Toughness Evolution of Flax-Fiber-Reinforced Composites under Repeated Salt Fog-Dry Aging Cycles.

This research examined the response of flax-fiber-reinforced composites (FFRCs) to simulated outdoor conditions involving repeated exposure to salt fog and drying. The study investigated the effect of cycles on the toughness of the FFRCs. To achieve this, the composites were exposed to humidity (salt fog) for 10 days, followed by 18 days of drying in cycles. A total of up to 3 cycles, each lasting 4 weeks, were conducted over a 12-week period. Throughout this process, changes in the material's weight, water absorption, and mechanical properties were monitored by water uptake and three-point bending tests. The findings revealed the significant impact of these humid-dry cycles on the mechanical response of the FFRCs. When exposed to humid environments without drying, the composite's toughness increased significantly, due to a weakening effect more pronounced for stiffness, with strength reductions of about 20%. However, subsequent drying partially restored the material's performance. After 18 days of drying, the composite regained most of its initial performance.

New Materials and Technologies for Durability and Conservation of Building Heritage.

The increase in concrete structures' durability is a milestone to improve the sustainability of buildings and infrastructures. In order to ensure a prolonged service life, it is necessary to detect the deterioration of materials by means of monitoring systems aimed at evaluating not only the penetration of aggressive substances into concrete but also the corrosion of carbon-steel reinforcement. Therefore, proper data collection makes it possible to plan suitable restoration works which can be carried out with traditional or innovative techniques and materials. This work focuses on building heritage and it highlights the most recent findings for the conservation and restoration of reinforced concrete structures and masonry buildings.

An Innovative Treatment Based on Sodium Citrate for Improving the Mechanical Performances of Flax Fiber Reinforced Composites.

The goal of this paper is to evaluate the effectiveness of a cost-effective and eco-friendly treatment based on the use of sodium citrate (Na3C6H5O7) on the mechanical properties of flax fiber reinforced composites. To this scope, flax fibers were soaked in mildly alkaline solutions of the sodium salt at different weight concentration (i.e., 5%, 10% and 20%) for 120 h at 25 °C. The modifications on fibers surface induced by the proposed treatment were evaluated through Fourier transform infrared analysis (FTIR), whereas scanning electron microscope (SEM) and helium pycnometer were used to obtain useful information about composites morphology. The effect of the concentration of the treating solution on the mechanical response of composites was determined through quasi-static tensile and flexural tests, Charpy impact tests and dynamical mechanical thermal (DMTA) tests. The results revealed that composites reinforced with flax fibers treated in 10% solution exhibit the best mechanical performances as well as the lowest void contents. SEM analysis supported these findings showing that, by treating fibers in solutions with concentration up to 10%, composites having better morphology can be manufactured, in comparison to untreated ones. Conversely, higher Na3C6H5O7 concentrations negatively affect both the morphology and the mechanical properties of composites.

Pinned Hybrid Glass-Flax Composite Laminates Aged in Salt-Fog Environment: Mechanical Durability.

The aim of the present paper is to study the mechanical performance evolution of pinned hybrid glass-flax composite laminates under environment aging conditions. Hybrid glass-flax fibers/epoxy pinned laminates were exposed to salt-spray fog environmental conditions up to 60 days. With the purpose of assessing the relationship between mechanical performances and failure mechanisms at increasing aging time, single lap joints at varying joint geometry (i.e., hole diameter D and hole distance E from free edge) were characterized after 0 days (i.e., unaged samples), 30 days, and 60 days of salt-fog exposition. Based on this approach, the property-structure relationship of the composite laminates was assessed on these critical environmental conditions. In particular, a reduction of failure strength for long-aging-time-aged samples was observed in the range 20-30% compared to unaged one. Due to the natural fiber degradation in a salt-fog environment, premature catastrophic fractures mode due to shear-out and net-tension were found, related to reduced joint fracture strength. This behavior identifies that this type of joint requires a careful design in order to guarantee an effective mechanical stability of the composite hybrid joint under long-term operating conditions in an aggressive environment.