Effect of Two Different Ageing Exposures on the Colour Stability of Transparent Polyurethane Finishing.

This paper deals with the influence of dark and light exposure on the colour change of a transparent two-component polyurethane surface finish. The surface finish with polyacrylic and aldehyde resin was applied to the surfaces of untreated and hydrothermally treated European beech, alder, Norway maple, and Paper birch wood. The test specimens were deposited indoors for 60 days. The colour values (lightness L*, redness + a*, yellowness + b*, chroma C*, hue angle h°) were expressed in the CIELAB system. The results showed that the colour difference of the finish surfaces of all hydrothermally treated wood species was 27-50% lower after the dark than when exposed to light. In the case of finished untreated wood, the colour difference was 51-73% lower after the dark than light exposure. Only the finished untreated and hydrothermally treated Norway maple wood surfaces showed similar and significant changes after both dark and light exposure. The lower value of the colour difference of the finished hydrothermally treated wood was due to the fact that steaming wood with saturated water steam has a positive effect on the overall colour stability of the finish and partial resistance to the initiation of photolytic reactions caused by light.

Thermal Modification of Spruce and Maple Wood for Special Wood Products.

This article presents a proposal of thermal modification of Norway spruce and sycamore maple for special wood products, mainly for musical instruments. Selected physical and acoustical characteristics (PACHs), including the density (ρ), dynamic modulus of elasticity along the wood grain (EL), specific modulus (Esp), speed of sound along the wood grain (cL), resonant frequency (fr) and acoustic constant (A), logarithmic decrement (ϑ), loss coefficient (η), acoustic conversion efficiency (ACE), sound quality factor (Q), and the timbre of sound, were evaluated. These two wood species were chosen regarding their use in the production or repair of musical instruments. For the thermal modification, a similar process to the ThermoWood process was chosen. Thermal modification was performed at the temperatures 135 °C, 160 °C and 185 °C. The resonant dynamic method was used to obtain the PACHs. Fast Fourier transform (FFT) was used to analyze the sound produced. The changes in the observed wood properties depended on the treatment temperature. Based on our results of all properties, the different temperature modified wood could find uses in the making of musical instruments or where the specific values of these wood characteristics are required. The mild thermal modification resulted in a decrease in mass, density, and increased speed of sound and dynamic modulus of elasticity at all temperatures of modification. The thermally modified wood showed higher sound radiation and lower loss coefficients than unmodified wood. The modification also influenced the timbre of sound of both wood species.

Changes in Chemical Structure of Thermally Modified Spruce Wood Due to Decaying Fungi.

Fungi play a critical role in the decomposition of wood and wood-based products in use. The ability of decaying fungi to cause degradation of polysaccharides and lignin in the thermally modified Norway spruce (Picea abies L. Karst.) wood was examined with pure culture decomposition tests in laboratory conditions using the brown-rot fungus Serpula lacrymans (Schumacher ex Fries) S.F. Gray and white-rot fungus Trametes versicolor (Linnaeus ex Fries) Pilat. Spruce wood samples were primary thermally treated under atmospheric pressure at the temperatures of 100, 150, 200, 220, 240 and 260 °C during 1, 3 and 5 h, whereby larger losses in their mass, holocellulose, mannose and xylose were achieved at harder thermal regimes. Meanwhile, the holocellulose percent content reduced considerably, and the percent content of lignin increased sharply. Spruce wood thermally modified at and above 200 °C better resisted to brown-rot fungus S. lacrymans than the white-rot fungus T. versicolor. Due to the decay processes, the mass fractions of holocellulose, cellulose and hemicelluloses were lower in those spruce wood samples in which thermal degradation was more intensive, with achieving the highest mass loss values after thermal treatments, after which the decay attacks were poorer or even none with the minimal mass loss values due to action by the brown-rot fungus S. lacrymans and the white-rot fungus T. versicolor. The mannose and glucose percent content in thermally-fungally attacked spruce wood was intensive reduced, e.g., by 17% to 98% in wood after thermal treatments at temperature equal and above 200 °C.

Colour Stabilisation of Surface of Four Thermally Modified Woods with Saturated Water Vapour by Finishes.

This paper deals with the influence of the type of transparent surface finish on the change of colour of the surfaces of native wood, and thermally treated wood, with saturated water vapour. In the experiment, alder, European beech, Paper birch, and Norway maple wood were thermally treated at a temperature of 135 °C under saturated water vapour for six hours. Three various types of surface finishes (acrylic-polyurethane, polyacrylic and aldehyde resin, and alkyd resin) were applied onto the wood surfaces. The colours of the surfaces in the system, CIE L*a*b* (lightness, coordinates a* and b*, chroma and hue angle), were measured during finishing and natural ageing behind glass windows in an interior, over a period of 60 days. The results show that the changes in the yellowness index, and the total colour differences after the application of individual surface finishes to wood species, changed because of sunlight exposure. Moreover, it is clear that different wood finishes behaved differently on all of the wood species. An analysis is presented in this paper.