RESUMO
Objective: To determine the effect of grit-blasting before and after sintering on the surface roughness of zirconia and the micro-tensile bond strength of a pressable veneering ceramic to zirconia. Methods: Pre-sintered zirconia blocks (IPS e.max ZirCAD, Ivoclar) were divided into four test groups of three specimens each and a control group ('CTR'; no surface treatment). Pre-S-30, Pre-S-50, and Pre-S-110 were grit-blasted with 30-µm SiO2-coated Al2O3, 50-µm Al2O3 and 110-µm Al2O3 particles, respectively, before sintering. Post-S-30 was grit-blasted with 30-µm SiO2-coated Al2O3 after sintering. For each treatment, the surface roughness was measured (Ra, Perthometer M4P, Mahr Perthen). After sintering the zirconia blocks, a liner was applied and a pressable ceramic (IPS e.max ZirPress, Ivoclar) was heat-pressed. Sixteen microbars were obtained from each block and submitted to micro-tensile bond-strength (µTBS) testing. Data were analyzed with one-way ANOVA. Any correlation between Ra and µTBS was evaluated (Sperman test). Results: Grit-blasting before sintering with 110-µm Al2O3 (RaPre-S-110 = 3.4 ± 0.4 µm), 50-µm Al2O3 (RaPre-S-50 = 2.3 ± 0.5 µm), and 30-µm SiO2-coated Al2O3 (RaPre-S-30 = 1.2 ± 0.2 µm) resulted in significantly higher roughness than grit-blasting after sintering with 30-µm SiO2-coated Al2O3 (RaPost-S-30 = 0.5 ± 0.1 µm). The highest µTBS was measured when the sintered zirconia was grit-blasted with 30-µm SiO2-coated Al2O3 (µTBSPost-S-30 = 28.5 ± 12.6 MPa), which was significantly different from that of specimens that were grit-blasted before sintering (µTBSPre-S-30 = 21.8 ± 10.4; µTBSPre-S-50 = 24.1 ± 12.6; µTBSPre-S-110 = 26.4 ± 14.1) or were not grit-blasted (µTBSCTR = 20.2 ± 11.2). Conclusions: Grit-blasting zirconia before sintering enhanced the surface roughness proportionally to the particle size of the sand used. Grit-blasting with 30-µm SiO2-coated Al2O3 after sintering improved bonding of the veneering ceramic to zirconia. Clinical Significance: As grit-blasting with 30-µm SiO2-coated Al2O3 after sintering improved bonding of the veneering ceramic to zirconia, it may reduce veneering ceramic fractures/chipping.
RESUMO
OBJECTIVES: To investigate the cytotoxicity on human dental pulp cells (HDPCs) and Streptococcus mutans (S.mutans) biofilm formation on universal resin composite cements (UCs). METHODS: Three UCs (RelyX Universal, 3 M Oral Care - RXU; Panavia SA Cement Universal, Kuraray Noritake - PSAU; SoloCem, Coltene - SCM) and one 'gold-standard' multi-step cement (Panavia V5, Kuraray Noritake - PV5) were used following two polymerization protocols (light-cured - LC; self-cured - SC). Cytotoxicity (MTT) tests were performed after 1, 3 and 7 days of direct contact. Carboxy-2',7'-dichlorodihydrofluorescein diacetate was used to detect the release of reactive oxygen species (ROS), and interleukin 6 (IL-6) expression was analyzed by IL-6 proquantum high sensitivity immunoassay. S. mutans biofilms were grown on UCs samples in a bioreactor for 24 h, then adherent viable biomass was assessed using MTT assay. For microbiological procedures, half of UCs samples underwent accelerated aging. Data were statistically analyzed (α = 0.05). RESULTS: The highest cytotoxicity was observed for PSAU SC, RXU SC, and PV5 SC at day 1, then for SC RXU after 3 days, and SC PSAU, LC PV5 and SCM after 1-week (p < 0.05). There was no increase in IL-6 expression after 1 day, while it increased depending on the group at 3 and 7 days. The highest ROS expression after 12 h was recorded for PSAU SC, PV5 SC and PV5 LC. Biofilm formation was as follows: RXU > > PSAU = PV5 > SCM, while light-curing systematically decreased biofilm formation (≈-33 %). Aging leveled out differences between UCs and between polymerization protocols. SIGNIFICANCE: The choice of cement brand, rather than category, and polymerization protocol influence cell viability and microbiological behavior. Light-curing is beneficial for reducing the harmful pulpal effect that UCs may possess.
