5 MPa). On the other hand, the infiltrated specimens had an increase in the amount of cubic zirconia on the surface and showed 26% (35h) and 31% (140h) of monoclinic zirconia after the hydrothermal aging ; the strength was kept unaltered after LTD-35 h (935.9 MPa) and an increase was observed after LTD-140 h (1033.6 MPa); the hardness values had no statistically significant changes during the process. Thus, one can concludes that the silica infiltration can prevent the decrease in the mechanical properties due to the LTD on partially stabilized zirconia materials.

A new silica-infiltrated Y-TZP obtained by the sol-gel method.

OBJECTIVE: The aim of this study was to evaluate silica infiltration into dental zirconia (VITA In-Ceram 2000 YZ, Vita Zahnfabrik) and its effects on zirconia's surface characteristics, structural homogeneity and bonding to a resin cement. METHODS: Infiltration was performed by immersion of the pre-sintered zirconia specimens in silica sols for five days (ZIn). Negative (pure zirconia specimens, ZCon-) and positive controls (specimens kept in water for 5 days, ZCon+) were also performed. After sintering, the groups were evaluated by X-ray diffraction (XRD), grazing angle X-ray diffraction (DRXR), scanning electron microscopy (SEM), contact angle measurements, optical profilometry, biaxial flexural test and shear bonding test. Weibull analysis was used to determine the Weibull modulus (m) and characteristic strength (σ0) of all groups. RESULTS: There were no major changes in strength for the infiltrated group, and homogeneity (m) was also increased. A layer of ZrSiO4 was formed on the surface. The bond strength to resin cement was improved after zirconia infiltration, acid conditioning and the use of an MDP primer. CONCLUSION: The sol-gel method is an efficient and simple method to increase the homogeneity of zirconia. Infiltration also improved bonding to resin cement. CLINICAL SIGNIFICANCE: The performance of a zirconia infiltrated by silica gel improved in at least two ways: structural homogeneity and bonding to resin cement. The infiltration is simple to perform and can be easily managed in a prosthesis laboratory.

Surface Treatments of Zirconia to Enhance Bonding Durability.

This article reviewed the surface treatments used most often to improve adhesion between zirconia and adhesive cements, focusing on their capacity to provide long-term bonding. Traditional and new treatments for zirconia bonding were searched. Some new treatments were discussed along with topographical views of the modified zirconia. New methods, such as selective infiltration etching and the low-fusing glassy porcelain application are promising, but more research is needed.

Durability of feldspathic veneering ceramic on glass-infiltrated alumina ceramics after long-term thermocycling.

AIM: This study compared the bond strength durability of a feldspathic veneering ceramic to glass-infiltrated reinforced ceramics in dry and aged conditions. METHODS: Disc shaped (thickness: 4 mm, diameter: 4 mm) of glass-infiltrated alumina (In-Ceram Alumina) and glass-infiltrated alumina reinforced by zirconia (In-Ceram Zirconia) core ceramic specimens (N=48, N=12 per groups) were constructed according to the manufacturers' recommendations. Veneering ceramic (VITA VM7) was fired onto the core ceramics using a mold. The core-veneering ceramic assemblies were randomly divided into two conditions and tested either immediately after specimen preparation (Dry) or following 30000 thermocycling (5-55 ºC±1; dwell time: 30 seconds). Shear bond strength test was performed in a universal testing machine (cross-head speed: 1 mm/min). Failure modes were analyzed using optical microscope (x20). The bond strength data (MPa) were analyzed using ANOVA (α=0.05). RESULTS: Thermocycling did not decrease the bond strength results for both In-Ceram Alumina (30.6±8.2 MPa; P=0.2053) and In-Ceram zirconia (32.6±9 MPa; P=0.3987) core ceramic-feldspathic veneering ceramic combinations when compared to non-aged conditions (28.1±6.4 MPa, 29.7±7.3 MPa, respectively). There were also no significant differences between adhesion of the veneering ceramic to either In-Ceram Alumina or In-Ceram Zirconia ceramics (P=0.3289). Failure types were predominantly a mixture of adhesive failure between the veneering and the core ceramic together with cohesive fracture of the veneering ceramic. CONCLUSION: Long-term thermocycling aging conditions did not impair the adhesion of the veneering ceramic to the glass-infiltrated alumina core ceramics tested.

Cementation of fiber post: influence of the cement insertion techniques on the bond strength of the fiber post-root dentin and the quality of the cement layer.

AIM: The aim of this study was to assess the influence of resin cement insertion methods on the bond strength of a fiber post to root dentin and quality of the cement layer. METHODS: Forty bovine single-roots (length =16 mm) were randomly allocated into four groups, according to the cement insertion methods (N.=10): Gr1- Lentulo drill #40, Gr2- Centrix syringe, Gr3- Explorer #5, Gr4- fiber post. The root canals were prepared at 12 mm, using preparation bur # 3 of a cylinder quartz-FRC post (Aesthet post-plus, Bisco). The fiber posts were cemented using a multi-step etch-and-rinse adhesive system (All Bond 2®, Bisco) and a dual-cured resin cement (Duolink, Bisco). Each root was cut into seven samples: four samples of 1.8 mm thickness for push-out testing, and three with 0.5 mm for cement layer quality analyzing. One-way ANOVA was used for the push-out test values and the One-Way Kruskal-Wallis (P<0.05) and Dunn (10%) tests for the cement layer analyzes. RESULTS: ANOVA showed that the cement layer quality was affected by the cement insertion methods (P=0.0044): Gr1 (3.8 ± 1.3a), Gr2 (3.2 ± 1.3a), Gr3 (5.2 ± 1.5a,b) and Gr4 (5.2 ± 1.5b) (Dunn test), whereas the bond strength (MPa) was not affected by cement insertion methods: G1 (4.2 ± 1.3), G2 (3.2 ± 1.8), G3 (4.5 ± 0.9), G4 (3.1 ± 1.3). CONCLUSION: The fiber posts should be cemented with the assistance of the lentulo drill or centrix syringe to promote the best cement layer results.