RESUMO
Fatal dendritic growth in lithium metal batteries is closely related to the composition and thickness of the modified separator. Herein, an ultrathin nanocoating composed of monolayer montmorillonite (MMT), poly(vinyl alcohol) (PVA) on a polypropylene separator is prepared. The MMT was exfoliated into monolayers (only 0.96 nm) by intercalating PVA under ultrasound, followed by cross-linking with glutaraldehyde. The thickness of the nanocoating on the polypropylene separator, as determined using the pull-up method, is only 200-500 nm with excellent properties. As a result, the lithium-symmetric battery composed of it has a low overpotential (only 40 mV) and a long lifespan of more than 7900 h at high current density, because ion transport is unimpeded and Li+ flows uniformly through the ordered ion channels between the MMT layers. Additionally, the separator exhibited excellent cycling stability in Li-S batteries. This study offers a new idea for fabricating ultrathin clay/polymer modified separators for metal anode stable cycling at high current densities.
RESUMO
The slow Li+ transport rate in the thick sulfur cathode of the Li-S battery affects its capacity and cycling performance. Herein, Fe-doped highly ordered mesoporous silica material (Fe-HSBA-15) as a sulfur carrier of the Li-S battery shows high ion conductivity (1.10 mS cm-1) and Li+ transference number (0.77). The Fe-HSBA-15/S cell has an initial capacity of up to 1216.7 mA h g-1 at 0.2C and good stability. Impressively, at a high sulfur load of 4.34 mg cm-2, the Fe-HSBA-15/S cell still maintains an area specific capacity of 4.47 mA h cm-2 after 100 cycles. This is because Fe-HSBA-15 improves the Li+ diffusion behavior through the ordered mesoporous structure. Theoretical calculations also confirmed that the doping of iron enhances the adsorption of polysulfides, reduces the band gap and makes the catalytic activity stronger.
RESUMO
Considering the electrochemical activity/stability and preparation feasibility of silicon (Si) nanomaterials, we designed a restricted-magnesium-vapor-reduction to fabricate sustainable Si/SiOx/C porous anodes with nanopores and polycrystalline structures.
RESUMO
Poor interface stability is a crucial problem hindering the electrochemical performance of solid-state lithium batteries. In this work, a novel approach for interface stability was proposed to integrate the cathode/solid electrolyte by forming an electrolyte buffer layer on the rough surface of the cathode and coating a layer of graphite on the side of the electrolyte facing the lithium anode. This hybrid structure significantly improves the integration and the interface stability of the electrode/electrolyte. The interfacial resistance was dramatically reduced, the stability of the plating/stripping of Li metal was enhanced, and the growth of lithium dendrites was also inhibited due to the formation of the LiC6 transition layer. The obtained solid-state lithium battery shows enhanced rate performance at room temperature from 0.5 to 4 C and stable cycling performance at 1 C with a retention capacity of 100 mAh g-1 after 200 cycles. This integrated electrode/electrolyte design approach is expected to be widely used to improve interfacial stability and room-temperature electrochemical performance of solid-state batteries.