RESUMO
Various implant surface treatment methods have been developed to achieve good osseointegration in implant treatment. However, some cases remain impossible to treat with implants because osseointegration is not obtained after implantation, and the implants fail. Thus, this study focused on phosphorylated pullulan because of its adhesiveness to titanium (Ti) and bone, high biocompatibility, and early replacement with bone. In this study, the response of bone-related cells to phosphorylated pullulan was evaluated to develop a new surface treatment method. Saos-2 (human osteosarcoma-derived osteoblast-like cells), MC3T3-E1 (mouse calvaria-derived osteoblast-like cells), and RAW264.7 (mouse macrophage-like cells) were used. In evaluating cellular responses, phosphorylated pullulan was added to the culture medium, and cell proliferation and calcification induction tests were performed. The proliferation and calcification of cells on the surface of Ti disks coated with phosphorylated pullulan were also evaluated. In addition, bone morphogenetic protein-2 (BMP-2), an osteogenic factor, was used to evaluate the role of phosphorylated pullulan as a drug carrier in inducing calcification on Ti disks. Phosphorylated pullulan tended to promote the proliferation of osteoblast-like cells and the formation of calcification on Ti disks coated with phosphorylated pullulan. Ti disks coated with phosphorylated pullulan loaded with BMP-2 enhanced calcification. Phosphorylated pullulan inhibited osteoclast-like cell formation. These results are due to the properties of phosphorylated pullulan, such as adhesiveness to titanium and drug-loading function. Therefore, phosphorylated pullulan effectively promotes bone regeneration when coated on titanium implants and is useful for developing a new surface treatment method.
RESUMO
PURPOSE: To measure zirconia-to-zirconia microtensile bond strength (µTBS) using composite cements with and without primer. MATERIALS AND METHODS: Two Initial Zirconia UHT (GC) sticks (1.8x1.8x5.0 mm) were bonded using four cements with and without their respective manufacturer's primer/adhesive (G-CEM ONE [GOne] and G-Multi Primer, GC; Panavia V5 [Pv5]), and Panavia SA Cement Universal [PSAu], and Clearfil Ceramic Plus, Kuraray Noritake; RelyX Universal (RXu) and Scotchbond Universal Plus [SBUp], 3M Oral Care). Specimens were trimmed to an hour-glass shaped specimen whose isthmus is circular in cross-section. After 1-week water storage, the specimens were either tested immediately (1-week µTBS) or first subjected to 50,000 thermocycles (50kTC-aged µTBS). The fracture mode was categorized as either adhesive interfacial failure, cohesive failure in composite cement, or mixed failure, followed by SEM fracture analysis of selected specimens. Data were analyzed using linear mixed-effects statistics (α = 0.05; variables: composite cement, primer/adhesive application, aging). RESULTS: The statistical analysis revealed no significant differences with aging (p = 0.3662). No significant difference in µTBS with/without primer and aging was recorded for GOne and PSAu. A significantly higher µTBS was recorded for Pv5 and RXu when applied with their respective primer/adhesive. Comparing the four composite cements when they were applied in the manner that resulted in their best performance, a significant difference in 50kTC-aged µTBS was found for PSAu compared to Pv5 and RXu. A significant decrease in µTBS upon 50kTC aging was only recorded for RXu in combination with SBUp. CONCLUSION: Adequate bonding to zirconia requires the functional monomer 10-MDP either contained in the composite cement, in which case a separate 10-MDP primer is no longer needed, or in the separately applied primer/adhesive.
