Evaluation of Carbon Dioxide-Based Urethane Acrylate Composites for Sealers of Root Canal Obturation.

A new root canal sealer was developed based on urethane acrylates using polycarbonate polyol (PCPO), a macrodiol prepared in the consumption of carbon dioxide as feedstock. The superior mechanical properties and biostability nature of PCPO-based urethane acrylates were then co-crosslinked with a difunctional monomer of tripropylene glycol diarylate (TPGDA) as sealers for resin matrix. Moreover, nanoscale silicate platelets (NSPs) immobilized with silver nanoparticles (AgNPs) and/or zinc oxide nanoparticles (ZnONPs) were introduced to enhance the antibacterial effect for the sealers. The biocompatibility and the antibacterial effect were investigated by Alamar blue assay and LDH assay. In addition, the antibacterial efficiency was performed by using Enterococcus faecalis (E. faecalis) as microbial response evaluation. These results demonstrate that the PCPO-based urethane acrylates with 50 ppm of both AgNP and ZnONP immobilized on silicate platelets, i.e., Ag/ZnO@NSP, exhibited great potential as an antibacterial composite for the sealer of root canal obturation.

Synthesis and Properties of Cyclopentyl Cardo-Type Polyimides Based on Dicyclopentadiene.

A crucial polymer intermediate, 4-[1-(4-hydroxyphenyl)cyclopentyl]-phenol (bisphenol CP), was developed from dicyclopentadiene (DCPD), a key byproduct of the C5 fraction in petrochemicals. On the basis of bisphenol CP, a diamine, 4,4'-((cyclopentane-1,1-diylbis(4,1-phenylene))bis(oxy))-dianiline (cyclopentyl diamine; CPDA) was subsequently obtained through a nucleophilic substitution of bisphenol CP, followed by the hydrogenation process. By using the CPDA diamine, a series of polyimides with cyclopentyl (cardo) units on the backbone were prepared along with a reference polyimide (API-6F) based on 4,4'-(4,4'-(propane-2,2-diyl)bis(4,1-phenylene))bis(oxy)dianiline (BPAA), and 4,4'-(hexafluoroisopropylidene)-diphthalic anhydride (6FDA) for the exploration of structure-properties relationship. Thanks to the presence of cyclopentyl units, this type of cardo polyimides exhibited comparable tensile properties, especially a large elongation (25.4%). It is also worth noting that CPI-6F exhibited better solubility in organic solvents, such as NMP, DMAc, THF, and chloroform, than the other PIs. Gas separation properties were also evaluated for these cardo-type polyimides.

In Search of a Green Process: Polymeric Films with Ordered Arrays via a Water Droplet Technique.

As an efficient technique for the preparation of polymeric hexagonal orderly arrays, the breath figure (BF) process has opened a modern avenue for a bottom-up fabrication method for more than two decades. Through the use of the water vapor condensation on the solution surface, the water droplets will hexagonally pack into ordered arrays, acting as a template for controlling the regular micro patterns of polymeric films. Comparing to the top-down techniques, such as lithography or chemical etching, the use of water vapor as the template provides a simple fabrication process with sustainability. However, using highly hazardous solvents such as chloroform, carbon disulfide (CS2), benzene, dichloromethane, etc., to dissolve polymers might hinder the development toward green processes based on this technique. In this review, we will touch upon the contemporary techniques of the BF process, including its up-to-date applications first. More importantly, the search of greener processes along with less hazardous solvents for the possibility of a more sustainable BF process is the focal point of this review.

Au Nanoparticles Immobilized on Honeycomb-Like Polymeric Films for Surface-Enhanced Raman Scattering (SERS) Detection.

We have successfully developed novel surface-enhanced Raman scattering (SERS) substrates with three-dimensional (3D) porous structures for effectively improving the sensitivity and reproducibility of SERS, which can rapidly detect small molecules (rhodamine 6G as an example). Periodical arrays of the honeycomb-like substrates were fabricated by self-assembling polyurethane-co-azetidine-2,4-dione (PU-PAZ) polymers. PU-PAZ comprising amphiphilic dendrons could stabilize the phase separation between the water droplets and polymer solution, and then organize into regular porous structures during the breath figure method. Subsequently, SERS substrates were fabricated by immobilizing gold nanoparticles (AuNPs) onto the honeycomb-like films with various 3D porous structures, controlled by the different PU-PAZ concentrations and relative humidities. Results show that surface enhancement factors of honeycomb-like substrates were 20 times higher than that of flat-film substrates (control group) due to enormous hot-spots resonance effects by the 3D porous structure, verified through Raman mapping at various positions of the z-axis. Furthermore, the particle size effects were evaluated by immobilized 12 and 67 nm of AuNPs on the honeycomb-like substrates, indicating larger AuNPs could induce more pronounced hot-spots effects. The generation of hot-spots resonance to enhance Raman intensity is strongly dependent on the diameter of AuNPs and the pore size of the honeycomb-like and 3D porous substrates for label-free and rapid SERS detection.