Mechanical, Hydrophobic, and Barrier Properties of Nanocomposites of Modified Polypropylene Reinforced with Low-Content Attapulgite.

Attapulgite (ATT) has never been used as a barrier additive in polypropylene (PP). As a filler, ATT should be added in high content to PP. However, that would result in increased costs. Moreover, the compatibility between ATT and the PP matrix is poor due to the lack of functional groups in PP. In this study, carboxylic groups were introduced to PP to form a modified polypropylene (MPP). ATT was purified, and a low content of it was added to MPP to prepare MPP/ATT nanocomposites. The analysis from FTIR indicated that ATT could react with MPP. According to the results of oxygen and water permeability tests, the barrier performance of the nanocomposite was optimal when the ATT content was 0.4%. This great improvement in barrier performance might be ascribed to the following three reasons: (1) The existence of ATT extended the penetration path of O2 or H2O molecules; (2) O2 or H2O molecules may be adsorbed and stored in the porous structure of ATT; (3) Most importantly, -COOH of MPP reacted with -OH on the surface of ATT, thereby the inner structure of the nanocomposite was denser, and it was less permeable to molecules. Therefore, nanocomposites prepared by adding ATT to MPP have excellent properties and low cost. They can be used as food packaging materials and for other related applications.

Barrier Properties and Hydrophobicity of Biodegradable Poly(lactic acid) Composites Reinforced with Recycled Chinese Spirits Distiller's Grains.

Adding natural biomass to poly(lactic acid) (PLA) as a reinforcing filler is a way to change the properties of PLA. This paper is about preparing PLA/biomass composites by physically melting and blending Chinese Spirits distiller's grains (CSDG) biomass and PLA to optimize the composite performance. Composites of modified PLA (MPLA) with varying amounts of CSDG were also prepared by the melt-mixing method, and unmodified PLA/CSDG composites were used as a control group for comparative analysis. The functional groups of MPLA enhanced the compatibility between the polymer substrate and CSDG. The composite water vapor/oxygen barrier and mechanical properties were studied. It was found that the barrier and mechanical properties of MPLA/CSDG composites were significantly improved. SEM was adopted to examine the tensile section structure of the composites, and the compatibility between the filler and the matrix was analyzed. An appropriate amount of CSDG had a better dispersibility in the matrix, and it further improved the interfacial bonding force, which in turn improved the composite mechanical properties. X-ray diffraction, thermogravimetric analysis, and differential scanning calorimetry were conducted to determine the crystalline properties and to analyze the stability of the composites. It was found that the CSDG content had a significant effect on the crystallinity. Barrier and biodegradation mechanisms were also discussed.