Assuntos
Resinas Compostas , Colagem Dentária , Teste de Materiais , Metacrilatos , Cimentos de Resina , Resistência à Tração , Zircônio , Zircônio/química , Cimentos de Resina/química , Resinas Compostas/química , Metacrilatos/química , Cimentos Dentários/química , Cerâmica/química , Análise do Estresse Dentário , Humanos , Fatores de Tempo , Água/química , Temperatura , Porcelana Dentária/química , Propriedades de Superfície , Materiais Dentários/química , Cimentos de Ionômeros de VidroRESUMO
OBJECTIVES: Resin composites may release bisphenol A (BPA) due to impurities present in the monomers. However, there is a lack of knowledge regarding the leaching characteristics of BPA from resin composites. Therefore, experimental resin composites were prepared with known amounts of BPA. The objective of this study was (1) to determine which amount of BPA initially present in the material leaches out in the short term and, (2) how this release is influenced by the resin composition. METHODS: BPA (0, 0.001, 0.01, or 0.1 wt%) was added to experimental resin composites containing 60 mol% BisGMA, BisEMA(3), or UDMA, respectively, as base monomer and 40 mol% TEGDMA as diluent monomer. Polymerized samples (n = 5) were immersed at 37 °C for 7 days in 1 mL of water, which was collected and refreshed daily. BPA release was quantified with UPLC-MS/MS after derivatization with pyridine-3-sulfonyl chloride. RESULTS: Between 0.47 to 0.67 mol% of the originally added BPA eluted from the resin composites after 7 days. Similar elution trends were observed irrespective of the base monomer. Two-way ANOVA showed a significant effect of the base monomer on BPA release, but the differences were small and not consistent. SIGNIFICANCE: The released amount of BPA was directly proportional to the quantity of BPA present in the resin composite as an impurity. BPA release was mainly diffusion-based, while polymer composition seemed to play a minor role. Our results underscore the importance for manufacturers only to use monomers of the highest purity in dental resin composites to avoid unnecessary BPA exposure in patients.
Assuntos
Compostos Benzidrílicos , Resinas Compostas , Fenóis , Fenóis/análise , Fenóis/química , Compostos Benzidrílicos/química , Resinas Compostas/química , Teste de Materiais , Cromatografia Líquida de Alta Pressão , Espectrometria de Massas em Tandem , Poliuretanos/química , Ácidos Polimetacrílicos/química , Metacrilatos/química , Metacrilatos/análise , Polietilenoglicóis/química , PolimerizaçãoRESUMO
Purpose To assess elution from direct composite materials for provisional restorations and compare them with elution from direct restorative composites for permanent restorations.Methods Two dual-cure (Integrity Multi-Cure and Tempsmart DC) and two self-curing composites (Protemp 4 and Structur 3) were used, with Essentia serving as a reference. Cylindrical specimens (n=20) were cured according to the manufacturer's instructions; the dual-cure materials were prepared in both self- and dual-curing modes. Elution experiments were performed using water and absolute ethanol. The samples were incubated at 37 °C for either 24 h or four weeks; the extraction solvents were refreshed weekly. The eluted BisEMA (-3 / -6 / -10), BisGMA, CQ, UDMA, and TEGDMA were quantified using UHPLC-MS/MS.Results Monomer elution was detected in all provisional composites at 24 h and four weeks, but the amounts released did not exceed those released by the reference composite. When prepared in self-curing mode, Integrity Multi-Cure exhibited significantly higher elution of BisEMA-3, -6, and -10 in ethanol both after 24 h and cumulatively after four weeks. Self-cured Tempsmart DC released significantly more CQ, TEGDMA, and UDMA in both water and ethanol after immersion for 24 h and four weeks, along with significantly more BisGMA in ethanol both after 24 h and four weeks comparison to dual-cured Tempsmart DC (two-way ANOVA, post-hoc Tukey, P < 0.05).Conclusions Provisional composite materials did not elute higher amounts of monomers than a restorative composite. Dual-cured materials, prepared in the self-curing mode, show a trend towards higher monomer elution.
RESUMO
PURPOSE: This study aimed to investigate the effects of the age and sex of tooth donors on dentin bond strength. METHODS: A total of 38 extracted teeth (12 male and 26 female donors; age range: 17-82 years) were used in this study. In addition to donor age and sex, four other microtensile bond strength (µTBS) test specimen factors were evaluated: dentin position, bonding area, presence of voids at the interface, and computed tomography (CT) values of dentin. The µTBS was measured immediately (24 h) and 6 months after storage in water. After the µTBS testing, linear mixed and nonlinear regression models were used to analyze the effects of these factors on the µTBS data. RESULTS: The results from the linear mixed model revealed that the bonding area (P = 0.02), presence of voids at the interface (P = 0.04), and storage time (P < 0.001) significantly affected bond strength. In contrast, no correlation was observed between the µ TBS and dentin position (P = 0.08) or sex (P = 0.07). The results of the nonlinear regression model with robust variance-covariance estimators revealed that age significantly affected bond strength (P < 0.001). In addition, a significant positive correlation was found between µTBS and age (P < 0.001), with nonlinearity (P = 0.002). However, no correlation was observed between the µTBS and CT values (P = 0.69) without nonlinearity (P = 0.39). CONCLUSIONS: These findings suggest that bond strength increases with age until 60 years but not afterward.
RESUMO
Dental adhesives are widely used in daily practice for minimally invasive restorative dentistry but suffer from bond degradation and biofilm attack. Bio-inspired by marine mussels having excellent surface-adhesion capability and high chemical affinity of polydopamine (PDA) to metal ions, herein, experimental zinc (Zn)-containing polydopamine-based adhesive formulation, further being referred to as "Zn-PDA@SiO2"-incorporated adhesive is proposed as a novel dental adhesive. Different Zn contents (5 and 10 mm) of Zn-PDA@SiO2 are prepared. Considering the synergistic effect of Zn and PDA, Zn-PDA@SiO2 not only presents excellent antibacterial potential and notably inhibits enzymatic activity (soluble and matrix-bound proteases), but also exhibits superior biocompatibility and biosafety in vitro/vivo. The long-term bond stability is substantially improved by adding 5 wt% 5 mm Zn-PDA@SiO2 to the primer. The aged bond strength of the experimentally formulated dental adhesives applied in self-etch (SE) bonding mode is 1.9 times higher than that of the SE gold-standard adhesive. Molecular dynamics calculations indicate the stable formation of covalent bonds, Zn-assisted coordinative bonds, and hydrogen bonds between PDA and collagen. Overall, this bioinspired dental adhesive provides an avenue technology for innovative biomedical applications and has already revealed promising perspectives for dental restorative dentistry.
Assuntos
Microesferas , Dióxido de Silício , Animais , Dióxido de Silício/química , Indóis/química , Zinco/química , Polímeros/química , Cimentos Dentários/química , Antibacterianos/química , Antibacterianos/farmacologia , Simulação de Dinâmica MolecularRESUMO
PURPOSE: This study aimed to investigate the bonding effectiveness of two HEMA/BPA-free universal adhesives (UAs) to flat dentin, to characterize their adhesive-dentin interfacial ultrastructure, and to measure their water sorption (Wsp), water solubility (Wsl), and hydrophobicity. MATERIALS AND METHODS: The immediate and aged (50,000 thermocycles) microtensile bond strength (µTBS) to flat dentin of the HEMA/BPA-free UAs Healbond Max (HbMax; Elsodent) and Healbond MP (HbMP; Elsodent) as well as the reference adhesives OptiBond FL (Opti-FL; Kerr), Clearfil SE Bond 2 (C-SE2; Kuraray Noritake), and Scotchbond Universal (SBU; 3M Oral Care) was measured. The adhesive-dentin interfaces of HbMax and HbMP were characterized by TEM. Wsp and Wsl of all adhesive resins and of the primer/adhesive resin mixtures of HbMax, Opti-FL, and C-SE2 were measured. Hydrophobicity was determined by measuring the contact angle of water dropped on adhesive-treated dentin. RESULTS: In terms of µTBS, HbMax and HbMP performed statistically similarly to Opti-FL and C-SE2, but outperformed SBU. Aging only significantly reduced the µTBS of SBU when applied in E&R bonding mode. TEM revealed typical E&R and SE hybrid-layer ultrastructures at dentin, while electron-lucent globules of unknown origin, differing in size and shape, were observed within the adhesive resin of HbMP and even more frequently in that of HbMax. Higher Wsp was measured for the primer/adhesive resin mixtures than for the adhesive resins. Opti-FL was more hydrophobic than all other adhesives tested. CONCLUSION: The HEMA/BPA-free UAs bonded durably to flat dentin with bond strengths comparable to those of the gold-standard E&R/SE adhesives and superior to that of the HEMA/BPA-containing 1-step UA.
Assuntos
Colagem Dentária , Cimentos Dentários , Adesivos Dentinários/química , Teste de Materiais , Resistência à Tração , Dentina , Cimentos de Resina/química , Água , Adesivos , Resinas CompostasRESUMO
OBJECTIVES: To investigate the influence of adhesive resin application modalities on the film thickness of the adhesive resin and the effectiveness of a two-step universal adhesive (UA) bonded in self-etch (SE) bonding mode to high C-factor class-I cavity-bottom dentin. MATERIALS AND METHODS: After application of the primer of G2-Bond Universal (G2B, GC), the adhesive resin was applied into standard class-I cavities (human molars) following four application modalities: (1) one layer, strongly air-blown; (2) one layer, gently air-blown; (3) two layers, each gently air-blown; (4) one layer, not air-blown. After being restored with composite, each tooth was sectioned to obtain one micro-specimen (n = 10), of which the adhesive resin film thickness was measured using optical microscopy. The micro-tensile bond strength (µTBS) was tested immediately or upon 100,000 thermocycles. Statistical analyses involved Kruskal-Wallis and Mann-Whitney U testing (p < 0.05). RESULTS: G2B's µTBS was significantly affected by the adhesive resin application modality and aging. Gently air-blowing the adhesive resin resulted in significantly higher immediate µTBS than strong air-blowing or no air-blowing. No significant difference in µTBS was found between single or double gently air-blown adhesive resin applications. The adhesive resin film thickness significantly varied with the application modalities. CONCLUSIONS: A too thin or too thick adhesive resin film thickness adversely affected bond strength of the two-step UA applied in SE mode and high C-factor condition. CLINICAL RELEVANCE: The adhesive resin layer thickness can affect the bonding performance of two-step UAs in high C-factor cavities. Dental clinicians remain advised to avoid improper air-blowing of UAs and strictly follow the application instructions.
Assuntos
Cárie Dentária , Cimentos Dentários , Dentina , Humanos , Envelhecimento , Dente MolarRESUMO
Controlling the formation of supramolecular protein assemblies and endowing them with new properties that can lead to novel functional materials is an important but challenging task. In this work, a new hybrid polyoxometalate is designed to induce controlled intermolecular bridging between biotin-binding proteins. Such bridging interactions lead to the formation of supramolecular protein assemblies incorporating metal-oxo clusters that go from several nanometers in diameter up to the micron range. Insights into the self-assembly process and the nature of the resulting biohybrid materials are obtained by a combination of Small Angle X-ray Scattering (SAXS), Transmission Electron Microscopy (TEM), and Dynamic Light Scattering (DLS), along with fluorescence, UV-vis, and Circular Dichroism (CD) spectroscopy. The formation of hybrid supramolecular assemblies is determined to be driven by biotin binding to the protein and electrostatic interactions between the anionic metal-oxo cluster and the protein, both of which also influence the stability of the resulting assemblies. As a result, the rate of formation, size, and stability of the supramolecular assemblies can be tuned by controlling the electrostatic interactions between the cluster and the protein (e.g., through varying the ionic strength of the solution), thereby paving the way toward biomaterials with tunable assembly and disassembly properties.
Assuntos
Compostos de Tungstênio , Compostos de Tungstênio/química , Proteínas/química , Espalhamento a Baixo Ângulo , Difração de Raios X , Dicroísmo Circular , Biotina/química , Polieletrólitos , ÂnionsRESUMO
Additive manufacturing (AM) of high-performance structural ceramic components with comparative strength and toughness as conventionally manufactured ceramics remains challenging. Here, a UV-curing approach is integrated in direct ink writing (DIW), taking advantage from DIW to enable an easy use of high solid-loading pastes and multi-layered materials with compositional changes; while, avoiding drying problems. UV-curable opaque zirconia-based slurries with a solid loading of 51 vol% are developed to fabricate dense and crack-free alumina-toughened zirconia (ATZ) containing 3 wt% alumina platelets. Importantly, a non-reactive diluent is added to relieve polymerization-induced internal stresses, avoid subsequent warping and cracking, and facilitate the de-binding. For the first time, UV-curing assisted DIW-printed ceramic after sintering reveals even better mechanical properties than that processed by a conventional pressing. This is attributed to the aligned alumina platelets, enhancing crack deflection and improving the fracture toughness from 6.8 ± 0.3 MPa m0.5 (compacted) to 7.4 ± 0.3 MPa m0.5 (DIW). The four-point bending strength of the DIW ATZ (1009 ± 93 MPa) is also higher than that of the conventionally manufactured equivalent (861 ± 68 MPa). Besides homogeneous ceramic, laminate structures are demonstrated. This work provides a valuable hybrid approach to additively manufacture tough and strong ceramic components.
RESUMO
Purpose This study aims to evaluate the effects of resin primers containing methyl methacrylate (MMA) and silane agent on the bonding effectiveness of indirect resin composite blocks with three different filler contents.Methods A commercially available computer-aided design/computer-aided manufacturing (CAD/CAM) resin composite block and two experimental resin composite blocks with different filler contents were alumina-blasted and two surface treatments (primer and silane agent) were applied. The resin cement was built up, and the micro-tensile bond strength (µTBS) was measured after 24 hours, 1 month or 3 months of water storage (n = 24 per group). The fracture surfaces after µTBS measurements and resin block/cement interface were observed by scanning electron microscopy (SEM).Results The primer treatment group showed a significantly higher bond strength than the silane group only in F0 (filler content 0 wt%) group (P < 0.001). In the primer group, F0 and F41 (filler content 41 wt%) groups showed significantly higher bond strengths than F82 (filler content 82 wt%) group (P < 0.001). In contrast, in the silane group, F41 group showed significantly higher bond strength than F0 and F82 groups (P < 0.001), and F82 group showed significantly higher bond strength than F0 group (P < 0.001). SEM revealed that the matrix resin was partially destroyed on the fracture surface of the primer group, and an uneven interface surface was observed compared with that of the silane group.Conclusions MMA-containing primers showed higher bonding effectiveness to CAD/CAM resin composite blocks than the silane treatment.
Assuntos
Colagem Dentária , Silanos , Silanos/química , Propriedades de Superfície , Teste de Materiais , Cimentos de Resina/química , Resinas Compostas/química , Coroas , Resistência à Tração , Desenho Assistido por ComputadorRESUMO
OBJECTIVE: This scoping review aims to assess the influence of air abrasion with aluminum oxide and bioactive glass on dentin bond strength. MATERIALS AND METHODS: An electronic search was conducted in three databases (PubMed, Cochrane Library, and Embase), on March 3rd, 2023, with previously identified MeSH Terms. A total of 1023 records were screened. Exclusion criteria include primary teeth, air abrasion of a substrate other than sound dentin, use of particles apart from aluminum oxide or bioactive glass, and studies in which bond strength was not assessed. RESULTS: Out of the 1023 records, title and abstract screening resulted in the exclusion of 895 and 67 studies, respectively, while full-text analysis excluded another 25 articles. In addition, 5 records were not included, as full texts could not be obtained after requesting the authors. Two cross-references were added. Thus, 33 studies were included in this review. It is important to emphasize the absence of standardization of air abrasion parameters. According to 63.6% of the studies, air abrasion does not influence dentin bond strength. Moreover, 30.3% suggest improving bonding performance, and 6.1% advocate a decrease. CONCLUSIONS: Air abrasion with aluminum oxide does not enhance or impair dentin bond strength. The available data on bioactive glass are limited, which hinders conclusive insights. CLINICAL SIGNIFICANCE: Dentin air abrasion is a widely applied technique nowadays, with numerous clinical applications. Despite the widespread adoption of this procedure, its potential impact on bonding performance requires a thorough analysis of the existing literature.
Assuntos
Colagem Dentária , Dentina , Propriedades de Superfície , Dentina/efeitos dos fármacos , Colagem Dentária/métodos , Humanos , Abrasão Dental por Ar/métodos , Óxido de Alumínio/químicaRESUMO
PURPOSE: To investigate the bonding performance of three universal adhesives (UAs) to dentin and the effect of different curing modes and hydrofluoric-acid (HF) etching of lithium-disilicate glass-ceramic on the adhesive performance of two UA/composite cement (CC) combinations. MATERIALS AND METHODS: In the first project part, the immediate and aged (25k and 50k thermocycles) microtensile bond strength (µTBS) of the two light-curing UAs G2-Bond Universal (G2B; GC) and Scotchbond Universal Plus (SBUp; 3M Oral Care), and the self-curing UA Tokuyama Universal Bond II (TUBII; Tokuyama) to flat dentin was measured, when applied in both E&R and SE bonding mode using a split-tooth design (n = 10). The resultant adhesive-dentin interfaces were characterized using TEM. In the second project part, CAD/CAM composite blocks were luted to flat dentin with either Scotchbond Universal Plus/RelyX Universal (SBUp/RxU; 3M Oral Care) or Tokuyama Universal Bond II/Estecem II Plus (TUBII/ECIIp; Tokuyama Dental) using different curing modes (AA mode: auto-curing of both adhesive and cement; AL mode: auto-curing of adhesive and light-curing of cement), upon which their immediate and aged (25k and 50k thermocycles) µTBS was measured. In the third project part, the same UA/CC combinations were luted to CAD/CAM glass-ceramic to measure their immediate and aged (6-month water storage) shear bond strength (SBS). RESULTS: In E&R bonding mode, the performance of G2B, SBUp and TUBII was not significantly different in terms of µTBS, while G2B and SBUp significantly outperformed TUBII in SE bonding mode. No significant difference in µTBS was found between the SBUp/RxU and TUBII/ECIIp UA/CC combinations, regardless of bonding mode, aging time, or curing mode. The cement-curing mode did not significantly influence µTBS, while a significantly higher µTBS was recorded for the UA/CC combinations applied in E&R bonding mode. HF significantly improved the SBS of the UA/CC combinations to glass-ceramic. CONCLUSION: The self-curing adhesive performed better when applied in E&R than in SE bonding mode. The curing mode did not influence the adhesive performance of the composite cements, while an E&R bonding mode rendered more favorable adhesion in a self-curing luting protocol. When bonding to glass-ceramic, the adhesive performance of the universal adhesive/composite cement combinations benefited from HF etching.
Assuntos
Colagem Dentária , Cimentos Dentários , Cimentos Dentários/química , Cimentos de Resina/química , Colagem Dentária/métodos , Cimentos de Ionômeros de Vidro , Teste de Materiais , Resistência à Tração , Adesivos Dentinários/química , Adesivos , DentinaRESUMO
Zirconia restorations are increasingly popular in dental treatment. Yttria-stabilized zirconia (YSZ) needs to be sintered for clinical applications and novel speed-sintering protocols are being developed for chairside treatments. Whether the properties of speed-sintered YSZ meet clinical requirements, however, remains unclear. Therefore, we conducted a systematic review and meta-analysis on the influence of speed-sintering on the optical and mechanical properties of dental YSZ according to the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) 2020 guidelines. A literature search was conducted using PubMed, Embase, and Web of Science databases for relevant articles published between January 1, 2010 and February 28, 2022 in English, Chinese, or Japanese. After full-text evaluation and quality assessment, 26 articles were selected. Meta-analysis revealed that speed-sintering does not significantly affect the CIEDE2000-based translucency parameter, contrast ratio, three-point flexural strength, biaxial flexural strength, or fracture toughness of YSZ (p < 0.01) compared to conventional sintering. However, the CIELab-based translucency parameter of conventionally sintered YSZ is higher than that of speed-sintered YSZ. The descriptive analysis indicated that speed-sintering does not affect the hardness of YSZ compared to that of conventionally sintered YSZ. The results indicate that speed-sintering is suitable for preparing YSZ for dental restorations.
RESUMO
PURPOSE: This randomized controlled trial aimed to evaluate the 14-year clinical performance of a HEMA-free 1-step self-etch adhesive (1SEa) compared with that of a 3-step etch-and-rinse adhesive (3E&Ra). MATERIALS AND METHODS: 267 non-carious cervical lesions in 52 patients were restored with the microhybrid composite Gradia Direct (GC), bonded in random order either with the HEMA-free 1SEa G-Bond (GB; GC) or the 3E&Ra Optibond FL (OFL; Kerr), which is considered the gold-standard E&Ra (control). The restorations were followed over 14 years for retention, marginal adaptation and discoloration, and caries occurrence. Statistical analysis involved a logistic regression model with generalized estimating equations (2-way GEE model). RESULTS: The patient recall rate at 14 years was 63%. In total, 79 restorations (39 GB, 40 OFL) failed because of retention loss (GB: 19.4%, OFL: 19.6%), severe marginal defects, discoloration and/or caries (GB: 21.7%; OFL: 22.5%). The overall clinical success rate was 58.9% and 57.9% for GB and OFL, respectively. The number of restorations with an unacceptable marginal defect (GB: 14.5%; OFL: 19.2%) and deep marginal discoloration (GB: 18.2%; OFL: 13.2%) increased during the last 5 years. No significant difference in overall clinical performance was recorded between the two adhesives (p > 0.05). Changes in the medical health of some patients and recurrence of abrasion/erosion/abfraction increased the failure rate and retention rate. CONCLUSION: After 14 years, restorations bonded with the HEMA-free 1SEa performed as well as those bonded with the 3E&Ra gold standard. Unacceptable marginal deterioration was the main reason for failure, followed by loss of retention.
Assuntos
Cárie Dentária , Humanos , Cárie Dentária/terapia , Projetos de PesquisaRESUMO
PURPOSE: The aim of this randomized controlled clinical trial was to evaluate the 3-year clinical performance of a universal adhesive (Clearfil Universal Bond Quick (CUBQ); Kuraray Noritake) when restoring non-carious cervical lesions (NCCLs) using two different application modes (etch-and-rinse vs self-etch with prior selective enamel etching). MATERIALS AND METHODS: Fifty-one patients participated in this study. A total of 251 NCCLs (n = 251) were assigned to two groups: 1) CUBQ applied in etch-and-rinse mode (n = 122; CUBQ-ER) and 2) CUBQ applied in self-etch mode with prior selective etching of enamel with phosphoric acid (n = 129; CUPQ-SEE). The same resin composite, Clearfil Majesty ES-2 (Kuraray Noritake), was used for all restorations. The restorations were evaluated at baseline, 1 and 3 years using FDI criteria: marginal staining, fracture and retention, marginal adaptation, post-operative sensitivity and recurrence of caries. Statistical analysis was performed using a logistic regression model with generalized estimating equations (2-way GEE model). RESULTS: The patient recall rate at 3 years was 90%. After 3 years, both groups presented an increase in the percentage of small but still clinically acceptable marginal defects (CUBQ-ER: 67%, CUBQ-SEE: 63.2%) and marginal staining (CUBQ-ER: 32.6%, CUBQ-SEE: 31.7%). The overall success rate was 82.6% and 83.8% for CUBQ-ER and CUBQ-SEE, respectively. In total, 38 restorations (19 CUBQ-ER, 19 CUBQ-SEE) failed because of loss of retention, fracture, severe marginal defect and/or marginal discoloration. A retention rate of 87.2% and 86.3% was recorded for CUBQ-ER and CUBQ-SEE, respectively. No significant difference was observed between the two bonding-mode groups for any of the evaluated parameters. CONCLUSION: After 3 years of clinical service, Clearfil Universal Bond Quick performed similarly in etch-and-rinse and self-etch modes with prior selective enamel etching.
Assuntos
Cárie Dentária , Humanos , Cárie Dentária/terapia , Esmalte DentárioRESUMO
INTRODUCTION: Understanding the healing process of dental pulp after tooth autotransplantation (TAT) and regenerative endodontic treatment (RET) of immature teeth is important both clinically and scientifically. This study aimed to characterize the pattern of dental pulp healing in human teeth that underwent TAT and RET using state-of-the-art imaging techniques. MATERIALS AND METHODS: This study examined 4 human teeth, 2 premolars that underwent TAT, and 2 central incisors that received RET. The premolars were extracted after 1 year (case 1) and 2 years (case 2) due to ankylosis, while the central incisors were extracted after 3 years (cases 3 and 4) for orthodontic reasons. Nanofocus x-ray computed tomography was used to image the samples before being processed for histological and immunohistochemical analysis. Laser scanning confocal second harmonic generation imaging (SHG) was used to examine the patterns of collagen deposition. A maturity-matched premolar was included as a negative control for the histological and SHG analysis. RESULTS: Analysis of the 4 cases revealed different patterns of dental pulp healing. Similarities were observed in the progressive obliteration of the root canal space. However, a striking loss of typical pulpal architecture was observed in the TAT cases, while a pulp-like tissue was observed in one of the RET cases. Odontoblast-like cells were observed in cases 1 and 3. CONCLUSIONS: This study provided insights into the patterns of dental pulp healing after TAT and RET. The SHG imaging sheds light on the patterns of collagen deposition during reparative dentin formation.
Assuntos
Polpa Dentária , Endodontia Regenerativa , Humanos , Polpa Dentária/diagnóstico por imagem , Regeneração , Endodontia Regenerativa/métodos , Transplante Autólogo , Necrose da Polpa Dentária/diagnóstico por imagem , Necrose da Polpa Dentária/terapia , Colágeno , Imagem MultimodalRESUMO
Despite being able to adhesively restore teeth, adhesives and cement do not possess any anticariogenic protection potential, by which caries recurrence may still occur and reduce the clinical lifetime of adhesive restorations. Several antibacterial agents have been incorporated into dental adhesives and cement to render them anticariogenic. Due to an additional therapeutic effect, such materials are classified as 'dental combination products' with more strict market regulations. We incorporated cetylpyridinium chloride (CPC), often used for oral hygiene applications, into montmorillonite (CPC-Mont), the latter to serve as a carrier for controlled CPC release. CPC-Mont incorporated into tissue conditioner has been approved by the Pharmaceuticals and Medical Devices Agency (PmontMDA) in Japan. To produce a clinically effective dental cement with the antibacterial potential to prevent secondary caries, we incorporated CPC-Mont into PMMA resin cement. We measured the flexural strength, shear bond strength onto dentin, CPC release, and the biofilm-inhibition potential of the experimental CPC-Mont-containing PMMA cement. An 8 and 10 wt% CPC-Mont concentration revealed the antibacterial potential without reducing the mechanical properties of the PMMA cement.